钨铜合金化学镀镍磷镀层在NaCl溶液中的腐蚀行为

郝龙;李锐;江莉;林安;甘复兴

武汉大学资源与环境工程学院环境工程系湖北武汉

Corrosion Behavior of Ni-P Deposit on W-Cu Alloy in NaCl Solution

武汉大学资源与环境工程学院环境工程系湖北武汉

全文: PDF(996 KB)

摘要: 采用化学沉积的方法在W-Cu粉末合金上成功地实现了化学镀Ni-P镀层，镀层表面光滑、致密，在结构上属于非晶态；经过25 d的3.5 mass% NaCl溶液浸泡研究表明：在浸泡的前16 d中，化学镀Ni-P镀层的腐蚀速率逐渐增大，在16 d之后腐蚀倾向有所降低；通过腐蚀失重实验得到Ni-P镀层的腐蚀失重小于W-Cu合金，说明化学镀Ni-P镀层可以对W-Cu合金起到保护作用。

关键词 ：钨铜合金, 化学镀, Ni-P镀层, 腐蚀

Abstract：The corrosion behavior of Ni-P deposit on W-Cu alloy in 3.5%(wt%) NaCl solution was tested by the polarization curves and electrochemical impedance spectroscopy (EIS). The results indicate that the passive region is not obvious after immersing in 3.5%(wt%) NaCl solution for 0.5 hour and with the increasing of the immersion time the passive membrane becomes integrated and the passive region is becoming obvious after immersing in 3.5%(wt%) NaCl solution for 2 days. After 6 days the point corrosion potential and passive region become smaller and its anti-corrosion ability is getting lower, but the passive parameter is better than that of W-Cu alloy. The polarization curves after immersing in 3.5%(wt%) NaCl solution for 13 days and 29 days were much the same as the one after 6 days and the corrosion behavior of Ni-P alloy in 3.5%(wt%) NaCl solution becomes stable.

Key words：

收稿日期: 2007-02-05

ZTFLH:

TG146

通讯作者: 郝龙 E-mail: chinahaolong@126.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	郝龙
	李锐
	江莉
	林安
	甘复兴
44.8K

引用本文:

郝龙; 李锐; 江莉; 林安; 甘复兴 . 钨铜合金化学镀镍磷镀层在NaCl溶液中的腐蚀行为[J]. 中国腐蚀与防护学报, 2008, 28(5): 307-310 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I5/307

[1]Fan J L,Liu J,Yan D J,et al.Study of process of fine-grainedW-Cu composite[J].Powder Metall.,2004,22(2):83-84(范景莲,刘军,严德剑等.细晶钨铜复合材料制备工艺的研究[J].粉末冶金技术,2004,22(2):83-84)
[2]Fan J L,Yan D J,Huang B Y,et al.Current study of R&D ofW-Cu composite materials in China and abroad[J].Powder Met-all.,2003,13(2):9-14(范景莲,严德剑,黄伯云等.国内外钨铜复合材料的研究现状[J].粉末冶金工业,2003,13(2):9-14)
[3]Cai Y X,Liu B W.Compact W-Cu composite materials and its method[J].Powder Metall.,1999,17(2):138-144(蔡一湘,流伯武.钨铜复合材料致密化问题和方法[J].粉末冶金技术,1999,17(2):138-144)
[4]Jiang X X,Shen W.The Fundamental and Practice of ElectrolessPlating[M].Beijing:Defence Industry Press,2000:124(姜晓霞,沈伟.化学镀理论及实践[M].北京:国防工业出版社,2000:124)
[5]Wang S L,Xu X B,Wu H H.Preparation and corrosion proper-ties of electroless Ni-Zn-P alloy deposits[J].J.Chin.Soc.Corros.Prot.,2004,24(5):297-300(王森林,徐旭波,吴辉煌.化学沉积Ni-Zn-P合金制备和腐蚀性能研究[J].中国腐蚀与防护学报,2004,24(5):297-300)
[6]Xia L T,Wei H,Zhu H X.Study of corrosion behavior on com-mon cast iron materials exposed to seawater[J].J.Chin.Soc.Cor-ros.Prot.,2003,23(2):99-102(夏兰廷,韦华,朱宏喜.常用铸铁材料海水腐蚀行为的研究[J].中国腐蚀与防护学报,2003,23(2):99-102)
[7]Gu C D,Lian J S,Li G Y,et al.Electroless Ni-P plating on theAZ91D magnesium alloy[J].J.Chin.Soc.Corros.Prot.,2005,25(5):271-274(谷长栋,连建设,李光玉等.AZ91D镁合金的化学镀镍[J].中国腐蚀与防护学报,2005,25(5):271-274)
[8]Qin X J,Shao G J.Study on the initial electro-deposition behav-ior of Ni-P alloy[J].J.Chin.Soc.Corros.Prot.,2004,24(1):6-9(秦秀娟,邵光杰.电沉积Ni-P合金初期沉积行为的研究[J].中国腐蚀与防护学报,2004,24(1):6-9)
[9]Feng L J,Ma X J,Lei A L.Corrosion resistance of electrolessplating Ni-P alloy coating in sulfur-bearing solution[J].J.Chin.Soc.Corros.Prot.,2006,26(3):157-159(冯拉俊,马小菊,雷阿利.含硫介质中化学镀Ni-P合金镀层耐蚀性研究[J].中国腐蚀与防护学报,2006,26(3):157-159)
[10]Li L B,An M Z,Wu G H.Corrosion resistance of electroless Nicoatings on SiCp/Al composite and mechanism[J].J.Chin.Soc.Corros.Prot.,2006,26(3):160-164(李丽波,安茂忠,武高辉.SiCp/Al复合材料化学镀镍层耐蚀性能及机理研究[J].中国腐蚀与防护学报,2006,26(3):160-164)
[11]Huo H W,Li Y,Wang F H.Electroless nickel plating on AZ91Dmagnesium alloy[J].J.Chin.Soc.Corros.Prot.,2002,22(1):14-17(霍宏伟,李瑛,王福会.AZ91D镁合金化学镀镍[J].中国腐蚀与防护学报,2002,22(1):14-17)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed