碳钢在液/固双相管流中磨损腐蚀的电化学行为

田兴玲;林玉珍;刘景军;雍兴跃

北京化工大学材料科学与工程学院

Electrochemical Behavior in Erosion- Corrosion of Carbon Steel in liquid-Solid Double Phase Flow Loop

Xingling Tian;Yuzhen Lin;Jingjun Liu;Xingyue Yong

北京化工大学材料科学与工程学院

全文: PDF(172 KB)

摘要: 利用自行研制的管流动态模拟试验装置，研究了碳钢在液/固双相流中的磨损腐蚀。结果表明：碳钢在含有5%河砂的双相流动3.5%NaCl溶液中，磨损腐蚀速度随流速的增加而显著增大，没有像单相流中出现磨损腐蚀速度显著降低的流速区段，其磨损腐蚀过程仍主要受阴极氧扩散控制。对碳钢施加阴极电流，由于抑制了腐蚀电化学因素，从而大幅度削弱了与流体力学因素间的协同效应，使碳钢的磨损腐蚀大大减轻。

关键词 ：碳钢, 液/固双相流, 管流体系, 磨损腐蚀, 腐蚀

Abstract：The electrochemical behavior in erosion-corrosion of carbon steel in flowing liquid-solid double phase solution was studied with self-made flow loop simulating apparatus. The experimental results showed that erosion-corrosion rate in flowing double phase 3.5% NaCl solution containing 5% sand increases markedly with increasing flow velocity. But it was not found that the erosion-corrosion rate-decreased region which happened in flowing single phase solution existed. The erosion-corrosion process of carbon steel in flowing liquid-solid double phase solution is still controlled by cathodic oxygen diffusion process. Once cathodic current was impressed on carbon steel, the erosion-corrosion rate of carbon steel decreases abruptly because the corrosion electrochemistry factor is restrained and the synergism is weakened. It was verified that corrosion electrochemical factor plays a dominant role in erosion-corrosion.

Key words： carbon steel flowing liquid/solid solution flow loop system erosion-corrosion corrosion electrochemi

收稿日期: 2003-01-30

ZTFLH:

TG172.9

通讯作者: 林玉珍

Corresponding author: Yuzhen Lin

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	田兴玲
	林玉珍
	刘景军
	雍兴跃
44.8K

引用本文:

田兴玲; 林玉珍; 刘景军; 雍兴跃 . 碳钢在液/固双相管流中磨损腐蚀的电化学行为[J]. 中国腐蚀与防护学报, 2004, 24(1): 48-51 .
Xingling Tian, Yuzhen Lin, Jingjun Liu, Xingyue Yong. Electrochemical Behavior in Erosion- Corrosion of Carbon Steel in liquid-Solid Double Phase Flow Loop. J Chin Soc Corr Pro, 2004, 24(1): 48-51 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I1/48

[1]McLauryBS ,ShiraziSA ,ShadleyJR ,RybickiEF .Howoperatingandenvironmentalconditionsaffecterosion[J].Corrosion,1999,34:1
[2]HeitsE .Chemo-mechanicaleffectofflowoncorrosion[J].Corrosion,1991,47(2):135
[3]FumioUmemura,TwruakiKawamoto.Influenceofvelocity,PHandtest ingmethodonerosioncorrosionrate[J].Anticorrosion,1985,34(7):175
[4]FumioUmemura,ShinjiMatukura,TeuakiKawamoto.Electrochemicalstudyonerosion-corrosionofcarbonsteelandstainlesssteel[J].BoshokuGijtsu,1987,36:627(梅村文夫,松仓伸二,川本辉明.碳素钢とステンレス钢のエロ一ジョン·コロ一ジョンに关する电气化学的考察[J].防食技术,1987,36:627)
[5]LinYuzhen.Progressinstudyonerosion-corrosionunderflowingcondi tion[J].TotalCorrosionControl,1996,10(4):1(林玉珍.在流动条件下磨损腐蚀的研究进展[J].全面腐蚀控制,1996,10(4):1)
[6]NesicS ,SolviGT ,EnerhaugJ .Comparisonoftherotatingcylinderandpipeflowtestsforflow-sensitivecarbondioxidecorrosion[J].Corro sion,1995,51(10):773
[7]BryanPoulson.Electrochemicalmeasurementsinflowingsolutions[J].Corros.Sci.,1983,23(4):391
[8]WeiBaoming.MetalCorrosionTheoryandApplication[M ].Beijing:ChemicalIndustryPress,1984:80,227(魏宝明.金属腐蚀理论及应用[M].北京:化学工业出版社,1984:80,227)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed