MECHANISM OF PROTECTIVE FILM FORMATION DURING CO2 CORROSION ON X65 STEEL

J Chin Soc Corr Pro

2007, Vol. 27

Issue (6): 338-341 DOI:

Research Report

Current Issue | Archive | Adv Search

MECHANISM OF PROTECTIVE FILM FORMATION DURING CO2 CORROSION ON X65 STEEL

;;

Download:

PDF(351KB)
Export: BibTeX | EndNote (RIS)

Abstract In the simulating the environment of CO2 corrosion in oilfield, XRD and SEM techniques were adopted to study the formation and development of CO2 corrosion product film on X65 steel. The results demonstrated that the corrosion scales are three layers in the cross-section. Structural characteristics and formation mechanism of the film were discussed respectively.

Key words: CO2 corrosion corrosion product film X65 steel

Received: 23 June 2006

ZTFLH:

TG172.9

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

. MECHANISM OF PROTECTIVE FILM FORMATION DURING CO2 CORROSION ON X65 STEEL. J Chin Soc Corr Pro, 2007, 27(6): 338-341 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2007/V27/I6/338

[1]Chang X Y,Di C,Lei L C.CO2 Corrosion and Control[M].Bei-jing:Chemical Industry Press,2000
[2]Hausler R H,Giddard H P.Laboratory investigation of the CO2corrosion mechanism as applied to hot deep gas wells[A].In:Hausler R H,Giddard H P(Eds),Advances in CO2 Corrosion,Vol.1,NACE[C].Houston,Texas,1984:72
[3]Long F L,Zheng W J,Chen C F,et al.Influence of temperature,CO2 partial pressure,flow rate and p H value on uniform corrosionrate of X65 pipeline steel[J].Corros.Prot.,2005,26(7):290-293(龙凤乐,郑文军,陈长风等.温度、CO2分压、流速、p H值对X65管线钢CO2均匀腐蚀速率的影响规律[J].腐蚀与防护,2005,26(7):290-293)
[4]Kermani M B,Morshed A.Carbon dioxide corrosion in oil and gasproduction-a compendium[J].Corrosion,2003,59(8):659-683
[5]Palacious C A,Shadley J R.Characteristics of corrosion scales onsteel in CO2-saturated Na Cl brine[J].Corrosion,1991,47(2):122-127
[6]Chen C F,Zhao G X,et al.Study of CO2 corrosion scales on N80steel[J].J.Chin.Soc.Corros.Prot.,2002,22(3):143-146(陈长风,赵国仙等.N80钢CO2腐蚀产物膜研究[J].中国腐蚀与防护学报,2002,22(3):143-146)
[7]Crolet J L,Thevenot N,Nesic S.Role of conductive corrosionproducts on the protectiveness of corrosion layers[A].Corrosion/96[C].Houston:NACE,1996
[8]Dugstad A,Hemmer H,Seiersten M.Effect of steel microstructureupon corrosion rate and protective iron carbonate film formation[A].Corrosion/2000[C].Houston:NACE,2000
[9]Chen C F,Lu M X,et al.Mechanical properties of CO2 corrosionscale on N80 well tube steel[J].Acta Metall.Sin.,2003,39(2):175-181(陈长风,路民旭等.N80油套管钢CO2腐蚀产物膜的力学性能[J].金属学报,2003,39(2):175-181)
[10]Chen C F,Lu M X,et al.Characters of CO2 corrosion scales onwell tube steels N80[J].Acta Metall.Sin.,2002,38(4):411-416(陈长风,路民旭等.N80油套管钢CO2腐蚀产物膜特征[J].金属学报,2002,38(4):411-416)

[1]	JIA Yizheng, ZHAO Mingjun, CHENG Shijing, WANG Baojie, WANG Shuo, SHENG Liyuan, XU Daokui. Corrosion Behavior of Mg-Zn-Y-Nd Alloy in Simulated Body Fluid[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[2]	Mingyu BAO, Chengqiang REN, Jingsi HU, Bo LIU, Jiameng LI, Feng WANG, Li LIU, Xiaoyang GUO. Stress Induced Corrosion Electrochemical Behavior of Steels for Oil and Gas Pipes[J]. 中国腐蚀与防护学报, 2017, 37(6): 504-512.
[3]	Di ZHANG,Ping LIANG,Yunxia ZHANG,Yanhua SHI,Hua QIN. Effect of Corrosion Product Film Formed in Artificial Solution Simulated Soil Medium at Ku'erle Area onPitting Corrosion Behavior of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2016, 36(4): 313-320.
[4]	Chen ZHANG,Jingmao ZHAO. Synergistic Inhibition Effect of Imidazoline Ammonium Salt and Three Anionic Surfactants in CO₂-saturatedBrine Solution[J]. 中国腐蚀与防护学报, 2015, 35(6): 496-504.
[5]	ZHAO Tong, ZHAO Jingmao, JIANG Ruijing. Effect of Flow Velocity and Carbon Chain Length on Corrosion Inhibition Performance of Imidazoline Derivates in High Pressure CO₂ Environment[J]. 中国腐蚀与防护学报, 2015, 35(2): 163-168.
[6]	ZHANG Timing, ZHAO Weimin, GUO Wang, WANG Yong. Susceptibility to Hydrogen Embrittlement of X65 Steel Under Cathodic Protection in Artificial Sea Water[J]. 中国腐蚀与防护学报, 2014, 34(4): 315-320.
[7]	XING Yunying, LIU Zhiyong, DU Cuiwei, LI Xiaogang, LIU Ranke, ZHU Min. Influence of H₂S Concentration and pH Value on Corrosion Behavior of Weld Joint of X65 Subsea Pipeline Steel[J]. 中国腐蚀与防护学报, 2014, 34(3): 231-236.
[8]	Minxv Lu. Effect of Alloying Elements and Microstructure on Steel Corrosion Behavior in CO2 Environments[J]. 中国腐蚀与防护学报, 2008, 28(4): 246-250 .
[9]	. Effect of Temperature on the Electrochemical Properties of CO2 Corrosion on N80 Steel in Stratum Water[J]. 中国腐蚀与防护学报, 2008, 28(2): 104-107 .
[10]	. APPLICATION OF ATOMIC FORCE MICROSCOPY IN STUDY OF SULFATE-REDUCING BACTERIA TO A3 STEEL[J]. 中国腐蚀与防护学报, 2007, 27(2): 70-.
[11]	;. Corrosion Behavior of N80 Steel in Simulated Water from deep Gaswell Containing Carbon Dioxide[J]. 中国腐蚀与防护学报, 2007, 27(1): 8-13 .
[12]	Jianping Li; Guoxian Zhao. DYNAMIC CORROSION BEHAVIORS OF N80,P105 AND SM110 STEEL[J]. 中国腐蚀与防护学报, 2005, 25(4): 241-244 .
[13]	Guoxian Zhao; Xianghong Lv; Helin Li; Minxv Lu. EFFECT OF TEMPERATURE ON CO2 CORROSION BEHAVIOUR OF P110 STEEL[J]. 中国腐蚀与防护学报, 2005, 25(2): 93-96 .
[14]	Guoan Zhang; Changfeng Chen; Minxv Lu; Yinshun Wu. PREDICTION MODELS FOR CO2 CORROSION OF OIL AND GAS FIELDS[J]. 中国腐蚀与防护学报, 2005, 25(2): 119-123 .
[15]	Guanfa Lin. Effect of CO2 Partial Pressure on the Morphology of Corrosion Metallic Product Scales[J]. 中国腐蚀与防护学报, 2004, 24(5): 284-288 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed