温度对P110钢CO2腐蚀行为的影响

中国腐蚀与防护学报

2005, Vol. 25

Issue (2): 93-96

研究报告

本期目录 | 过刊浏览

温度对P110钢CO2腐蚀行为的影响

赵国仙;吕祥鸿;李鹤林;路民旭

西安交通大学材料科学与工程系

EFFECT OF TEMPERATURE ON CO2 CORROSION BEHAVIOUR OF P110 STEEL

Guoxian Zhao;Xianghong Lv;Helin Li;Minxv Lu

西安交通大学材料科学与工程系

全文: PDF(166 KB)

摘要: 在模拟油田实际腐蚀环境中研究了温度对P110钢CO2腐蚀行为的影响。用SEM、XRD等分析了在不同温度条件下材料表面腐蚀产物膜的形貌以及对腐蚀速率和腐蚀形态的影响。研究结果表明，40℃时表层腐蚀产物类似于疏松的土壤，少且很松散地附着在材料表面，成份主要是溶液中沉积的KCL。90℃时腐蚀产物主要是钙铁镁的碳酸盐和少量的KCl和Fe2O3，腐蚀产物呈颗粒状，较致密但是膜层中含有大量的孔洞。140℃时，试样表层腐蚀产物呈致密的粘土形貌、下层腐蚀产物仍是颗粒状，产物层致密，成份主要是FeCO3和KCl。不同温度下不同的腐蚀产物形貌造成随温度升高，材料的平均腐蚀速率在90℃时出现峰值。

关键词 ： CO2腐蚀, P110钢, 腐蚀产物膜, 腐蚀速率, 腐蚀

Abstract：Influences of temperature on CO2 corrosion behaviors of P110 steel were studied in stimulated oilfield environments. Morphologies of scales and their effects on corrosion rate and corrosion shape were analyzed by SEM and XRD. The results showed, at 40℃, corrosion products were similar to loosen soil, few and hanging on the surface of the material composed by deposited KCl. In 90℃, corrosion products were grains, compact and much holes in it, constituted by calcium/magnesium/iron carbonate and few KCl and Fe2O3. In 140℃, corrosion products were in the similar morphology as compact clay in the outer layer and grains in the inner layer, made up of FeCO3 and KCl. The phenomena of different morphology in different temperature resulted in that the maximal corrosion rate presented in 90℃.

Key words： CO2 corrosion P110 steel corrosion scale corrosion rate temperature

收稿日期: 2003-10-15

ZTFLH:

TG172

通讯作者: 赵国仙 E-mail: zhaoguoxianxian@sohu.com

Corresponding author: Guoxian Zhao E-mail: zhaoguoxianxian@sohu.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	赵国仙
	吕祥鸿
	李鹤林
	路民旭
44.8K

引用本文:

赵国仙; 吕祥鸿; 李鹤林; 路民旭 . 温度对P110钢CO2腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2005, 25(2): 93-96 .
Guoxian Zhao, Xianghong Lv, Helin Li, Minxv Lu. EFFECT OF TEMPERATURE ON CO2 CORROSION BEHAVIOUR OF P110 STEEL. J Chin Soc Corr Pro, 2005, 25(2): 93-96 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I2/93

[1]De,WaardC ,LotzU ,MilliamsDE .PredictionmodelforCO2 cor rosionengineeringinwetnaturalgaspipeline[A ].Corrosion/91,Corrosion,1991,47(12):976
[2]DugstadA ,LundeL ,VidemK .ParametricstudyofCO2 corrosionofcarbonsteel[A].Corrosion/94[C].NACE ,1994,14
[3]McMahonAJ ,PaisleyDME .Corrosionpredictionmodeling-aguidetotheuseofcorrosionpredictionmodelsforriskassessmentinoilandgasproductionandtransportationfacilities[A].ReportNo.ESR96.ER .066[C].BPInternational,Sunbury,1997
[4]HalvorsenAMK ,SontvedtT .CO2 corrosionmodelforcarbonsteelincludingawallshearstressmodelformultiphaseflowandlimitsforproductionratetoavoidmesaattack[A].Corrosion/99[C].NACE ,1999,42
[5]NesicS ,PostlethwaiteJ ,NyborgR .AmechanisticmodelforCO2corrosion[A].Corrosion/2001[C].NACE ,2001,40
[6]LindaGSGray,BruceGAnderson.EffectofpHandtemperatureonthemechanismofcarbonsteelcorrosionbyaqueouscarbondiox ide[A].Corrosion/90[C].NACE ,1990,40
[7]MishraB ,etal.PredictionofmicrostructuraleffectonthecorrosionofpipelinesteelsinCO2-brinesolution[A].Corrosion/93[C].NACE ,1993,90
[8]HauslerRH ,StegmannDW .CO2 corrosionanditspreventionbychemicalinhibitioninoilandgasproduction[A].Corrosion/88[C].NACE ,1988,363
[9]IkedaA ,UedaM ,MukaiS .AdvancedinCO2 corrosion,EditedbyBurke,PAetal

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed