O,O'-二（环己基）二硫代磷酸-N,N-二乙铵对Q235钢在硫酸溶液中的缓蚀性能研究

谢斌^1,2,赖川³,邹立科²,何林芯²,伍一峥²,黄炎俊³,相阳光³

1. 材料腐蚀与防护四川省高校重点实验室自贡 643000
2. 四川理工学院功能材料研究所自贡 643000
3. 四川理工学院材料与化学工程学院自贡 643000

INHIBITION OF N,N-DIETHYLAMMONIUM O,O'-DICYCLOHEXYLDITHIOPHOSPHATE FOR Q235 STEEL IN SULFURIC SOLUTION

XIE Bin^1,2, LAI Chuan³, ZOU Like², HE Linxin², WU Yizheng², HUANG Yanjun³, XIANG Yangguang³

1. University Key Laboratory of Material Corrosion and Protection of Sichuan Province, Zigong 643000
2. Institute of Functionalized Materials, Sichuan University of Science & Engineering, Zigong 643000
3. School of Material and Chemical Engineering, Sichuan University of Science & Engineering, Zigong 643000

全文: PDF(1068 KB)

摘要: 合成了新型酸洗缓蚀剂O,O'-二（环己基）二硫代磷酸-N,N-二乙铵（EDCDP），通过失重和电化学方法研究EDCDP在H₂SO₄溶液中对Q235钢的缓蚀性能。结果表明，(27±1)℃，5% H₂SO₄溶液中，EDCDP质量浓度为100 mg/L时，缓蚀率为97.32%；在 Q235钢表面的吸附规律符合Langmuir吸附等温式，属于自发进行的化学吸附。EDCDP是一种受H₂SO₄浓度、温度和待测时间影响较小的混合型缓蚀剂。

关键词 ： O,O'-二烃基二硫代磷酸盐, H₂SO₄, 缓蚀剂, Q235钢, 吸附, 缓蚀率

Abstract：A new corrosion inhibitor N,N-diethylammonium O,O' -dicyclohexyldithiophosphate (EDCDP) has been synthesized. The inhibition effect of EDCDP against the corrosion of Q235 steel in H₂SO₄ solution was studied by mass loss, potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) methods. mass loss shows that the inhibition efficiency is up to 97.32 % at the inhibitor concentration of 100 mg/L in 5 % H₂SO₄solution. The adsorption of EDCDP on Q235 steel surface obeys the Langmuir's isotherm. Polarization curves indicate that the EDCDP is a mixed type inhibitor. The inhibition efficiency of EDCDP is less impact by concentration of H₂SO₄, temperature and immersion time.

Key words： O,O'-dialkyldithiophosphate H₂SO₄ corrosion inhibitor Q235 steel adsorption inhibition efficiency

收稿日期: 2010-03-29

ZTFLH:

TG174.42

基金资助:

四川省教育厅重点项目（09ZA057）、材料腐蚀与防护四川省高校重点实验室重点项目（2008CL03）、四川省科技厅应用基础项目（2009JY0072）及泸州老窖科研奖学金（09ljzk10）资助

通讯作者: 谢斌 E-mail: xiebinqhg@sina.com.cn

作者简介: 谢斌，男，1965年生，教授，硕士，研究方向为有机合成和缓蚀剂

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	谢斌
	赖川
	邹立科
	何林芯
	伍一峥
	黄炎俊
	相阳光
44.8K

引用本文:

谢斌,赖川,邹立科,何林芯,伍一峥,黄炎俊,相阳光. O,O'-二（环己基）二硫代磷酸-N,N-二乙铵对Q235钢在硫酸溶液中的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2011, 31(3): 225-230.
XIE Bin, LAI Chuan, ZOU Li-Ke, HE Lin-Xin, WU Yi-Zheng, HUANG Tan-Jun, XIANG Yang-Guang. INHIBITION OF N,N-DIETHYLAMMONIUM O,O'-DICYCLOHEXYLDITHIOPHOSPHATE FOR Q235 STEEL IN SULFURIC SOLUTION. J Chin Soc Corr Pro, 2011, 31(3): 225-230.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I3/225

[1] Tang B, Chen X Y. Study of corrosion inhibitors in acid pickling [J]. Clean World, 2006, 22(2): 22-28

    (汤兵, 陈欣义. 酸洗过程中的缓蚀剂 [J]. 清洗世界, 2006, 22(2): 22-28)

[2] Zhang T S. Corrosion Inhibitors [M]. Beijing: Chemical Industry Press, 2001

    (张天胜．缓蚀剂 [M]. 北京: 化学工业出版社, 2001)

[3] Yu G J, Tang B. Electrochemical methods of inhibitor research [J]. J. Chin. Soc. Corros. Prot., 2009, 29(1): 76-80

    (余国骏, 汤兵. 缓蚀剂研究中的电化学方法 [J]. 中国腐蚀与防护学报, 2009, 29(1): 76-80)

