中国腐蚀与防护学报  2003, Vol. 23 Issue (5): 316-320     
  综述 本期目录 | 过刊浏览 |
铝-锂合金腐蚀性能研究综述
李劲风;张昭;张鉴清
中南大学材料科学与工程学院
REVIEW OF RESEARCH ON CORROSION BEHAVIOR OF Al-Li ALLOYS
Jinfeng Li;Zhao Zhang;Jianjing Zhang
中南大学材料科学与工程学院
全文: PDF(173 KB)  
摘要: 综述了铝-锂合金孔蚀、晶间腐蚀、应力腐蚀断裂(SCC)及剥 蚀的研究现状,阐述了加工状态、热处理、显微组织及腐蚀介质对一些铝-锂合金孔蚀及晶 间腐蚀行为与SCC敏感性的影响及其影响机制.同时报道了一些研究铝-锂合金剥蚀的新方法 ,并提出了进一步研究的方向.
关键词 铝-锂合金腐蚀剥蚀    
Abstract:Current research status of pitting corrosion,interg ranular corrosion,stress-corrosion cracking(SCC) and exfoliation corrosion of Al -Li alloys are reviewed in this paper.The effect of processing,heat treatment,mi crostructure and corrosion medium on the pitting and intergranular corrosion beh avior and SCC susceptibility of some Al-Li alloys are given,the correlated effec t mechanisms are described and some new test methods for Al-Li alloy exfoliation are reported.Meanwhile,the next research objective is outlined.
Key wordsAl-Li alloys    corrosion    exfoliation
收稿日期: 2002-01-30     
ZTFLH:  TG174.3  
通讯作者: 李劲风     E-mail: jfli2000@163.net
Corresponding author: Jinfeng Li     E-mail: jfli2000@163.net

引用本文:

李劲风; 张昭; 张鉴清 . 铝-锂合金腐蚀性能研究综述[J]. 中国腐蚀与防护学报, 2003, 23(5): 316-320 .
Jinfeng Li, Zhao Zhang, Jianjing Zhang. REVIEW OF RESEARCH ON CORROSION BEHAVIOR OF Al-Li ALLOYS. J Chin Soc Corr Pro, 2003, 23(5): 316-320 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2003/V23/I5/316

