外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响 |
朱丽霞1,2( ), 贾海东3, 罗金恒1, 李丽锋1, 金剑3, 武刚1, 胥聪敏4 |
1.中国石油集团石油管工程技术研究院 石油管材及装备材料服役行为与结构安全国家重点实验室 西安 710077 2.西安理工大学材料学院 西安 710048 3.中石油管道有限责任公司西部分公司 乌鲁木齐 830013 4.西安石油大学材料科学与工程学院 西安 710065 |
|
Effect of Applied Potential on Stress Corrosion Behavior of X80 Pipeline Steel and Its Weld Joint in a Simulated Liquor of Soil at Lunnan Area of Xinjiang |
ZHU Lixia1,2( ), JIA Haidong3, LUO Jinheng1, LI Lifeng1, JIN Jian3, WU Gang1, XU Congmin4 |
1. State Key Laboratory for Performance and Structure Safety of Petroleum Tubular Goods and Equipment Materials, CNPC Tubular Goods Research Institute, Xi'an 710077, China 2. School of Materials Science and Engineering, Xi'an University of Technology, Xi'an 710048, China 3. PetroChina West Pipeline Company, Urumchi 830013, China 4. School of Materials Science and Engineering, Xi'an Shiyou University, Xi'an 710065, China |
引用本文:
朱丽霞, 贾海东, 罗金恒, 李丽锋, 金剑, 武刚, 胥聪敏. 外加电位对X80管线钢在轮南土壤模拟溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 325-331.
Lixia ZHU,
Haidong JIA,
Jinheng LUO,
Lifeng LI,
Jian JIN,
Gang WU,
Congmin XU.
Effect of Applied Potential on Stress Corrosion Behavior of X80 Pipeline Steel and Its Weld Joint in a Simulated Liquor of Soil at Lunnan Area of Xinjiang. Journal of Chinese Society for Corrosion and protection, 2020, 40(4): 325-331.
链接本文:
https://www.jcscp.org/CN/10.11902/1005.4537.2019.118
或
https://www.jcscp.org/CN/Y2020/V40/I4/325
|
[1] |
Yan M C, Xu J, Yu L B, et al. EIS analysis on stress corrosion initiation of pipeline steel under disbonded coating in near-neutral pH simulated soil electrolyte [J]. Corros. Sci., 2016, 110: 23
doi: 10.1016/j.corsci.2016.04.006
|
[2] |
Liu Z Y, Li X G, Du C W, et al. Effect of inclusions on initiation of stress corrosion cracks in X70 pipeline steel in an acidic soil environment [J]. Corros. Sci., 2009, 51: 895
doi: 10.1016/j.corsci.2009.01.007
|
[3] |
Li H L, Ji L K, Tian W. Significant technical progress in the West-East gas pipeline projects-line one and line two [J]. Nat. Gas Ind., 2010, 30(4): 1
doi: 10.3787/j.issn.1000.0976.2010.04.001
|
[3] |
(李鹤林, 吉玲康, 田伟. 西气东输一、二线管道工程的几项重大技术进步 [J]. 天然气工业, 2010, 30(4): 1)
doi: 10.3787/j.issn.10000976.2010.04.001
|
[4] |
Mohd M H, Paik J K. Investigation of the corrosion progress characteristics of offshore subsea oil well tubes [J]. Corros. Sci., 2013, 67: 130
doi: 10.1016/j.corsci.2012.10.008
|
[5] |
Du Y F. Hua Jianmin: By the end of the 12th Five Year Plan, the total mileage of our long oil and gas pipeline exceeded 100000 km [DB/OL]. (2010-09-25).
|
[5] |
(杜燕飞. 华建敏: 十二五末我长输油气管道总里程超10万公里 [DB/OL]. (2010-09-25) . )
|
[6] |
Dang D N, Lanarde L, Jeannin M, et al. Influence of soil moisture on the residual corrosion rates of buried carbon steel structures under cathodic protection [J]. Electrochim. Acta, 2015, 176: 1410
doi: 10.1016/j.electacta.2015.07.097
|
[7] |
Caleyo F, Valor A, Alfonso L, et al. Bayesian analysis of external corrosion data of non-piggable underground pipelines [J]. Corros. Sci., 2015, 90: 33
doi: 10.1016/j.corsci.2014.09.012
|
[8] |
People'sNetwork. Intelligent construction of oil and gas pipeline to be speeded up [N]. China Energy News, 2019-03-29 (19)
|
[8] |
人民网. 油气管道智能化建设待提速 [N]. 中国能源报, 2019-03-29 (19))
|
[9] |
Wang X Q, Wang B Q, Wang B, et al. The current situation and development trend of China's Long distance natural gas pipeline [J]. Petrol. Plann. Eng., 2018, 29(5): 1
|
[9] |
(王小强, 王保群, 王博等. 我国长输天然气管道现状及发展趋势 [J]. 石油规划设计, 2018, 29(5): 1)
|
[10] |
China Economic Network. The scale of China's oil and gas pipeline network will reach 240000 km by the year of 2025 [DB/OL]. (2017-07-12).
