西部油田油管腐蚀结垢机理研究

万里平;孟英峰

中国石油天然气集团公司石油管材研究所

MECHANISM OF CORROSION AND SCALE DEPOSIT OF TUBES IN WESTERN OILFIELD

;

中国石油天然气集团公司石油管材研究所

全文: PDF(316 KB)

摘要: 通过对西部某油田油管腐蚀结垢现状调查、单井采出液成分分析和垢样ＸＲＤ分析，结合油管结垢趋势预测及室内高温高压腐蚀试验，探讨了油管腐蚀结垢机理。结果表明：垢物主要是ＣａＣＯ３、ＣａＳＯ４和铁锈产物，在结垢出现的同时伴随油管腐蚀的发生。影响油管腐蚀结垢的主要因素是采出液中含有丰富的的Ｃａ２＋、ＨＣＯ３－、Ｃｌ－以及原油伴生气中的ＣＯ２含量较多。该油田存在严重的腐蚀结垢趋势。

关键词 ：腐蚀, 结垢, 油管, 防腐, 防垢

Abstract：Corrosion and scale deposit reasons of tubes were discussed, through the in-situ investigation, pro?鄄duced water composition analysis, XRD analysis of scaling samples of single well in Western oilfield, combining scaling prediction and corrosion rate monitor. The results show that scaling types are mainly CaCO3?CaSO4 and iron rust, scaling in connection with corrosion. Predominating factors affecting corrosion and scaling of tubing are abundant in Ca2+?HCO3-?Cl- containing in produced water and CO2 exiting in accompanying gas with crude oil. Severe corrosion and scaling of tubes were found in this oilfield.

Key words： corrosion scale deposit tube anti-corrosion scaling control

收稿日期: 2006-02-21

ZTFLH:

TG172

通讯作者: 万里平 E-mail: wanlp@tgrc.org

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	万里平
	孟英峰
44.8K

引用本文:

万里平; 孟英峰 . 西部油田油管腐蚀结垢机理研究[J]. 中国腐蚀与防护学报, 2007, 27(4): 247-251 .
. MECHANISM OF CORROSION AND SCALE DEPOSIT OF TUBES IN WESTERN OILFIELD. J Chin Soc Corr Pro, 2007, 27(4): 247-251 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2007/V27/I4/247

[1]Zhang Y,Zhang N S,Wu J Q.Scaling prediction and software devel-opment in Huachi oilfield[J].Special Oil&Gas Reservoir,2004,11(6):100-102(张益,张宁生,吴金桥.华池油田结垢预测及软件开发[J].特种油气藏,2004,11(6):100-102)
[2]Li J P,Zhao G X,Hao S M.The study on static corrosion of oil thimble used in Tarim oil field[J].J.Chin.Soc.Corros.Prot.,2004,24(4):230-233(李建平,赵国仙,郝士明.塔里木油田用油套管钢的静态腐蚀研究[J].中国腐蚀与防护学报,2004,24(4):230-233)
[3]Wu S L,Cui Z D,Li C F.Study on corrosion of oil tubes in carbon dioxide saturated crude oil/water mixtures[J].J.Chin.Soc.Corros.Prot.,2003,23(6):340-344(吴水林,崔振铎,李春福等.油管钢在饱和二氧化碳模拟油田液中的腐蚀研究[J].中国腐蚀与防护学报,2003,23(6):340-344)
[4]Nesi S,John P,Vrhova M.CO2corrosion of carbon steel-from mech-anism to empirical modeling[J].Corros.Rev.,1997,15:112-126
[5]Eugenio L P,Lucrezia S.Corrosion and environmental cracking e-valution of high density brines for use in HPHT fields[A].SPE97593High Pressure/High Temperature Sour Well Design Application Technology Workshop[C].The Woodland,Texas,2005,5
[6]Gunaltun Y.Carbon dioxide corrosion in oil wells[A].Middle East Oil Show[C].SPE21330Bahrain,1991,11
[7]Skillman H F,McDonald J P,Stiff H A.A simple,accurate,fast method for calculating calcium sulfate solubility in oilfield brine[A].API Spring Meeting of the Southwestern District[C].Texas,1969,3
[8]Zhu Y W,Zhao Z Z,Ju Q Y.Scaling Mechanism and Prevention Technology of Oilfield Development[M].Xi'an:Science Technology Press of Shannxi,1995(朱义吾,赵作滋,巨全义.油田开发中的结垢机理及其防治技术[M].西安:陕西科学技术出版社,1995)
[9]Chen D C,Liu J R,Wu X D.Models for predicting paraffin deposi-tion profile in waxy oil wellbore[J].J.Univ.Petroleum China,1999,23(4):36-39(陈德春,刘均荣,吴晓东.含蜡原油井筒结蜡剖面的预测模型[J].石油大学学报,1999,23(4):36-39)
[10]Yin X Q,Wu J Z,Wang Z L.Analysis and prediction of scaling mechanism of CaCO3from oilfield injection waters[J].PetroleumExploration and Development,2002,29(3):85-87(尹先清,伍家忠,王正良.油田注入水碳酸钙垢结垢机理分析与结垢预测[J].石油勘探与开发,2002,29(3):85-87)
[11]DuZG.ResearchondescalingandanticorrosionofwellboreinQian-miqiao oilfield[D].Chengdou:Southwest Petroleum University,2002(杜志广.千米桥地区井筒除垢防腐技术研究[D].成都:西南石油大学,2002)

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[4]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[5]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[6]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[7]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[8]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[10]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed