| Research Progress of Thiobacilli on Concrete corrosion |
| 中南大学 |
|
Cite this article:
. Research Progress of Thiobacilli on Concrete corrosion. J Chin Soc Corr Pro, 2007, 27(6): 373-378 .
|
|
|
Abstract Thiobacilli corrosion is often a problem in sewer environment. The research progresses of thiobacilli on concrete corrosion in recent years were reviewed. It’s concluded that the research done on thiobacilli corrosion of concrete can roughly be divided into two groups: bacteria simulation tests and exposure tests in situ .The corrosion mechanism of concrete induced by thiobacilli and the distinction between sulfuric acid corrosion and thiobacilli corrosion were explained. In addition, the parameters which were used to evaluate the concrete’s corrosion degree and the methods which were used to improve the concrete’s durability were also concluded. The conclusions as following are made at the end: Though some advances had been made so far, there are a lot of void in the study of concrete corrosion resulted from thiobacilli. Especially the grading of the corrosion, the models for predicting corrosion rate, the relationship between substratum and the bacteria responsible for the production of the sulfuric acid and whether can utilize the bacteria to improve the concrete’s durability or not should be intensified as soon as possible.
|
|
Received: 13 April 2006
|
|
|
[1]Chen L P.Ecnomic losses induced by microorganism corrosion andits countermeasures[J].Corros.Prot.,1996,(6):248-251(陈六平.微生物腐蚀所导致的经济损失与对策[J].腐蚀与防护,1996,(6):248-251)
[2]Olmstead W M,Hamlin H.Converting portions of the Los Angelesoutfall sewer into a septic tank[J].Eng.News,1900,44:317
[3]Parker C D.The corrosion of concreteⅠ.The isolation of a speciesof bacterium associated with the corrosion of concrete exposed toatmospheres containing hydrogen sulfide[J].Australian J.Experi-mental Biology and Medical Sci.,1945,23:81-90
[4]Parker C D.The corrosion of concreteⅡ.The function of thiobacil-lus concretivorus novel species in the corrosion of concrete ex-posed to atmospheres containing hydrogen sulfide[J].Australian J.Experimental Biology and Medical Sci.,1945,23:91-98
[5]Parker C D.Mechanics of corrosion of concrete sewers by hydrogensulfide[J].Sewage Ind Wastes,1951,23:1477-1485
[6]Redner J A,Esfandi E J,His R P.Evaluation of protective coat-ings for concrete exposed to sulfide generation in wastewater treat-ment facilities[J].J.Prot.Coat.Lin.,1991,(8):48-58
[7]Chandra S,Berntsson L.Deterioration of concrete in swimming poolsin the south of Sweden[J].ACI Mater.J.,1988,85:489
[8]Zherebyateva T V,Lebedeva E V,Karavaiko G I.Microbiologicalcorrosion of concrete structures of hydraulic facilities[J].Geomi-crobiology Journal,1991,(9):119-127
[9]Liu H F,Xu L M,Zheng J S.Steel corrosion under sulfate-reduc-ing bacteria biofilm[J].Oilfield Chemistry,2000,17(1):93-96(刘宏芳,许立铭,郑家.硫酸盐还原菌生物膜下钢铁腐蚀研究概况[J].油田化学,2000,17(1):93-96)
[10]Roberts D J,Nica D,Zuo G,et al.Quantifying microbially in-duced deterioration of concrete:initial studies[J].International Biodeterior.Biodegrad.,2002,49:227-234
[11]Ismail N,Nonaka T,Noda S,et al.Effect of carbonation on mi-crobial corrosion of concrete[J].J.Constr.Manage.Eng.,1993,20:133-138
[12]Han J Y,Dai C,Gao Z H,et al.Microorganism corrosion ofconcrete[J].Mater.Rep.,2002,16(10):42-44(韩静云,戴超,郜志海等.混凝土的微生物腐蚀[J].材料导报,2002,16(10):42-44)
