黄磷尾气燃气锅炉的腐蚀行为

中国腐蚀与防护学报

2011, Vol. 31

Issue (1): 51-55

研究报告

本期目录 | 过刊浏览

黄磷尾气燃气锅炉的腐蚀行为

郜华萍^1,吴飞¹,龙晋明¹,介星迪¹,张冬平²

1. 昆明理工大学材料科学与工程程学院昆明 650093
2. 昆明锅炉有限责任公司昆明 650217

ANALYSIS ON CORROSION BEHAVIORS OF THE BOILER FOR COMBUSTING WITH YELLOW PHOSPHORIC TAIL GAS

GAO Huaping¹, WU Fei¹, LONG Jinming¹, JIE Xingdi¹, ZHANG Dongping²

1. School of Materials Science and Engineering, Kunming University of Science and Technology, Kunming 650093
2. Kunming Boiler Co., Ltd., Kunming 650217

全文: PDF(1551 KB)

摘要: 采用实验室加速腐蚀实验对比研究316L、304不锈钢和20^#锅炉钢(记为20g)在模拟黄磷尾气腐蚀环境条件下的腐蚀性能。结果表明，316L不锈钢的耐蚀性要优于304不锈钢和20g，在250℃~300℃时304和316L不锈钢均发生酸蒸汽的露点腐蚀，且 304不锈钢出现较为严重的孔蚀现象。

关键词 ：黄磷尾气, 锅炉, 露点腐蚀, 不锈钢, 孔蚀

Abstract：The corrosion properties of 316L, 304 stainless steel and 20^# boiler steel (20g) in a simulated corrosive atmosphere were investigated by means of accelerated corrosion test. The results show that corrosion rate of 316L was significantly lower than that of 304 and 20g in the simulated atmosphere. From temperature 250℃ to 300℃, the acid dew point corrosion became serious. Cavities were observed in the surface of 304 after the dew point corrosion, at where occurred pitting corrosion.

Key words： yellow phosphoric tail gas boiler dew point corrosion stainless steel pitting corrosion

收稿日期: 2009-09-17

ZTFLH:

TQ126.35

基金资助:

云南省省院省校合作项目（2006YX22）和科技型中小企业技术创新基金项目（07C26215301967）资助

通讯作者: 郜华萍 E-mail: ynkmghp@263.net

Corresponding author: GAO Huaping E-mail: ynkmghp@263.net

作者简介: 郜华萍，女，1962年生，研究员，研究方向为环境工程

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	吴飞
	龙晋明
	郜华萍
	介星迪
	张冬平
44.8K

引用本文:

郜华萍,吴飞,龙晋明,介星迪,张冬平. 黄磷尾气燃气锅炉的腐蚀行为[J]. 中国腐蚀与防护学报, 2011, 31(1): 51-55.
WU Fei, MANG Jin-Meng, GAO Hua-Ping, GE Xing-Di, ZHANG Dong-Beng. ANALYSIS ON CORROSION BEHAVIORS OF THE BOILER FOR COMBUSTING WITH YELLOW PHOSPHORIC TAIL GAS. J Chin Soc Corr Pro, 2011, 31(1): 51-55.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I1/51

[1] He H M. Development Direction and Measures of Phosphorus Chemicals in China [M]. Beijing: Chemical Industry Press,2007.19-21

    (何浩明. 对中国磷化工业发展的思考 [M]. 北京: 化学工业出版社, 2007. 19-21)

[2] Zhou S B. Conventional alloy used in WPA production [J]. Phosphat.Compd. Fert., 2005, 20(3): 64-67

    (周绍彪. 湿法磷酸生产中常用的合金材料 [J]. 磷肥与复肥, 2005, 20(3): 64-67)

[3] Lin C J, Xie Z X, Tian Z W. Electrochemical scanning tunneling microscope studies of initial pitting corrosion 18/8 stainless steel [J]. Corros. Sci. Prot. Technol., 1997, 9(4): 259-264)

    (林昌健, 谢兆雄, 田昭武. 不锈钢点腐蚀发生的早期过程 [J].腐蚀科学与防护技术, 1997, 9(4): 259-264)

[4] Al-Hashem A, Caceres P G, Abdullah A. Cavitation corrosion of duplex stainless steel in sea water [J]. Corrosion, 1997, 53(2): 103-113

[5] Guo Q S, Huang Y C.Wear-corrosion behavior of high Cr-Mo alloys in wet process for phosphoric acid production [J]. Corros. Sci. Prot.Technol., 1994, 6(4): 364-366

    (郭清胜, 黄永昌. 高铬钼不锈钢在湿法磷酸中磨损腐蚀行为 [J]. 腐蚀科学与防护技术, 1994, 6(4): 364-366)

[6] Mobin M, Malik A U. Investigations on the failure of economizer tubes in a high-pressure boiler [J]. J. Failure Anal.Prev., 2008. 69-74

[7] Uusitalo M A, Vuoristo P M J, Mantyla T A. High temperature corrosion of coatings and boiler steels in oxidizing chlorine-containing atmosphere [J]. Mater. Sci. Eng., 2002, A322: 1-10

[8] Wang R G, Wei Y, Zhang Q L, et al. Study on SCC behavior of austenitic stainless steels SUS316 and SUS316L in H₂S saturated aqueous solutions containing Cl^- [J]. J. Chin. Soc. Corros. Prot., 2000, 20(1): 48-53

    (王荣光, 魏云, 张清廉等. 奥氏体不锈钢SUS316及SUS316L在含Cl^-的饱和H₂S水溶液中的应力腐蚀行为研究 [J].中国腐蚀与防护学报, 2000, 20(1): 48-53)

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[7]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	刘志峰,朱志平,石纯,黄赵鑫. 载流法制备硫酸露点腐蚀模拟气体的试验研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 1-9.
[10]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[11]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[12]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[13]	付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[14]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[15]	李雨,关蕾,王冠,张波,柯伟. 机械应力对不锈钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 215-226.

Viewed

Full text

Abstract

Cited

Shared

Discussed