[1]ZhangLingquan.Currentstatusofaluminum-lithiumalloys[J].LightAlloysFabricationTechnol.,1986,(7):23-28(张灵泉.铝-锂合金的发展现状[J].轻合金加工技术,1986,(7):23-28)
[2]XiaDeshun.Developmentandapplicationofaluminum-lithiumal loys[J].AstronavigationCraft.,1998,(1):50-54(夏德顺.铝锂合金的发展和应用[J].航天工艺,1998,(1):50-54)
[3]QiuHuizhong.Al-LialloysandtheirmanufacturingtechniquesforaerospaceproductsoutsideChina[J].AerospaceMater.Technol.,1998,(4):39-43(邱惠中.国外Al-Li合金及其航天产品的制造技术[J].宇航材料工艺,1998,(4):39-43)
[4]TianRongzhang,WangZhutang.AluminumAlloysandTheirFabri cation[M].Changsha:CentralSouthUniversityPublicationPress,2000.(田荣璋,王祝堂主编.铝合金及其加工技术[M ].长沙:中南大学出版社,2000)
[5]LiuJing’an,ZhuXianwen.Developmentandapplicationofalu minum-lithiumalloys[J].LightAlloyFabricationTechnol.,1996,24(5):2-5,10(刘静安,朱献文.Al-Li合金的发展与应用[J].轻合金加工技术,1996,24(5):2-5,10)
[6]ColvinEL ,CahhenGL ,StonerGE .EffectofgermaniumadditionsonthecorrosionbehaviorofanAl-Lialloy[J].Corrosion,1986,42(7):416-421
[7]NiskanenP ,SandersTH ,RinkerJG ,etal.Corrosionofaluminumalloyscontaininglithium[J].Corros.Sci.,1982,22(4):283-304
[8]MoranJP ,StarkeEA ,StonerGE ,etal.Theinfluenceofcomposi tionandmicrostructureonthecorrosionbehavioroftwoAlLiXal loys[J].Corrosion,1987,43(6):374-382
[9]BuchheitRG ,MoranJP ,StonerGE .Electrochemic
[21]JinkerJG ,MaraekMM ,SandersTH .Microstructures,toughnesssionofAl-2%Li-3%Cualloys[J].Corrosion,1994,50(2):120-130
[10]BuchheitRG ,MoranJP ,StonerGE .Localizedcorrosionbehaviorofalloy2090-theroleofmicrostructureheterogeneity[J].Corro sion,1990,46(8):610-617
[11]KumaiC ,KusinskiJ,ThomasG ,etal.Influenceofagingat200℃onthecorrosionresistanceofAl-LiandAl-Cu-Lialloys[J].Corrosion,1989,45(4):294-302
[12]AmbatR ,DwarakadasaES .Effectofchlorideionconcentrationduringcorrosionofmediumstrengthaluminumalloys8090,2091and2014[J].Br.Corros.J .,1993,28(2):142-148
[13]AmbatR ,DwarakadasaES .TheinfluenceofpHonthecorrosionofmediumstrengthaerospacealloys8090,2091and2014[J].Cor ros.Sci.,1992,32(5):681-690
[14]SrivastanTS ,SudarshanTS ,BobeckGE .CorrosionbehaviorofaquaternaryAl-Li-Cu-Mgalloyin3.5%NaClsolution[J].Br.Corros.J .,1990,25(1):39-45
[15]TraversoP ,BeccariaAM ,PoggiG .Corrosionbehaviorofalu minum-lithium8090-T81inseawater[J].Br.Corros.J.,1995,30(3):227-231
[16]MurthyKSN ,AmbatR ,DwarakadasaES .Theroleofmetalcationsinthecorrosionbehaviorof8090-T851alloyinapH 2.0solution[J].Corros.Sci.,1994,36(10):1765-1775
[17]MurthyKSN ,DwarakadasaES .RoleofLi+ionsincorrosionbe haviorof8090Al-LialloyandaluminuminpH 12aqueoussolu tions[J].Br.Corros.J.,1995,30(2):111-115
[18]MarsacS ,MankowskiG ,DabosiF .Stresscorrosioncrackingbe haviorof2091Al-Lialloyinsulphateandchloridecontainingso lutions[J].Br.Corros.J.,1992,27(1):50-58
[19]BurleighTD .Thepostulatedmechanismsofstresscorrosioncrackingofaluminumalloys,areviewoftheliterature1980-1989[J].Corrosion,1991,47(2):89-98
[20]DorawrdRC ,HasseKR .StresscorrosioncharacteristicsofAlCuLiAA2090alloy[J].Corrosion,1988,44(12):932-941
[21]JinkerJG ,MaraekMM ,SandersTH .Microstructures,toughnessandstresscorrosioncrackingbehaviorofaluminumalloy2020[J].Mater.Sci.Eng.,1984,64:203-221
[22]MeletisEI.Microstructureandstresscorrosioncrackingrelation shipinanAl-Li-Cu-Zralloy[J].Mater.Sci.Eng.,1987,93:235-245
[23]LumsdenJB ,AllenAT .ThestresscorrosioncrackingofAlLial loy8090[J].Corros.Sci.,1988,44(4):527-532
[24]DorwardRC .InfluenceofgrainstructureonstresscorrosioncrackingandtensilepropertiesofAl-2Li-2Cu-1.5Mgalloysheet[J].Corrosion,1990,46(4):348-352
[25]BuisA ,SchijveJ.StresscorrosioncrackingbehaviorofAl-Li2090-T83alloyinartificialseawater[J].Corrosion,1992,48(11):898-909
[26]CondeA ,FernandezBJ,DamboreneaJJde.CharacterizationoftheSCCbehaviorof8090Al-Lialloybymeansoftheslow-strain-ratetechnique[J].Corros.Sci.,1998,40(1):91-102
[27]LiDi,ZuoShangzhi,GuoBaolan.StudyontheexfoliationcorrosionofLY12alloy[J].J .Chin.Soc.Corros.Prot.,1995,15(3):203-208(李荻,左尚志,郭宝兰.LY12铝合金剥蚀行为的研究[J].中国腐蚀与防护学报,1995,15(3):203-208)
[28]ZhengZiqiao.Processingofthe2 ndNationalAluminum-Lithiumalloys[C].Changsha:CentralSouthUniversityofTechnologyPub licationPress,1993(郑子樵主编.第二届全国铝锂合金会议论文集[C].长沙:中南工业大学出版社,1993)
[29]Standardtestmethodforexfoliationcorrosionsusceptibilityin2×××and7×××seriesaluminumalloys(EXCOTest)[S].ASTM 34-79.
[30]KellyDJ,RobinsonMJ.InfluenceofheattreatmentandgrainshapeonexfoliationcorrosionofAl-Lialloy8090[J].Corrosion,1993,49(10):787-795
[31]HabashiM ,BonteE ,GallandJ ,etal.Quantitativemeasurementsofthedegreeofexfoliationonaluminumalloys[J].Corros.Sci.,1993,35(4):168-183
[32]CondeA ,DamboneaJde.Electrochemicalmodellingofexfoliationcorrosionbehaviorof8090alloy[J].Electrochimi.Acta,1998,43(8):849-860
[1] 董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2] 唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3] 韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4] 张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6] 左勇, 曹明鹏, 申淼, 杨新梅. MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7] 王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9] 郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10] 于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11] 贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12] 赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13] 马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14] 岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15] 艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.