[13]Barton L,Tomei F.Characteristics and activities of sulfate re-ducing bacteria[A].Sulfate-Reducing Bacteria Plenum Press[C].NewYork,1995
[14]Zhang X L,Chen Z X,Liu H H,et al.Effect of environmentfactors on the growth of sulfate reducing bactria[J].J.Chin.Soc.Corros.Prot.,2000,20(4):224-229(张小里,陈志昕,刘海洪等.环境因素对SRB生长的影响[J].中国腐蚀与防护学报,2000,20(4):224-229)
[15]Mori T,Nonaka T,Tazaki K,et al.Interactions of nutrients,mois-ture and p H on microbial corrosion of concrete sewer pipes[J].Water Res.,1992,26(1):29-37
[16]Webster M T,Loehr R C.Long-term leaching of metals from con-crete products[J].J.Environ.Eng.,1996,122:714-721
[17]Wang Y S,Hu W J.The H2S problem of sewer pipe and its controlmeasuerment[J].Shandong Eviron.,1996,(5-6):24-25(王以森,胡望均.污水管道硫化氢问题及其控制对策[J].山东环境,1996,(5-6):24-25)
[18]Gu J D,Ford T E.,Berke N S,et al.Biodeterioration of con-crete by the fungus fusarium[J].Inter.Biodeterior.Biodegrad.,1998,41:101-109
[19]Nica D,Davis J L,Kirby L,et al.Isolation and characterizationof microorganisms involved in the biodeterioration of concrete insewers[J].Inter.Biodeterior.Biodegrad.2000,46:61-68
[20]Suk K C,Mori T.A newly isolated fungus participates in the cor-rosion of concrete sewerpipes[J].Water Sci.Technic,1995,31(7):263-271
[21]Morton R L,Yanko W A,Grahom D W,et al.Relationship be-木焱tween metal concentrations and crown corrosion in Los Angeles County sewers[J].Res.J.Water Pollut.Control Fed.,1991,(63):789-798
[22]Lee W,Characklis W G.Corrosion of mild steel under anarobicbiofilm[J].Corrosion,1993,49(3):186-198
[23]Attiogbe E K,Rizkalla S H.Response of concrete to sulfuric acidattack[J].ACI Mater.J.,1988,84(6):481-488
[24]Wafa F F.Accelerated sulfate attack on concrete in a hot climate[J].Cem.Concr.Aggregates,1994,16(1):31-35
[25]Cohen M D,Mather B.Sulfate attack on concrete research needs[J].ACI Mater.J.,1991,88(1):62-69
[26]Torii K,Kawamura M.Effects of fly ash and silica fume on theresistance of mortar to sulfuric acid and sulfate attack[J].Cem.Concr.Res.,1994,24(2):361-370
[27]Davis J L,Nica D,Shields K,et al.Analysis of concrete from cor-roded sewer pipe[J].Inter.Biodeterior.Biodegrad.,1998,42:75-84
[28]He H Z,Lu S H.Study on the resistance of fly ash concrete tocorrosion by city sewage[J].J.Build.Mater.,1999,2(4):314-318(贺鸿珠,陆善后.掺粉煤灰混凝土耐城市污水侵蚀性能的研究[J].建筑材料学报,1999,2(4):314-318)
[29]Elke Vincke,Ellen Van Wanseele,Joke Monteny.Influence ofpolymer addition on thiobacilli attack of concrete[J].Inter.Biodeterior.Biodegrad.,2002,49:283-292
[30]Monteny J,Belie N D,Vincke E.Chemical and microbiologicaltests to simulate sulfuric acid corrosion of polymer-modified con-crete[J].Cem.Concr.Res.,2001,31:1359-1365
[31]Hormann K,Hofmann F,Schmidt M.Stability of concrete againstthiobacilli corrosion,a new method for determination[A].Proceed-ings of the 10th International Congress on the Chemistry of Cement[C].Gothenburg,1997
[32]Mechelen A C A,Polder R B.Rioleringen(XI),biogene zwavelzu-uraantasting,overflag van eon vervolgonderzoek in Rotterdam[J].Cem.,1991,(2):26-30
[33]Ramakrishnan V,Bang S S,Deo K S.A novel technique for re-pairing cracks in high performance concrete using bacteria[A].Proceeding of the International Conference on High Performance,High Strength Concrete[C].Perth,1998
[34]Ghosh P,Mandal S,Chattopadhyay B D,et al.Use of microor-ganism to improve the strength of cement mortar[J].Cem.Concr.Res.,2005,35:1980-1983 |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|
|