突扩管条件下材料的冲刷腐蚀机理研究Ⅱ不锈钢

中国腐蚀与防护学报

2000, Vol. 20

Issue (5): 263-268

研究报告

本期目录 | 过刊浏览

突扩管条件下材料的冲刷腐蚀机理研究Ⅱ不锈钢

阍永贵;郑玉贵;姚治铭

中科院金属腐蚀与防护研究所

EROSION-CORROSION MECHANISM UNDER SUDDEN PIPE EXPANSION Ⅱ.STAINLESS STEEL

Yonggui Yan;Yugui Zheng;Zhiming Yao;

中科院金属腐蚀与防护研究所

全文: PDF(189 KB)

摘要: 利用新近研制的双相流冲刷腐蚀激光多普勒实验装置,通过失重测试、表面形貌观察、局部流速流态测试和典型部位的电化学测试，研究了突扩管条件下不锈钢AISI316L在单相及含砂人工海水介质中的冲刷腐蚀机理。结果表明：冲刷腐蚀峰值发生在距突扩位置约3.0D的部位(D为粗管直径),与切向流速扰动度的峰值位置相同.在3.0D和5.5D的部位,冲刷作用是主要的,而在回流区(1.5D),则为氧扩散控制.不同部位的冲刷腐蚀形貌有明显差异,并与局部流速流态是相互对应的.冲刷电流随流速的提高而增大以及致钝峰的出现.

关键词 ：冲刷腐蚀, 不锈钢, 人工海水, 扰流, 激光多普勒

Abstract：The erosion-corrosion mechanism of AISI316L in artificial sea water with or without different silica sand under sudden pipe expansion condition was investigated through weight loss test, surface morphology observaton,local flow regume measurements (LDA)and electrochemical measurements at specific position.The results showed that the maximum of erosion-corrosion was located at about 3.0D (large pipe diameter) downstream the sudden pipe expansion whic was the same as the maximum of turbulent fluctuations of tangential velocity of 1.5mm away from the pipe wall.The erosion-corrosion of 3.0D and 5.5D downstream the sudden pipe expansion dominated, in contrast, that of 1.5D (recirculation zone )was oxygen diffusion controlled.The erosion-corrosion morphologies at different positions were significanly different. which was just responding the local flow regime .The effects of erosion on corrosion were not only due to the enhanced mass transfer of the oxygen, but also due to the weakness and/or breakdown of passive film.

Key words： erosion-corrosion stainless steel artificial sea water disturbed flow Laser-Doppler-Anemometry elect

收稿日期: 1999-08-30

ZTFLH:

TG172.85.TG172.2

Corresponding author: Yonggui Yan

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	阍永贵
	郑玉贵
	姚治铭
44.8K

引用本文:

阍永贵; 郑玉贵; 姚治铭 . 突扩管条件下材料的冲刷腐蚀机理研究Ⅱ不锈钢[J]. 中国腐蚀与防护学报, 2000, 20(5): 263-268 .
Yonggui Yan, Yugui Zheng, Zhiming Yao. EROSION-CORROSION MECHANISM UNDER SUDDEN PIPE EXPANSION Ⅱ.STAINLESS STEEL. J Chin Soc Corr Pro, 2000, 20(5): 263-268 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2000/V20/I5/263

[1]郑玉贵,阎永贵,龙康等.双相流冲刷腐蚀激光多普勒测试装置及其校正[J].中国腐蚀与防护学报,1999,19(5):301-305
[2]阎永贵,郑玉贵,姚治铭等.突扩管条件下材料的冲刷腐蚀机理研究-Ⅰ碳钢[J].中国腐蚀与防护学报,2000,20(5):257-266
[3] Blatt W, Kohley T, Lotz U, et al. The influence of hydrodynamics on erosion-corrosion in two-phase liquid-particle flow[J].Corrosion,1989,45(10):793
[4] Lotz U, Postlethwaite J. Erosion-corrosion in disturbed two phase liquid/particle flow[J]. Corrosion Science,1990,30(1):95-106
[5] Nesic S, Postlethwaite J. Relationship between the structure of disturbed flow and erosion-corrosion[J].Corrosion,1990,46(11):874-880
[6] Postlethwaite J,Nesic S. Erosion in disturbed liquid/particle pipe flow: effects of flow geometry and particle surface roughness[J].Corrosion,1993,49(10):850-857
[7] Turenne S, Fiset M,Masounave J.The effect of sand concentration on the erosion of materials by a slurry jet[J]. Wear, 1989,133:95-106

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[7]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	胡宗武, 刘建国, 邢蕊, 尹法波. 单相流条件下90°水平弯管冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 115-122.
[10]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[11]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[12]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[13]	付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[14]	王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[15]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.

Viewed

Full text

Abstract

Cited

Shared

Discussed