镀锌层破损汽车钢板的腐蚀行为研究

中国腐蚀与防护学报

2009, Vol. 29

Issue (3): 172-176

研究报告

本期目录 | 过刊浏览

镀锌层破损汽车钢板的腐蚀行为研究

张红¹;杜翠薇¹;李晓刚^1;2;齐慧滨³

1.北京科技大学腐蚀与防护中心北京 100083
2.中国科学院金属研究所金属腐蚀与防护国家重点实验室沈阳 110016
3.宝钢研究院焊接与表面技术研究所上海 201900

CORROSION PROPERTIES OF AUTO GALVANIZED STEEL SHEET WITH VARIOUS BROKEN AREAS OF THE ZINC COATING

ZHANG Hong¹;DU Cuiwei¹;LI Xiaogang^1;2;QI Huibin³

1. Corrosion and Protection Center; University of Science and Technology Beijing; Beijing 100083
2. State Key Laboratory for Corrosion and Protection; Institute of Metal Research; Chinese Academy of Sciences;Shenyang 110016
3. Institute of Welding and Surface Technology; R & D of Baosteel; Shanghai 201900

全文: PDF(1461 KB)

摘要:

采用稀盐酸溶解汽车板部分镀锌层，研究了镀层破损率不同试样在5%NaCl溶液中的腐蚀行为，并对腐蚀产物形貌进行了观察。结果表明：在腐蚀初期，镀锌层试样的腐蚀速率高于基板，镀层的消耗对试样失重起主要贡献；试样的整体腐蚀速率随镀层破损率的增加而增大，且随腐蚀时间的延长而有所下降；采用电偶腐蚀电位、电化学阻抗谱(EIS)和动态极化等测量方法研究了镀层破损双相耦合电极的腐蚀电化学特性，所得结果基本一致。

关键词 ：汽车钢板, 镀锌层, 破损, 腐蚀

Abstract：

Research on the corrosion properties of the specimens of auto galvanized steel sheet with various broken areas of the zinc coating prepared by dissolution with a dilute hydrochloric acid solution were carried out in 5 %NaCl solution in the present paper. The results show that in the initial period of time the corrosion mass-losses of the specimens with coating were higher than that of the specimen without coating, the loss of coating made the major part of contribution to the corrosion weigh-loss of specimen. The corrosion rates increased with the broken area of the coating and decreased with exposing time. In addition, the electrochemical characteristics of the duplex phase galvanic electrodes were studied by galvanic corrosion potential measuring, electrochemical impedance spectrum (EIS) and potentiodynamic polarization and compared with the corrosion results.

Key words： auto steel sheet zinc coating breakage corrosion

ZTFLH:

TG172

基金资助:

国家自然科学基金项目(No.50571022)，国家科技基础条件平台建设资助项目（No.2005DKA10400）

通讯作者: 张红 E-mail: hongzhang0523@163.com

Corresponding author: hongzhang E-mail: hongzhang0523@163.com

作者简介: 张红，女，1966生，博士生，研究方向为腐蚀与防护

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张红
	张红
44.8K

引用本文:

张红杜翠薇李晓刚齐慧滨. 镀锌层破损汽车钢板的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2009, 29(3): 172-176.

链接本文:

https://www.jcscp.org/CN/Y2009/V29/I3/172

[1] El-Mahdy G A, Nishikata A , Tsuru T. AC impedance study on corrosion of 55% Al-Zn alloy coated steel under thin electrolyte layers[J]. Corros. Sci., 2000，42(1): 183-194
[2] Lee J M. Numerical analysis of galvanic corrosion of Zn/Feinterface beneath a thin electrolyte[J]. Electrochim. Acta,2006，51(16): 3256-3260
[3] Zhang X G. Galvanic protection distance of zinc coated steel under various environmental conditions[J].Corrosion, 2000, 56(2): 139-143
[4] Abreu C M, Cristoobal M J,Montemor M F. Galvanic coupling between carbon steel and austenitic stainless steel in alkaline media[J]. Electrochim. Acta, 2002,47(13-14): 2271-2279
[5] Varela F E, KurataY, Sanada N. The influence of temperature on the galvanic corrosion of a cast iron-stainless steel couple prediction by boundary element method[J]. Corros. Sci., 1997, 39(4): 775-788
[6] Tahara A, Kodama T. Potential distribution measurement in galvanic corrosion of Zn/Fe couple by means of Kelvin probe[J]. Corros. Sci., 2000, 42(4):655-673
[7] Huang G Q, Yu C J, Li L S. Study on galvanic corrosion of steel couples in seawater[J]. J. Chin.Soc.Corros.Prot., 2001,21(1): 46-52
    (黄桂桥, 郁春娟, 李兰生。海水中钢的电偶腐蚀研究[J]. 中国腐蚀与防护学报, 2001, 21(1): 46-52)
[8] Du M, Guo Q K, Zhou C J.Galvanic corrosion of carbon steel /titanium and carbon steel/ titanium / naval brass in seawater[J].J. Chin. Soc. Corros. Prot., 2006, 26(5): 263-266
    (杜敏, 郭庆锟, 周传静。碳钢/Ti和碳钢/Ti/海军黄铜在海水中电偶腐蚀的研究[J]. 中国腐蚀与防护学报, 2006, 26(5): 263-266)
[9] CaoC N. Principle of Corrosion Electrochemistry [M]. Beijing: Chemistry Industry Press, 2005
    (曹楚南. 腐蚀电化学原理[M]. 北京: 化学工业出版社, 2005)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed