Abstract The development and the applying situation of weathering steel and progress in research on weathering steel were reviewed in the work. The effect of alloy element such as Cu, P, Cr, Ni on the corrosion resistance of weathering steel and its mechanisms were summarized as well. At the same time, it was analyzed that the process and the mechanisms of rut layer transformation and revolution. A better prospect of weathering steel development is described. It was concluded that the good performance of weathering steel resistance to corrosion came from the additions of alloy elements. The inner rust layer formed on the weathering steel is constituted mainly by compact α-FeOOH after lots of year exposure. The transformation of γ-FeOOH to α-FeOOH is a reason for the good property of weathering steel resistance to corrosion.
|
|
Received: 10 April 2006
|
|
|
[1]Cao C N.Environmental Corrosion of Materials in China[M].Bei-jing:Chemical Industry Press,2005(曹楚南.中国材料的自然环境腐蚀[M].北京:化学工业出版社,2005)
[2]Matsushima I.Translated by Jin Y K.Low-Alloy Corrosion Resis-tant Steels-A History of Development Application and Research[M].Beijing:Metallurgical Industry Press,2004(松岛岩著.靳裕康译.低合金耐蚀钢—开发、发展及研究[M].北京:冶金工业出版社,2004)
[3]Hou W T,Yu J D,Liang C F.Evaluation of atmospheric corrosiv-ity of 7 test sites in China and corrosion mechanism of steels[J].Corros.Sci.Prot.Technol.,1994,6(2):137-142(侯文泰,于敬敦,梁彩凤.钢的大气腐蚀性4年调查及其机理研究[J].腐蚀科学与防护技术,1994,6(2):137-142)
[4]Liang C F,Hou W T.Atmospheric corrosion of carbon steels and lowalloy steels[J].Corros.Sci.Prot.Technol.,1995,7(3):183-186(梁彩凤,侯文泰.碳钢及低合金钢8年大气暴露腐蚀研究[J].腐蚀科学与防护技术,1995,7(3):183-186)
[5]Liang C F,Hou W T.Atmospheric corrosivity for steels[J].J.Chin.Soc.Corros.Prot.,1998,18(1):1-6(梁彩凤,侯文泰.环境因素对钢的大气腐蚀的影响[J],中国腐蚀与防腐学报,1998,18(1):1-6)
[6]Liang C F,Yu C J,Hou W T.A study of atmospheric corrosionof stainless steels—a summary of 12-year exposure testing[J].J.Chin.Soc.Corros.Prot.,1999,19(4):228-232(梁彩凤,郁春娟,侯文泰.不锈钢的大气腐蚀研究—12年暴露试验总结[J].中国腐蚀与防腐学报,1999,19(4):228-232)
[7]Liang C F,Hou W T.Sixteen-year atmospheric corrosion expo-sure study of steels[J].J.Chin.Soc.Corros.Prot.,2005,5(1):183-186(梁彩凤,侯文泰.碳钢、低合金钢16年大气暴露腐蚀研究[J].中国腐蚀与防腐学报,2005,5(1):183-186)
[8]Hoerle S,Mazaudier F,Dillmann P,et al.Advances in under-standing atmospheric corrosion of ironⅡ.Mechanistic modeling ofwet-dry cycles[J].Corros.Sci.,2004,46:1431-1465
[9]Evans U R.Mechanism of rusting[J].Corros.Sci.,1969,9:813-821
[10]Evans U R,Taylor C A J.Mechanism of atmospheric rusting[J].Corros.Sci.,1972,12:227-246
[11]Kihira H,Senuma T,Tanaka M,et al.A corrosion predictionmethod for weathering steels[J].Corros.Sci.,2005,47:2377-2390
[12]Mendoza A R,Corvo F.Outdoor and indoor atmospheric corro-sion of carbon steel[J].Corros.Sci.,1999,41:75-86
[13]Vera R,Rosales B M,Tapia C.Effect of the exposure angle inthe corrosion rate of plain carbon steel in a marine atmosphere[J].Corros.Sci.,2003,45:321-337
[14]Sun-Tae K,Yasuaki M,Yoshio T.Assessment of the effect ofair pollution on material damages in Northeast Asia[J].Atmo-spheric Environ.,2004,38:37-48
[15]Yu J D,Wu Y L,Cui X L,et al.Mechanism of atmosphericcorrosion resistance of 08Cu PVRE steel[J].J.Chin.Soc.Corros.Prot.,1994,14(1):82-86(于敬敦,吴幼林,崔秀岭等.08Cu PVRE钢耐大气腐蚀的机理[J].中国腐蚀与防护学报,1994,14(1):82-86)
[16]Leygraf C,Graedel T.Translated by Han E H,et al.Atmo-spheric Corrosion[M].Beijing:Chemical Industry Press,2005(莱格拉夫C,格雷德尔T著.韩恩厚等译.大气腐蚀[M].北京:化学工业出版社,2005)
[17]Stratmann M,Bohnenkamp K,Ramchandran T.The influenceof copper upon the atmospheric corrosion of iron[J].Corros.Sci.,1987,27:905-926
[18]Dillmann P,Balasubramaniam R,Beranger G.Characterizationof protective rust on ancient Indian iron using microprobe analyses[J].Corros.Sci.,2002,44:2231-2242
[19]Kihira H,Ito S,Murata T.The behavior of phosphorous duringpassivation of weathering steel by protective patina formation[J].Corros.Sci.,1990,31:383-388
[20]Zhang Q C,Wang J J,Wu J S,et al.Effect of iron selectiveproperty on protective ability of rust layer formed on weatheringsteel exposed in the marine atmosphere[J].Acta Metall.Sin.,2001,2:193-196(张全成,王建军,吴建生等.锈层离子选择性对耐候钢抗海洋大气腐蚀性能的影响[J].金属学报,2001,2:193-196)
[21]Kamimura T,Nasu S,Segi T.Corrosion behavior of steel underwet and dry cycles containing Cr3+ion[J].Corros.Sci.,2003,45:1863-1879
[22]Kamimura T,Stratmann M.The influence of chromium on the at-mospheric corrosion of steel[J].Corros.Sci.,2001,43:429-447
[23]Toshiyasu N,Hideki K,Kazuhiko N,et al.Effect of Co and Nion the corrosion behavior of low alloy steels in wet/dry environ-ments[J].Corros.Sci.,2000,42:1611-1621
[24]Oh S J,Cook D C,Townsend H E.Atmospheric corrosion of dif-ferent steels in marine,rural and industrial environments[J].Cor-ros.Sci.,1999,41:1687-1702
[25]Mizoguchi T,Ishii Y,Okada T,et al.Magnetic property basedcharacterization of rust on weathering steels[J].Corros.Sci.,2005,47:2477-2491
[26]Lin Q,Chen B W,Guo F,et al.Mechanism of atmosphericcorrosion resistance of RE in weathering steel[J].Chin.Rare Earths,2003,24(5):26-28(林勤,陈帮文,郭锋等.稀土改善09Cu PTi RE耐候钢耐蚀性的作用机理[J].稀土,2003,24(5):26-28)
[27]Guo F,Lin Q,Sun X Y.Effect of rare earths on corrosion re-sisting property of carbon-manganese purity steel[J].J.Chin.Rare Earths Soc.,2004,22(3):365-368(郭峰,林勤,孙学义.稀土对碳锰纯净钢耐腐蚀性能的影响[J].中国稀土学报,2004,22(3):365-368)
[28]Yue L J,Wang L M,Piao X Y,et al.Electrochemical charac-teristics of rust layer on 10PCu RE weathering steel[J].Chin.Rare Earths,2005,26(5):56-60(岳丽杰,王龙妹,朴秀玉等.10PCu RE耐候钢耐蚀锈层的电化学特征[J].稀土,2005,26(5):56-60)
[29]Li C Y,Wang X D,Jiang S M,et al.Study of the effect of rareearths on corrosion resistance of mild steels[J].Chin.Rare Earths,2005,12(6):23-28(李春艳,王向东,江社明等.稀土对低碳钢耐大气腐蚀性能影响的研究[J].稀土,2005,12(6):23-28)
[30]Wang B,Liu Q Y,Wang X D,et al.Effect of RE(Rare Earth)on improving the corrosion resistance of steel[J].Iron and Steel,2005,40(supplement):207-211(汪兵,刘清友,王向东等.稀土对低碳钢抗腐蚀性能的影响[J].钢铁,2005,40(增刊):207-211)
[31]Toshiyasu N,Toshiaki K.Clarification of chemical state for al-loying elements in iron rust using binary-phase potential-p H dia-gram and physical analyses[J].Corros.Sci.,2003,45:1073-1084
[32]Itagaki M,Nozue R,Watanabe K,et al.Electrochemical impedanceof thin rust film of low-alloy steels[J].Corros.Sci.,2004,46:1301-1310
[33]Flavio D,Stefano R.Premature corrosion failure of structuralhighway components made from weathering steel[J].Eng.Failure Analysis.,2002,9:541-551
[34]Ishikawa T,Takeuchi K,Kandori K,et al.Transformation ofγ-Fe OOH toα-Fe OOH in acidic solutions containing metal ions[J].Colloids Surf.A:Physicochem.Eng.Aspects,2005,266:155-159
[35]Zhang Q C,Wu J S.Current status of R & D work on weatheringsteel[J].Mater.Rev.,2000,14(7):12-14(张全成,吴建生.耐候钢的研究与发展现状[J].材料导报,2000,14(7):12-14)
[36]Wang J J,Guo X D,Zheng W L,et al.Analysis of the corro-sion rust on weathering steel and carbon steel exposed in marineatmosphere for three years[J].Corros.Prot.,2002,23(7):288-291(王建军,郭小丹,郑文龙等.海洋大气暴露3年的碳钢与耐候钢表面锈层分析[J].腐蚀与防护,2002,23(7):288-291)
[37]Wang J H,Wei F I,Chang Y S,et al.The corrosion mecha-nisms of carbon steel and weathering steel in SO2 polluted atmo-spheres[J].Mater.Chem.Phy.,1997,47:1-8
[38]Yamashita M,Konishi H,Kozakura T,et al.In situ observationof initial rust formation process on carbon steel under Na2SO4 and Na Cl solution films with wet/dry cycles using synchrotron radiation X-ray[J].Corros.Sci.,2005,47:2492-2498
[39]Misawa T,Asami K,Hashimoto K,et al.The mechanism of at-mospheric rusting and the protective amorphous rust on low alloysteel[J].Corros.Sci.,1974,14:279-289
[40]Chen Y Y,Tzeng H J,Wei L I.Corrosion resistance and me-chanical properties of low-alloy steels under atmospheric condi-tions[J].Corros.Sci.,2005,47:1001-1021
[41]Dillmann P,Mazaudier F,Hoerle S.Advances in understandingatmospheric corrosion of iron.I.Rust characterisation of ancientferrous artefacts exposed to indoor atmospheric corrosion[J].Cor-ros.Sci.,2004,46:1401-1429
[42]Kamimura T,Hara S,Miyuki H,et al.Composition and protec-tive ability of rust layer formed on weathering steel exposed tovarious environments[J].Corros.Sci.,2006,48:2799-2812
[43]Yamashita M,Miyuki H,Matsuda Y,et al.The long termgrowth of the protective rust layer formed on weathering steel byatmospheric corrosion during a quarter of a century[J].Corros.Sci.,1994,36:283-299
[44]Kimura M,Kihira H,Ohta N,et al.Control of Fe(O,OH)6nano-network structures of rust for high atmospheric-corrosion re-sistance[J].Corros.Sci.,2005,47:2499-2509
