纳米晶镀锌层在3.5%NaCl溶液中的腐蚀电化学行为

中国腐蚀与防护学报

2008, Vol. 28

Issue (5): 303-306

论文

本期目录 | 过刊浏览

纳米晶镀锌层在3.5%NaCl溶液中的腐蚀电化学行为

姜莉莉;李谋成;张文麒;沈嘉年

上海大学材料研究所

Elctrochemical Corrosion Behavior of Nanocrystalline Zinc Coatings in 3.5%NaCl Solution

;;;

上海大学材料研究所

全文: PDF(1071 KB)

摘要: 以脉冲电沉积方法为基础，通过改变峰值电流以及添加剂等实验条件制备出不同晶粒尺寸的镀锌层。用电化学方法研究了镀层在3.5% NaCl溶液中的耐蚀性能。结果表明，纳米晶镀锌层的耐蚀性明显优于传统粗晶镀锌层，镀层的结构、晶粒取向等因素对镀锌层的耐蚀性影响较大。

关键词 ：脉冲电沉积, 纳米镀锌层, 极化曲线, 阻抗谱

Abstract：Pulse electrodeposition was used to produce the zinc coatings with different grain sizes by changing the peak current density and the additives. The corrosion behaviors of zinc coatings in 3.5% NaCl solution were investigated by potentiodynamic polarization and EIS techniques. The results demonstrated clearly the better corrosion resistance of nanocrystalline zinc coatings compared with conventional coarse-grain zinc coatings. The structure and the crystal orientation had also a significant influence on the corrosion resistance of zinc coatings.

Key words：

收稿日期: 2007-01-17

ZTFLH:

TG174

通讯作者: 姜莉莉 E-mail: koklily@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	姜莉莉
	李谋成
	张文麒
	沈嘉年
44.8K

引用本文:

姜莉莉; 李谋成; 张文麒; 沈嘉年 . 纳米晶镀锌层在3.5%NaCl溶液中的腐蚀电化学行为[J]. 中国腐蚀与防护学报, 2008, 28(5): 303-306 .
. Elctrochemical Corrosion Behavior of Nanocrystalline Zinc Coatings in 3.5%NaCl Solution. J Chin Soc Corr Pro, 2008, 28(5): 303-306 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2008/V28/I5/303

[1]Yan X C,Wen H,Yu N,et al.Corrosion and inhibition mecha-nism of zinc nanocrystalline electrodeposition in sulfuric acid solu-tions[J].J.Wuhan Univ.(Nat.Sci.),2005,41(6):683-686(颜肖慈,文汉,余娜等.纳米锌镀层在硫酸中的腐蚀和缓蚀机理[J].武汉大学学报(理学版),2005,41(6):683-686)
[2]Cao Y,Shen T H,Yao J Y,et al.Electrodeposition nanolaminat-ed growth of zinc[J].Electrochemistry,2004,10(1):107-111(曹莹,沈天慧,姚锦元等.电沉积纳米锌层的研究[J].电化学,2004,10(1):107-111)
[3]Liu X H,Yan X C,Li X F,et al.Corrosion behavior of nanocrys-talline zinc plate in NaCl solution[J].Mater.Prot.,2003,36(1):11-13(刘小虹,颜肖慈,李学丰等.纳米镀锌层在NaCl溶液中的腐蚀行为研究[J].材料保护,2003,36(1):11-13)
[4]Youssef Kh M S,Koch C C,Fedkiw P S.Improved corrosion be-havior of nanocrystalline zinc produced by pulse-current elec-trodeposition[J].Corros.Sci.,2004,46(1):51-64
[5]Mishra R,Balasubramaniam R.Effect of nanocrystalline grain sizeon the electrochemical and corrosion behavior of nickel[J].Cor-ros.Sci.,2004,46(12):3019-3029
[6]Shi J H,Wu B L,Liu G.Study on corrosion property of 316Lstainless steel with nanocrystalline surface[J].Mater.Eng.,2005(10):42-46(石继红,武保林,刘刚.316L不锈钢表面纳米化后腐蚀性能研究[J].材料工程,2005(10):42~46)
[7]КитайгородскийАИ,Translated by Gou R G.XRD for StructureAnalysis[M].Beijing:Science Press,1958(A.基达依哥罗茨基,龚荛圭译.X射线结构分析[M].北京:科学出版社,1958)
[8]Li M C,Zeng C L,Lin H C,et al.Corrosion behavior for 316Lstainless steel in dilute hydydrochloric acid solutions aerated withhydrogen gas[J].Acta Metall.Sin.,2002,38(12):1287-1291(李谋成,曾潮流,林海潮等.316不锈钢在通氢稀盐酸中的腐蚀行为[J].金属学报,2002,38(12):1287-1291)
[9]Park H,Szpunar J A.The role of texture and morphology in opti-mizing the corrosion resistance of zinc-based electrogalvanizedcoating[J].Corros.Sci.,1998,40(4/5):525-545
[10]Zidoune M,Grosjean M H,Roue L,et al.Comparative study onthe corrosion behavior of milled and unmilled magnesium by elec-trochemical impedance spectroscopy[J].Corros.Sci.,2004,46(12):3041-3055

[1]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[2]	李子运, 王贵, 罗思维, 邓培昌, 胡杰珍, 邓俊豪, 徐敬明. 热带海洋大气环境中EH36船板钢早期腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[5]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[6]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[7]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[8]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[9]	焦明远, 金伟良, 毛江鸿, 李腾, 夏晋. 电化学修复过程混凝土内环境对钢筋表面析氢影响的实验研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 463-470.
[10]	宋增意, 刘莉, 邓丽, 孙元, 周亦胄. N5镍基单晶高温合金在王水中的电化学溶解行为研究[J]. 中国腐蚀与防护学报, 2018, 38(4): 365-372.
[11]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[12]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[13]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[14]	梅朦, 郑红艾, 陈惠达, 张鸣, 张大全. 硫酸盐还原菌对Cu在循环冷却水中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2017, 37(6): 533-539.
[15]	孟凡帝, 刘莉, 李瑛, 王福会. 用于原位检测在深海并压力交变环境中有机涂层电化学阻抗的预埋微电极研究[J]. 中国腐蚀与防护学报, 2017, 37(6): 561-566.

Viewed

Full text

Abstract

Cited

Shared

Discussed