[4] Chen Y, Tang Y M, Yang W Z, et al. Inhibition of 3,5-bis(2-thienyl)-4-amino-1,2,4-triazole on copper in HCl media [J]. Corros. Soc. Prot. Techno1., 2009, 21(4): 406-409

    (陈云, 唐永明, 杨文忠等. 盐酸介质中3,5-二(2-噻吩基)-1,2,4-三唑(2-TAT)对紫铜的缓蚀作用 [J].腐蚀科学与防护技术, 2009, 21(4): 406-409)

[5] Hu S, Kang X Y, Fu C Y. Rice bran extraction used as pickling inhibitor in hydrogen chloride acid [J]. J.Chin. Soc. Corros. Prot., 2009, 29(2): 149-153

    (胡胜, 康笑阳, 付朝阳. 米糠提取液作为盐酸酸洗缓蚀剂的研究 [J]. 中国腐蚀与防护学报, 2009, 29(2): 149-153)

[6] Ajmal M, Mideen A S, Quraishi M A.2-hydrazino-6-methyl-ben- zothiazole as an effective inhibitor for the corrosion of mild steel in acidic solutions[J]. Corros. Sci., 1994; 36(1): 79-84

[7] Hong T, Sun Y H, Jepson W P. Study on corrosion inhibitor in large pipelines under multiphase flow using EIS [J]. Corros. Sci., 2002, 44(1): 101-112

[8] Siddiqui R A, Abdullah H A. Hydrogen embrittlement in 0.31 % carbon steel for petrochemical application [J]. J. Mater. Prot. Technol., 2005, 170(1-2): 430-435

[9] Bentiss F, Bouanis M, Mernari B, et al. Understanding the adsorption of 4H-1,2,4-triazole derivatives on mild steel surface in molar hydrochloric acid [J]. Appl.Surf. Sci., 2007, 253: 3696-3704

[10] Xie B, Wu S Y. Synthesis and characterization of (5,7,7,12, 14,14-hexamethyl-1,4,8,11-etraazacyclotetradeca-4,1-die-no) nickel bis (O,O$^\prime$-dialkyldithiophosphate) [J].Chem. J. Chin. Univ., 1998, 19(1): 74-77

     (谢斌, 吴士业. (5,7,7,12,14,14-六甲基-1,4,8,11-四氮杂环十四-4,11-二烯合)镍双(O,O'-二烃基二硫代磷酸酯)的合成与研究 [J]. 高等学校化学学报, 1998, 19(1): 74-77)

[11] Unnikrishnan R, Jain M C, Harinarayan A K, et al. Additive-additive interaction: an XPS study of the effect of ZDDP on the AW/EP characteristics of molybdenum based additives [J]. Wear, 2002, 252(3): 240-249

[12] Quraishi M A, Sharma H K. 4-Amino-3-butyl-5-mercapto- 1,2,4-triazole: a new corrosion inhibitor for mild steel in sulphuric acid [J]. Mater. Chem.Phys., 2002, 78: 18-28

[13] Shukla S K, Quraishi M A. The effects of pharmaceutically active compound doxycycline on the corrosion of mild steel in hydrochloric acid solution [J]. Corros. Sci., 2010, 52: 314-321

[1]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[2]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[4]	邵明鲁, 刘德新, 朱彤宇, 廖碧朝. 乌洛托品季铵盐缓蚀剂的合成与复配研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 244-250.
[5]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[6]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[7]	李向红, 邓书端, 徐昕. 木薯淀粉三元接枝共聚物对钢在H₂SO₄溶液中的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 105-114.
[8]	吕祥鸿,张晔,闫亚丽,侯娟,李健,王晨. 两种新型曼尼希碱缓蚀剂的性能及吸附行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 31-37.
[9]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[10]	刘建国,高歌,徐亚洲,李自力,季菀然. 咪唑啉类衍生物缓蚀性能研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 523-532.
[11]	李亚琼,马景灵,王广欣,朱宇杰,宋永发,张景丽. NaPO₃与SDBS缓蚀剂对AZ31镁合金空气电池在NaCl电解液中放电性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 587-593.
[12]	孔佩佩, 陈娜丽, 白德忠, 王跃毅, 卢勇, 冯辉霞. 壳聚糖及其衍生物的制备与缓蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(5): 409-414.
[13]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[14]	刘峥, 李海莹, 王浩, 赵永, 谢思维, 张淑芬. 分子动力学模拟水溶液中席夫碱基表面活性剂在Zn表面的吸附行为[J]. 中国腐蚀与防护学报, 2018, 38(4): 381-390.
[15]	彭晚军, 丁纪恒, 陈浩, 余海斌. 生物基缓蚀剂糠醇缩水甘油醚的缓蚀性能及机理[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.

Viewed

Full text

Abstract

Cited

Shared

Discussed