[45]Mizoguchi T,Ishii Y,Okada T,et al.Magnetic peroperty basedcharacterization of rust on weathering steels[J].Corros.Sci.,2005,47:2477-2497
[46]Yamashita M,Shimizu T,Konishi H.Structure and protectiveperformance of atmospheric corrosion product of Fe-Cr alloy filmanalyzed by Mossbauer spectroscopy and with synchrotron radia-tion X-rays[J].Corros.Sci.,2003,45:381-394
[47]Kimura M,Kihira H.Nanoscopic Mechanism of Protective Rust Formation on Weathering Steel Surfaces[J].Nippon Steel Techni-cal Report,2005,91:86-90
[48]Toshiaki O,Tomohiro K.Enhancement of electric conductivityof the rust layer by adsorption of water[J].Corros.Sci.,2005,47:2571-2577
[49]Stratmann M,Bohnenkamp K,Engell H J.An electrochemicalstudy of phase-transitions in rust layers[J].Corros.Sci.,1983,23:969-985
[50]Antony H,Legrand L,Marechal L,et al.Study of lepidocrociteγ-Fe OOH electrochemical reduction in neutral and slightly alka-line solutions at 25℃[J].Electrochem.Acta,2005,51:745-753
[51]Stratmann M,Hoffmann K.In situ Mossbauer spectroscopic studyof reactions within rust layers[J].Corros.Sci.,1989,29:1329-1352
[52]Stratmann M,Streckel H.On the atmospheric corrosion of met-als which are covered with thin electrolyte layers-I.Verification ofthe experimental technique[J].Corros.Sci.,1990,30:681-696
[53]Stratmann M,Streckel H.On the atmospheric corrosion of met-als which are covered with thin electrolyte layers-Ⅲ.the measure-ment of polarisation curves on metal surfaces which are covered bythin electrolyte layers[J].Corros.Sci.,1990,30:715-734
[54]Nasrazadani S.The application of infrared spectroscopy to a studyof phosphoric and tannic acids interactions with magnetite(Fe3O4),goethite(α-Fe OOH)and lepidocrocite(γ-Fe OOH)[J].Corros.Sci.,1997,39:1845-1859
[55]Wang F P,Yan C W,Zhang X Y,et al.Quartz crystal mi-crobalance and its applications in atmospheric corrosion studies[J].Chem.,2001,6:382-387(王凤平,严川伟,张学元等.石英晶体微天平(QCM)及其在大气腐蚀中的应用[J].化学通报,2001,6:382-387)
[56]Lin C,Wang F P,Li X G.The progress of research methods onatmospheric corrosion[J].J.Chin.Soc.Corros.Prot.,2004,24(4):249-256(林翠,王凤平,李晓钢.大气腐蚀研究方法进展[J].中国腐蚀与防护学报,2004,24(4):249-256)
[57]Wang Y H,Zhang T,Wang J,et al.Applications of Kelvinprobe technique in the studies of atmospheric corrosion[J].J.Chin.Soc.Corros.Prot.,2004,24(1):59-64(王燕华,张涛,王佳等.Kelvin探头参比电极技术在大气腐蚀研究中的应用[J].中国腐蚀与防护学报,2004,24(1):59-64)
[58]She J,Song S Z.Measurement of carbon steel corrosion in arti-ficially polluted atmospheres by reluctance probe[J].Corros.Sci.Prot.Technol.,2006,18(1):9-11(佘坚,宋诗哲.磁阻探针研究碳钢在人造污染大气中的腐蚀行为[J].腐蚀科学与防护技术,2006,18(1):9-11) |
| No Suggested Reading articles found! |
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
| |
Shared |
|
|
|
|
| |
Discussed |
|
|
|