| 304奥氏体不锈钢离子辐照后再活化性能测试和表面形貌观察 |
| 李红梅;刘杏;蔡珣;杨武 |
| 上海交通大学材料学院 |
|
| Electrochemical Potentiokinetic Reactivation Measurement and Surface Feature Observation on Austenitic Stainless Steel Irradiated by High Energy He+ or Fe+ Ions |
| Hongmei Li;Xing Liu;Xun Cai;Wu Yang |
| 上海交通大学材料学院 |
引用本文:
李红梅; 刘杏; 蔡珣; 杨武 . 304奥氏体不锈钢离子辐照后再活化性能测试和表面形貌观察[J]. 中国腐蚀与防护学报, 2006, 26(1): 37-42 .
Hongmei Li,
Xing Liu,
Xun Cai,
Wu Yang.
Electrochemical Potentiokinetic Reactivation Measurement and Surface Feature Observation on Austenitic Stainless Steel Irradiated by High Energy He+ or Fe+ Ions. J Chin Soc Corr Pro, 2006, 26(1): 37-42 .
链接本文:
https://www.jcscp.org/CN/
或
https://www.jcscp.org/CN/Y2006/V26/I1/37
|
[1]Yang W,Zhang M J,Zhao G Z.Stress corrosion cracking ofaustenitic stainless steel in high temperature water[J].Acta Metall.Sin.,1991,27(2):116-120(杨武,张美杰,赵国珍.304不锈钢在高温水中的应力腐蚀破裂[J].金属学报,1991,27(2):116-120)
[2]Yang W.Advances in research on irradiation assisted stress corro-sion cracking[J].Mater.Prot.,1994,27(2):1-4
[3]Was G S,Allen T.Intercomparison of microchemical evolution un-der various types of particle irradiation[J].J.Nuclear Mater.,1993,205:332-338
[4]Semenov A A,Woo C H.Stochastic fluctuations and microstructuralevolution during irradiation by neutrons and heavy ions[J].J.Nu-clear Mater.,1993,205:74-83
[5]Lee E L,Hunn J D,Hashimoto N,et al.Hardness and defect struc-tures in EC316LN austenitic alloy irradiated under a simulated spal-lation neutron source environment using triple ion-beams[J].J.Nuclear Mater.,2000,278:266-272
[6]Ahmet Cakir,Sabri Tuncell,Alptekin Aydin.AE response of 316LSS test under potentiostatic control[J].Corros.Sci.,1999,41:1175-1183
[7]Van N R.Electrochemical noise measurements under pressurizedwater reactor conditions[J].Corrosion,2000,56(2):161-166
[8]Kim Y J.In-situ electrochemical impedance measurement of oxidefilm formed on type 304 stainless steel in high-temperature water[J].Corrosion,2000,56(4):389-394
[9]Wan F R.Irradiation Damage of Metal Material[M].Beijing:Sci-ence Press,1993(万发荣.金属材料的辐射损伤[M].北京:科学出版社,1993)
[10]Wei B M.Corrosion Theory and Application of Metal[M].Beijing:Chemical Industry Press,1984(魏宝明主编.金属腐蚀理论及应用[M].北京:化学工业出版社,1984)
[11]Cao C N.Corrosion Electrochemistry[M].Beijing:Chemical In-dustry Press,1994(曹楚南编著.腐蚀电化学[M].北京:化学工业出版社,1994)
[12]Liu Y H,Zhang P F.Metal Corrosion Theory[M].Beijing:Pub-lishing Company of Aviation Industry,1993(刘永辉,张佩芬.金属腐蚀学原理[M].北京:航空工业出版社,1993)
[13]Xiao J M.Metal Corrosion Under Stress[M].Beijing:Chemical In-dustry Prss,1990(肖纪美著.应力作用下的金属腐蚀[M].北京:化学工业出版社,1990)
[14]Xiao J M.Metallurgy of Austenitic Stainless Steel[M].Beijing:Publishing Company of Metallurgical Industry,1993(肖纪美著.不锈钢的金属学问题[M].北京:冶金工业出版社,1993)
[15]Zhao W Z.New Surface Technique of Metal Material[M].Xi’an:Publishing Company of Xi’an Jiaotong University,1992(赵文珍编.金属材料表面新技术[M].西安:西安交通大学出版社,1992)
[16]Poate J M,Foti G,Jacobson D C.Surface Property Changing andAlloying[M].Beijing:Science Press,1988(J.M.波特,G.福蒂,D.C.雅各布森主编.表面改性与合金化[M].北京:科学出版社,1988)
[17]Liu J L,Zhou Z R,Su B R.Heat Treatment of High Energy Beam[M].Beijing:Publishing Company of Mechanical Industry,1997(刘江龙,邹至荣,苏宝容编著.高能束热处理[M].北京:机械工业出版社,1997) |
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|