|
[10] |
(中国经济网. 2025年我国油气管网规模将达到24万公里 [DB/OL]. (2017-07-12). )
|
[11] |
Bi Z Y, Liu H Z, Niu H. X80 pipe for the second west east gas pipeline and its welding process [J]. Weld. Join., 2011, (11): 47
|
[11] |
(毕宗岳, 刘海璋, 牛辉. 西气东输二线用X80管材及其焊接工艺 [J]. 焊接, 2011, (11): 47)
|
[12] |
Yan M C, Sun C, Xu J, et al. Role of Fe oxides in corrosion of pipeline steel in a red clay soil [J]. Corros. Sci., 2014, 80: 309
doi: 10.1016/j.corsci.2013.11.037
|
[13] |
Fang B Y, Atrens A, Wang J Q, et al. Review of stress corrosion cracking of pipeline steels in "low" and "high" pH solutions [J]. J. Mater. Sci., 2003, 38: 127
doi: 10.1023/A:1021126202539
|
[14] |
Chen X, Li X G, Du C W, et al. Effect of cathodic protection on corrosion of pipeline steel under disbonded coating [J]. Corros. Sci., 2009, 51: 2242
doi: 10.1016/j.corsci.2009.05.027
|
[15] |
Javidi M, Horeh S B. Investigating the mechanism of stress corrosion cracking in near-neutral and high pH environments for API 5L X52 steel [J]. Corros. Sci., 2014, 80: 213
doi: 10.1016/j.corsci.2013.11.031
|
[16] |
Yang D P, Xu C M, Luo J H, et al. Stress corrosion cracking behavior of X80 pipeline steel with design factor of 0.8 in near-neutral pH value solutions [J]. J. Mater. Eng., 2015, 43: 89
|
[16] |
(杨东平, 胥聪敏, 罗金恒等. 0.8设计系数用X80管线钢在近中性pH溶液中的应力腐蚀开裂行为 [J]. 材料工程, 2015, 43: 89)
|
[17] |
Cui Z Y, Liu Z Y, Wang L W, et al. Effect of plastic deformation on the electrochemical and stress corrosion cracking behavior of X70 steel in near-neutral pH environment [J]. Mater. Sci. Eng., 2016, A677: 259
|
[18] |
Xu C M, Luo J H, Zhou Y, et al. Effect of SRB on stress corrosion cracking of X100 pipeline steel in northwest saline soil [J]. Trans. Mater. Heat Treat., 2016, 37(5): 82
|
[18] |
(胥聪敏, 罗金恒, 周勇等. SRB对X100管线钢在西北盐渍土壤中应力腐蚀开裂行为的影响 [J]. 材料热处理学报, 2016, 37(5): 82)
|
[19] |
Luo J H, Xu C M, Yang D P. Stress corrosion cracking of X100 pipeline steel in acid soil medium with SRB [J]. J. Chin. Soc. Corros. Prot., 2016, 36: 321
|
[19] |
(罗金恒, 胥聪敏, 杨东平. SRB作用下X100管线钢在酸性土壤环境中的应力腐蚀开裂行为 [J]. 中国腐蚀与防护学报, 2016, 36: 321)
doi: 10.11902/1005.4537.2015.177
|
[20] |
Liu Z Y, Wang C P, Du C W, et al. Effect of applied potentials on stress corrosion cracking of X80 pipeline steel in simulated YingTan soil solution [J]. Acta Metall. Sin., 2011, 47: 1434
doi: 10.3724/SP.J.1037.2011.00046
|
[20] |
(刘智勇, 王长朋, 杜翠薇等. 外加电位对X80管线钢在鹰潭土壤模拟溶液中应力腐蚀行为的影响 [J]. 金属学报, 2011, 47: 1434)
doi: 10.3724/SP.J.1037.2011.00046
|
[21] |
Asher S L, Leis B N, Colwell J, et al. Investigating a mechanism for transgranular stress corrosion cracking on buried pipelines in near-neutral pH environments [J]. Corrosion, 2007, 63: 932
doi: 10.5006/1.3278311
|
[22] |
Yuan H Z, Liu Z Y, Li X G, et al. Influence of applied potential on the stress corrosion behavior of X90 pipeline steel and its weld joint in simulated solution of near neutral soil environment [J]. Acta Metall. Sin., 2017, 53: 797
doi: 10.11900/0412.1961.2016.00530
|
[22] |
(苑洪钟, 刘智勇, 李晓刚等. 外加电位对X90钢及其焊缝在近中性土壤模拟溶液中应力腐蚀行为的影响 [J]. 金属学报, 2017, 53: 797)
doi: 10.11900/0412.1961.2016.00530
|
[23] |
Chu W Y. Fracture and Environmental Fracture [M]. Beijing: Science Press, 2000: 109
|
[23] |
(褚武扬. 断裂与环境断裂 [M]. 北京: 科学出版社, 2000: 109)
|
[24] |
Egbewande A, Chen W X, Eadie R, et al. Transgranular crack growth in the pipeline steels exposed to near-neutral pH soil aqueous solutions: Discontinuous crack growth mechanism [J]. Corros. Sci., 2014, 83: 343
doi: 10.1016/j.corsci.2014.02.032
|
[25] |
Cheng Y F, Niu L. Mechanism for hydrogen evolution reaction on pipeline steel in near-neutral pH solution [J]. Electrochem. Commun., 2007, 9: 558
doi: 10.1016/j.elecom.2006.10.035
|
[26] |
Marshakov A I, Ignatenko V E, Bogdanov R I, et al. Effect of electrolyte composition on crack growth rate in pipeline steel [J]. Corros. Sci., 2014, 83: 209
doi: 10.1016/j.corsci.2014.02.012
|
[27] |
Barbalat M, Lanarde L, Caron D, et al. Electrochemical study of the corrosion rate of carbon steel in soil: Evolution with time and determination of residual corrosion rates under cathodic protection [J]. Corros. Sci., 2012, 55: 246
doi: 10.1016/j.corsci.2011.10.031
|
|
Viewed |
|
|
|
Full text
|
|
|
|
|
Abstract
|
|
|
|
|
Cited |
|
|
|
|
|
Shared |
|
|
|
|
|
Discussed |
|
|
|
|