黄铜管腐蚀监测传感器的研制

尹立辉;宋诗哲

天津大学材料学院

Study on the Sensor for Monitoring Brass Tube Corrosion

Yin Lihui;Song Shizhe

全文: PDF(128 KB)

摘要: 设计制作了用于对电厂凝汽器H70/30黄铜管进行监测的传感器。采用电厂实际使用过和未经使用的黄铜管制作电解池，用制作的传感器测量了黄铜管的电化学阻抗谱和极化阻力。结果表明，该传感器可以用于对黄铜管的腐蚀进行监测。

关键词 ：黄铜, 腐蚀传感器, 电化学阻抗谱, 极化阻力

Abstract：A sensor for monitoring corrosion of brass tube of power station is designed and made. The Ag/AgCl wire is used as reference electrode and the pt-Ir alloy wire as assistant electrode. Insulatedly, the two electrodes are filled in a tailor-made EVA(polymer of ethylene and acetic acid ethylene) tube whose diameter is one millimeter. So the sensor can be put into long tube for monitoring .A simulation cell is made for simulating the sondition of power station. The used and not used brass tubes are cut into same length for making cell. The inside of brass tube is used as work electrode, the tap water is used as electrolyte. The sensor is applied to measure polarization resistance(Rp) of the two brass tubes of cell. The results show that the sensor can be used for monitoring the corrosion of brass tube.

Key words： brass corrosion sensor electrochemical impedance spectrum(EIS) polarization resistance

收稿日期: 2003-01-27

ZTFLH:

TG174

通讯作者: 尹立辉

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	尹立辉
	宋诗哲
44.8K

引用本文:

尹立辉; 宋诗哲 . 黄铜管腐蚀监测传感器的研制[J]. 中国腐蚀与防护学报, 2004, 24(1): 52-54 .
Yin Lihui, Song Shizhe. Study on the Sensor for Monitoring Brass Tube Corrosion. J Chin Soc Corr Pro, 2004, 24(1): 52-54 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I1/52

[1]DanWToenley,StevenJDuraneeau.On-lineelectrochemicalnoisecor rosionmonitoringinpotablewaterdistributionsystems[A].NACE 2002[C].Houston,Texas,PaperNO .02328
[2]MokWY ,DoughertyJ,JovancicevicV .Potentiostaticelectrochemicalnoiseforcorrosionmonitoring:generalandlocalizedcorrosion[A].NACE 2002[C].Houston,Texas,PaperNO .02335
[3]HabibK .In-situmonitoringofpittingcorrosionofcopperalloysbyholographicinterferometry[J].Corros.Sci.,1998,40(8):1435-1440
[4]ZhouBS .CorrosionandProtectionofMetalinIndustryCoolingWaterSystem[M].Beijing:ChemicalIndustryPress,1993:261(周本省.工业冷却水系统中金属的腐蚀与防护[M].北京:化学工业出版社,1993:261)
[5]SongSZ .CorrosionElectrochemistryStudyMethods[M].Beijing:Chemi calIndustryPress,1988:107-109(宋诗哲.腐蚀电化学研究方法[M ].北京:化学工业出版社,1988:107-109)

[1]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[2]	白苗苗, 白子恒, 蒋立, 张东玖, 姚琼, 魏丹, 董超芳, 肖葵. H62黄铜/TC4钛合金焊接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 159-166.
[3]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[4]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[5]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[6]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[7]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[8]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[9]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[10]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[11]	孟凡帝, 刘莉, 李瑛, 王福会. 用于原位检测在深海并压力交变环境中有机涂层电化学阻抗的预埋微电极研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.
[12]	王军, 冯超, 彭碧草, 谢亿, 张明华, 吴堂清. S450EW焊接接头在NaHSO₃溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 575-582.
[13]	王佳, 贾梦洋, 杨朝晖, 韩冰. 腐蚀电化学阻抗谱等效电路解析完备性研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 479-486.
[14]	陈振宁,陈日辉,潘金杰,滕艳娜,雍兴跃. L921A钢在3.5%NaCl溶液中的有机/无机复配缓蚀剂研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.
[15]	冯立, 张立功, 李思振, 郑大江, 林昌健, 董士刚. 柠檬酸铁浓度对镁合金微弧氧化黑色膜层微观结构及耐蚀性的影响[J]. 中国腐蚀与防护学报, 2017, 37(4): 360-365.

Viewed

Full text

Abstract

Cited

Shared

Discussed