316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀 |
何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春( ) |
长沙理工大学化学与食品工程学院 长沙 410114 |
|
Passivation and Pitting of 316L and HR-2 Stainless Steel in Hydrochloric Acid Liquid Membrane Environment |
HE Zhuang,WANG Xingping,LIU Zihan,SHENG Yaoquan,MI Mengxin,CHEN Lin,ZHANG Yan,LI Yuchun( ) |
School of Chemistry and Food Engineering, Changsha University of Science and Technology, Changsha 410114, China |
引用本文:
何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
Zhuang HE,
Xingping WANG,
Zihan LIU,
Yaoquan SHENG,
Mengxin MI,
Lin CHEN,
Yan ZHANG,
Yuchun LI.
Passivation and Pitting of 316L and HR-2 Stainless Steel in Hydrochloric Acid Liquid Membrane Environment. Journal of Chinese Society for Corrosion and protection, 2020, 40(1): 17-24.
链接本文:
https://www.jcscp.org/CN/10.11902/1005.4537.2019.221
或
https://www.jcscp.org/CN/Y2020/V40/I1/17
|
[1] | Wang Y L, Chen X, Wang J D, et al. Electrochemical behavior of 316L stainless steel in borate buffer solution with different pH [J]. J. Chin. Soc. Corros. Prot., 2017, 37: 162 | [1] | (王彦亮, 陈旭, 王际东等. 316L不锈钢在不同pH值硼酸溶液中的电化学行为研究 [J]. 中国腐蚀与防护学报, 2017, 37: 162) | [2] | Zhou D, Yang S C, Hou Y B. Cause analysis on corrosion and perforation for condenser of 316L stainless steel pipe [J]. Northeast Electr. Power Technol., 2016, 37(9): 24 | [2] | (周多, 杨少才, 侯亚波. 凝汽器316L不锈钢管腐蚀穿孔原因分析 [J]. 东北电力技术, 2016, 37(9): 24) | [3] | Chen Y, Chen X, Liu T, et al. Effect of potential on electrochemical corrosion behavior of 316L stainless steel in borate buffer solution [J]. J. Chin. Soc. Corros. Prot., 2015, 35: 137 | [3] | (陈宇, 陈旭, 刘彤等. 成膜电位对316L不锈钢在硼酸溶液中电化学行为的影响 [J]. 中国腐蚀与防护学报, 2015, 35: 137) | [4] | Yang L Q, Liu D X, Xie C Y, et al. Corrosion behavior of 316L and HR-2 stainless steels in ferric chloride solution [J]. Corros. Sci. Prot. Technol., 2017, 29: 117 | [4] | (杨柳青, 刘道新, 谢朝阳等. 氯化铁溶液中316L和HR-2不锈钢的腐蚀行为研究 [J]. 腐蚀科学与防护技术, 2017, 29: 117) | [5] | Lei H D, Huang W R, Guo P, et al. Preliminary inquiry of weldability and formation reason of porosity for laser beam welding of hydrogen resistant stainless steel [J]. Weld. Technol., 2002, 31(3): 8 | [5] | (雷华东, 黄文荣, 郭鹏等. 抗氢不锈钢的激光焊接性及气孔成因初探 [J]. 焊接技术, 2002, 31(3): 8) | [6] | Zuo Y, Wang H T, Zhao J M, et al. The effects of some anions on metastable pitting of 316L stainless steel [J]. Corros. Sci., 2002, 44: 13 | [7] | Liu X H, Wu X Q, Han E-H. Effects of temperature on lectrochemical corrosion of domestic nuclear-grade 316L stainless steel in Zn-injected aqueous environment [J]. Acta Metall. Sin., 2014, 50: 64 | [7] | (刘侠和, 吴欣强, 韩恩厚. 温度对国产核级316L不锈钢在加Zn水中电化学腐蚀性能的影响 [J]. 金属学报, 2014, 50: 64) | [8] | Li Y Y, Fan C G, Rong L J, et al. Hydrogen embrittlement resistance of austenitic alloys and aluminium alloys [J]. Acta Metall. Sin., 2010, 46: 1335 | [8] | (李依依, 范存淦, 戎利建等. 抗氢脆奥氏体钢及抗氢铝 [J]. 金属学报, 2010, 46: 1335) | [9] | Tseng C M, Tsai W T. Environmentally assisted cracking behavior of single and dual phase stainless steels in hot chloride solutions [J]. Mater. Chem. Phys., 2004, 84: 162 | [10] | Han M S, Park J C, Jang S K, et al. Effects of applied potential on SCC and HE for STS 316L in seawater [J]. Phys. Scr., 2010, 139: 014037 | [11] | Burstein G T, Pistorius P C, Mattin S P. The nucleation and growth of corrosion pits on stainless steel [J]. Corros. Sci., 1993, 35: 57 | [12] | Pride S T, Scully J R, Hudson J L. Metastable pitting of aluminum and criteria for the transition to stable pit growth [J]. J. Electrochem. Soc., 1994, 141: 3028 | [13] | Chen Z, Yu Q, Liao D H, et al. Surface activity of HR-2 stainless steel in acid solution with SECM [J]. J. Chin. Soc. Corros. Prot., 2013, 33: 54 | [13] | (陈阵, 余强, 廖登辉等. 酸性介质中HR-2不锈钢表面活性的SECM三维图像表征研究 [J]. 中国腐蚀与防护学报, 2013, 33: 54) | [14] | Feng X G, Zuo Y, Tang Y M, et al. The degradation of passive film on carbon steel in concrete pore solution under compressive and tensile stresses [J]. Electrochim. Acta, 2011, 58: 258 | [15] | Tan H L, Zhou C, Liu X H, et al. Effect of Cr on corrosion resistance of Q420 steel in atmosphere with high salinity [J]. J. Chin. Soc. Corros. Prot., 2017, 37: 267 | [15] | (谭何灵, 周成, 刘希辉等. Cr对Q420钢在高盐度大气环境下耐蚀性的影响 [J]. 中国腐蚀与防护学报, 2017, 37: 267) | [16] | Liu Z Y, Du C W, Zhang X, et al. Effect of pH value on stress corrosion cracking of X70 pipeline steel in acidic soil environment [J]. Acta Metall. Sin. (Engl. Lett)., 2013, 26: 489 | [17] | Marshakov A I, Ignatenko V E, Bogdanov R I, et al. Effect of electrolyte composition on crack growth rate in pipeline steel [J]. Corros. Sci., 2014, 83: 209 | [18] | Pokhmurs'kyi V I. Adsorption-electrochemical theory of the corrosion fatigue of metals [J]. Mater. Sci., 2010, 46: 156 |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|