动态再结晶特征及其对黄铜腐蚀敏感性的影响

赵月红,林乐耘,王振海

北京有色金属研究总院北京 100088

CHARACTERISTIC OF DYNAMIC RECRYSTALLIZATION AND ITS INFLUENCE ON CORROSION SENSITIVITY OF COPPER ALLOY

ZHAO Yuehong, LIN Leyun, WANG Zhenhai

Beijing General Research Institute for Nonferrous Metals, Beijing 100088

全文: PDF(2793 KB)

摘要: 研究了具有不同组织结构的铜合金管材在淡水中的腐蚀行为。合金存在大量粒径小于5µm的晶粒，且大小晶粒差别显著，表现为不完全再结晶的组织结构。大量细小晶粒的存在增加了铜合金在淡水中的腐蚀敏感性，主要表现为表面膜层不稳定、膜层鼓泡脱落、出现微裂纹和沿晶腐蚀。不完全再结晶的组织可以形成腐蚀通道，使合金的腐蚀迅速向纵深发展。这种组织来源于热加工中的动态再结晶过程，因某种原因保留到了冷加工及其热处理过程之后。

关键词 ：铜合金, 腐蚀, 动态再结晶, 淡水

Abstract：The corrosion behavior of copper alloy tube with different microstructures in fresh water was investigated in this paper. A lot of minute grains with less than 5 µm diameter were discovered in the alloy matrix, indicating imperfect recrystallization. The existence of many micro-grains made local corrosion of copper alloy much more sensitive when servicing in fresh water, during which the film was unstable and peeled and micro cracking and intergranular corrosion appeared. Furthermore, this kind of microstructure with imperfect recrystallization could form corrosion channel and make the corrosion developing along grain boundary quickly. The microstructure was from dynamic recrystallization in hot deformation and remained in the material structure after cold working and heat treatment.

Key words： copper alloy corrosion dynamic recrystallization fresh water

收稿日期: 2010-12-29

ZTFLH:

TG172.5

基金资助:

国家自然科学基金项目(50701008)资助

通讯作者: 赵月红 E-mail: zhaoyuehong5@126.com

Corresponding author: ZHAO Yuehong E-mail: zhaoyuehong5@126.com

作者简介: 赵月红，1973年，女，高级工程师，研究方向为有色金属腐蚀与防护

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	赵月红
44.8K

引用本文:

赵月红,林乐耘,王振海. 动态再结晶特征及其对黄铜腐蚀敏感性的影响[J]. 中国腐蚀与防护学报, 2012, 32(2): 102-108.
DIAO Ru-Hong. CHARACTERISTIC OF DYNAMIC RECRYSTALLIZATION AND ITS INFLUENCE ON CORROSION SENSITIVITY OF COPPER ALLOY. J Chin Soc Corr Pro, 2012, 32(2): 102-108.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2012/V32/I2/102

[1] Esteban P B. A continuum theory for dynamic recrystallization with microstructure-related length scales[J].Intern. J. Plast., 1998, 14(4): 319-353

[2] Gourdet S, Montheillet F. A model of continuous dynamic recrystallization[J]. Acta Mater., 2003, 51(9): 2685-2699

[3] Taku S. Dynamic recrystallization microstructures under hot working conditions[J]. J. Mater. Process. Technol., 1995，53(1-2): 349-361

[4] Zhang L W, Lu Y, Deng X H. Simulation of effect of nucleation mechanism on dynamic recrystallization process[J]. J.Dalian Univ. Technol., 2008, 48(3): 351-355

    (张立文, 卢瑜,邓小虎, 不同形核机制下对动态再结晶过程模拟研究[J]. 大连理工大学学报,2008, 48(3): 351-355)

[5] Manonukul A, Dunne P E. Initiation of dynamic recrystallization under inhomogeneous stress states in pure copper[J]. Acta Mater., 1999, 47(17): 4339-4354

[6] Gao W, Belyakov A, Miura H, et al. Dynamic recrystallization of copper polycrystals with different purities[J].Mater. Sci. Eng., 1999, A256: 233-239

[7] Wusatowska-Sarnek A M, Miura H. Nucleation and microtexture development under dynamic recrystallization of copper[J]. Mater. Sci. Eng., 2002, A323: 177-186

[8] Mao W M，Zhao X B. Recrystallization and Grain Growing of Metal Material [M]. Beijing: Metallurgical Industry Press, 1994:12-18

    (毛卫民, 赵新兵. 金属材料的再结晶和晶粒长大[M]. 北京:冶金工业出版社, 1994: 12-18)

[9] Shi F J, Wang J M, Xu X J. The investigation of equal channel angular pressing[J]. Hot Working Technol., 2003, (1): 51-53

    (石凤健, 汪建敏, 许晓静. 等截面角形挤压的研究内容及现状[J].热加工工艺, 2003, (1): 51-53)

[10] Wang J M, Xu X J, Shi F J. Investigation on ultra-fine grain copper by equal channel angular pressing[J]. Hot Working Technol., 2004, (7): 6-10

     (汪建敏, 许晓静, 石凤健.等径角挤压获得超细晶铜的研究[J]. 热加工工艺, 2004, (7): 6-10)

[11] Wang D S , Hou Y W. Investigation of grain refinement on brass processed by ECAP[J]. Forg. Stamp. Technol., 2006, (2): 39-42

     (王德胜,侯英玮. ECAP 法对H62黄铜的晶粒细化研究[J]. 锻压技术,2006, (2): 39-42)

[12] Shi F J, Wang J M, Xu X J. Study on recrystallization behavior of ultra-fine grain copper fabricated by equal channel angular pressing[J]. Hot Working Technol., 2005, 12: 24-26

     (石凤健, 汪建敏, 许晓静. ECAP法制备超细晶铜的再结晶行为研究[J].热加工工艺, 2005, 12: 24-26)

[13] Zhu Y Z Yang Y. Investigation of recrystallization behavior in rapid deformation[J]. Aluminium Working, 2000, 23(3):43-46

     (朱远志, 杨扬.高速变形条件下的动态再结晶机制的研究进展[J]. 铝加工, 2000,23(3):43-46)

[14] Yang Y, Cheng X L. Current status and trends in researches on adiabatic shearing[J]. Chin. J. Nonferrous Met., 2002,12(3): 401-408

      (杨扬, 程信林.绝热剪切的研究现状及发展趋势[J]. 中国有色金属学报, 2002, 12(3):401-408)

[15] Zhao D M, Dong Q M, Liu P, et al. Precipitation and recrystallization in Cu2Ni2Si alloy during aging treatment[J].Function Mater., 2002, 33(6): 618-621

     (赵冬梅, 董企铭,刘平等. Cu-Ni-Si合金在时效过程中析出与再结晶行为[J]. 功能材料, 2002,33(6): 618-621)

[16] Zhang D Q, He J W. On characterization of microstress measured by X-ray diffraction[J]. Acta Metall. Sin., 1998, 34(12):1273-1278

     (张定铨, 何家文.关于X射线衍射法测定微观应力的表征值的讨论[J]. 金属学报, 1998,34(12): 1273-1278

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed