| Study on Corrosion Behavior on Joint Section of Aircraft Aluminium Alloy Structure |
| ;;; |
| 北京航空工程技术中心 |
|
Cite this article:
;. Study on Corrosion Behavior on Joint Section of Aircraft Aluminium Alloy Structure. J Chin Soc Corr Pro, 2007, 27(6): 334-337 .
|
|
|
Abstract The Corrosion features on the joint section of aircraft Aluminum alloy structure were expounded briefly. The corrosion behaviors on the joint section of aircraft aluminium alloy structure painted coating were studied using the accelerated corrosion environment spectrum testing method. The corrosion damage course was reproduced and the corrosion growth laws were brought to light under the laboratory condition.
|
|
Received: 20 April 2006
|
|
|
[1]Wanhill R J H,De Luccia J J,Russo M T.The fatigue in aircraftcorrosion testing(FACT)program[R].AGARD Report No.713,1989:3-25
[2]Li J F,Cao F H,Zhang Z,el at.Review on exfoliation suscepti-bility of aluminium alloys and quantitative measurement method[J].J.Chin.Soc.Corros.Prot.,2004,24(1):56-57(李劲风,曹发和,张昭等.铝合金剥蚀敏感性及其定量研究方法[J].中国腐蚀与防护学报,2004,24(1):56-57)
[3]Maitra S,English G C.Mechanism of localized corrosion of 7075alloy plate[J].Metall.Trans.,1981,12A:535-541
[4]Chen Q Z.A technique system research on the calendar life of air-craft structure under corrosive environment[D].Beijing:Beijing U-niversity of Aeronautics and Astronautics,1999:10-25(陈群志.腐蚀环境下飞机结构日历寿命技术体系研究[D].北京:北京航空航天大学,1999:10-25)
[5]Sun Y,Hu J.Corrosion and Control of Metal[M].Harbin:Harbin Industry and Technology University Press,2003:92-93(孙跃,胡津.金属腐蚀与控制[M].哈尔滨:哈尔滨工业大学出版社,2003:92-93)
[6]Li D,Zou S Z,Guo B L.Study on exfoliation behavior of LY12aluminum alloy[J].J.Chin.Soc.Corros.Prot.,1995(3):203-209(李荻,左尚志,郭宝兰.LY12铝合金剥蚀行为研究[J].中国腐蚀与防护学报,1995,15(3):203-209)
[7]Cai J,Liu M,Luo Z H,et al.Study on accelerated tests for alu-minum alloy atmospheric corrosion[J].J.Chin.Soc.Corros.Prot.,2005,25(5):262-266(蔡健平,刘明,罗振华等.航空铝合金大气腐蚀加速试验研究[J].中国腐蚀与防护学报,2005,25(5):262-266)
[8]Su J X,Zhang Z,Cao F H,et al.Review on the intergranular cor-rosion and exfoliation corrosion of aluminum alloys[J].J.Chin.Soc.Corros.Prot.,2005,25(3):186-190(苏景新,张昭,曹发和等.铝合金的晶间腐蚀与剥蚀[J].中国腐蚀与防护学报,2005,25(3):186-190)
[9]Buchheit R G Jr,Moran J P,Stoner G E.Localized corrosion behav-ior of alloy 2090-the role of microstructural heterogeneity[J].Corrosion,1990,46(8):610-617
[10]Braun R.Exfoliation corrosion testing of aluminium alloys[J].Br.Corros.J.,1995,30(30):203-208
[11]Zhang W L,Frankel G S.Localized corrosion growth kinetics in AA2024 alloys[J].Electrochem.Soc.,2002,149(22):B510-B519
[12]Zhang W L,Frankel G S.Transitions between pitting and inter-granular corrosion in AA2024[J].Electrochem.Acta,2003,48:1193-1210 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|