铀在三种溶液中的动电位极化和电化学阻抗谱研究

周萍;汪小琳;王庆富;杨江荣;王晓红

中国工程物理研究院

Potentiodynamic Polarization and EIS Behavior of Uranium in Three Different Solutions

中国工程物理研究院

全文: PDF(887 KB)

摘要: 用动电位极化和电化学阻抗谱（EIS）研究铀在0.5 mol/L H2SO4溶液、1 mol/L NaOH溶液和1 mol/L Na2SO4溶液中的腐蚀电化学行为。结果显示，铀在H2SO4溶液和Na2SO4溶液中的动电位极化曲线有类似的极化趋势，而在NaOH溶液中则有明显的钝化现象。EIS谱均有明显的容抗弧特征。利用软件对电化学阻抗谱进行拟合，得到了3种溶液中铀的电化学阻抗谱等效电路，拟合的阻抗谱与实验测得的阻抗谱拟合得比较好，拟合方差在10-3数量级。

关键词 ：铀, 腐蚀, 动电位极化, 电化学阻抗谱, 等效电路

Abstract：The corrosion electrochemical behavior of cast uranium has been studied in 0.5mol•L-1 H2SO4, 1mol•L-1 NaOH and 1mol•L-1 Na2SO4 solutions respectively using potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) techniques. The results obtained by potentiodynamic polarization curves indicated that there appear “fake-passivity” phenomena in H2SO4 and Na2SO4 solutions, while in NaOH solution it exhibited a additional “passivity” region besides the former phenomena. The EIS results all exhibit obvious capacitance-resistance arc characteristic. The software named ZsimpWin was used to fit the data form EIS to obtain corresponding equivalent circuit which consistent well with the measured data. The physical model of corrosion for uranium in three different solutions were proposed to interpret their equivalent circuits. The chi-square values between simulated data and measured data are within 10-3 order of magnitude.

Key words： uranium corrosion Potentiodynamic polarization EIS equivalent circuit

收稿日期: 2006-11-15

ZTFLH:

TG174.3

通讯作者: zhouping E-mail: pingbeijing_2008@126.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	周萍
	汪小琳
	王庆富
	杨江荣
	王晓红
44.8K

引用本文:

周萍; 汪小琳; 王庆富; 杨江荣; 王晓红 . 铀在三种溶液中的动电位极化和电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2008, 28(4): 215-218 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I4/215

[1]Yang J R.Anticorrosion study of uranium surface treated by CO[D].Sichuan:China Academy of Physic Engineering,2001(杨江荣.金属铀表面经CO处理后的抗腐蚀性研究[D].四川:中国工程物理研究院,2001)
[2]Cao C N.Principle of Corrosion Electrochemistry(second edition)[M].Beijing:Chemical Industry Press,2004(曹楚南.腐蚀电化学原理(第二版)[M].北京:化学工业出版社,2004)
[3]Cao C N,Zhang J Q.An Introduction to Electrochemical Impedance Spectroscopy[M].Beijing:Science Press,2002(曹楚南,张鉴清.电化学阻抗谱导论[M].北京:科学出版社,2002)
[4]Mansfeld F,Kending M W.ASTM STP[M].1985,866:122
[5]Wang Q F.Electrochemical corrosion behaviours of nickel depositpulse-plated on depleted uranium surface[J].J.Eng.Mater.,2005,4(2):5-9(王庆富.贫铀表面脉冲电镀镍的电化学腐蚀行为[J].工程材料,2005,4(2):5-9)
[6]Fu X G,Wang X L,Bai C M,et al.Electrochemical corrosion behavior of uranium-niobium alloy in aqueous solutions[J].Ordn.Mater.Sci.Eng.,2001,24(4):13-16(伏晓国,汪小琳,柏朝茂等.铀铌合金在水溶液中的电化学腐蚀行为[J].兵器材料科学与工程,2001,24(4):13-16)
[7]Li J F,Zhang Z,Cao F H,et al.Study on electrochemical impedancefeatures of Al-Li alloys in EXCO solution[J].Acta Metall.Sin.,2003,39(4):426-430(李劲风,张昭,曹发和等.Al-Li合金在EXCO溶液中腐蚀的电化学阻抗研究[J].金属学报,2003,39(4):426-430)
[8]Su J X,Zhang Z,Cao F H,et al.Exfoliation corrosion behaviorof T6 treated 2090 Al-Li alloy in EXCO solution and EIS duringexfoliation corrosion evolution[J].Acta Metall.Sin.,2005,41(9):974-978(苏景新,张昭,曹发和等.T6态2090Al-Li合金在EXCO溶液中剥蚀行为和剥蚀发展过程中的电化学阻抗谱[J].金属学报,2005,41(9):974-978)
[9]Shao H B,Zhang J Q,Wang J M,et al.EIS analysis on the an-odic dissolution process of pure aluminum in an alkaline solution[J].Acta Phys.Chim.Sin.,2003,19(4):372-375(邵海波,张鉴清,王建明等.纯铝在强碱溶液中阳极溶解的电化学阻抗谱解析[J].物理化学学报,2003,19(4):372-375)
[10]Reddy B P,Vandarkuzhali S,Subramanian T,et al.Electro-chemical studies on the redox mechanism of uranium chloride inmolten LiCl-KCl eutectic[J].Electrochim.Acta,2004,49:2471-2478
[11]Miserque F,Gouder T,Wegen D H,et al.Use of UO2 films forelectrochemical studies[J].J.Nucl.Mater.,2001,298:280-290
[12]Shoesmith DW.Fuel corrosion processes under waste disposal con-ditions[J].J.Nucl.Mater.,2000,282:1-31
[13]Zhang J Q,Cao C N.The application of Kramers-Kronig trans-forms in impedance data analysis[J].J.Chin.Soc.Corros.Prot.,1991,11(2):105-110(张鉴清,曹楚南.Kramers-Kronig转换在阻抗数据分析中的应用[J].中国腐蚀与防护学报,1991,11(2):105-110)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[12]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[13]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[14]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[15]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.

Viewed

Full text

Abstract

Cited

Shared

Discussed