RESEARCH OF SULFURIC ACID CORROSION AND CORROSION PRODUCT OF POLY (METHYL METHACRYLATE)/ MONTMORILLONITE NANOCOMPOSITES

全文: PDF(778 KB)

摘要: 用XRD和TEM对聚甲基丙烯酸甲酯/KH-V6型蒙脱土（PMMA/KH-V6型MMT）纳米复合材料进行结构表征，用失重法研究其耐H2SO4腐蚀行为，并用FTIR和XPS分析腐蚀产物膜。结果表明，蒙脱土质量分数为3%时，以单片层剥离形式存在于PMMA基体中，试样的腐蚀速率是纯PMMA的34.2%；PMMA与复合材料的腐蚀产物主要成分均为C、H、O和S元素；蒙脱土的阻隔效应，使PMMA/3%KH-V6型MMT纳米复合材料中PMMA基体的降解行为减弱，腐蚀产物中C元素含量下降，O和S元素含量上升。

关键词 ：硫酸, 腐蚀, 聚甲基丙烯酸甲酯, 蒙脱土, 纳米复

Abstract：The structure of poly (methyl methacrylate)/ montmorillonite (PMMA/MMT) nanocomposites was characterized by means of XRD and TEM. The sulfuric acid corrosion behavior of PMMA/MMT nanocomposites were studied using weight loss testing method, and the corrosion products were analyzed by FTIR and XPS. The solutions show that，exfoliated PMMA/MMT nanocomposites is made, and the corrosion rate of composites is 34.2 percent to PMMA when the mass fraction of MMT reaches 3 %. The corrosion products of both PMMA and its composites are C, H, O and S. Compared with the corrosion product of pure PMMA, C element content of the corrosion product of PMMA/ 3wt% MMT nanocomposites decreases while S and O elements increase introduced by the weaker of the degradation behavior of PMMA matrix for the barrier effect of MMT layer.

Key words： sulfuric acid corrosion poly (methyl methacrylate) montmorillonite nanocomposites

收稿日期: 2007-01-04

ZTFLH:

TB337

通讯作者: 陈奎 E-mail: chenkui405@126.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	陈奎
	杨瑞成
	张天云
44.8K

引用本文:

陈奎; 杨瑞成; 张天云 . PMMA/MMT纳米复合材料硫酸腐蚀研究[J]. 中国腐蚀与防护学报, 2008, 28(5): 296-298 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I5/296

[1]Essawy H,Badram A,Youssef A,et al.Synthesis of poly(methyl-methacrylate)/montmorillonite nanocomposites via in situ intercala-tive suspension and emulsion polymerization[J].Polym.Bull.,2004,53(1):9-17
[2]Zou G,Fang K,He P S.Study on bulk intercalation polymeriza-tion of PMMA/montmorillonite intercalated nanocomposite by dy-namic torsional vibration method[J].J.Mater.Sci.Lett.,2002,21(10):761-763
[3]Panchatapa J,Charles A W.Effects of surfactants on the thermaland fire properties of poly(methyl methacrylate)/clay nanocompos-ites[J].Polym.Degradation Stab.,2005,88:401-406
[4]Zhang W A,Shen X F,Li Y,et al.Synthesis and characteriza-tion of poly(methyl methacrylate)/OMMT nanocomposites byγ-ray irradiation polymerization[J].Radiat.Phys.Chem.,2003,67(5):651-656
[5]Xu Y J,William J Brittain,Xue C C,et al.Effect of clay type onmorphology and thermal stability of PMMA-clay nanocompositesprepared by heterocoagulation method[J].Polymer,2004,45(11):3735-3746
[6]Chen K,Yang R C,Wu M L,et al.Percolation analysis of poly-mer-montmorillonite exfoliated nanocomposites[J].J.LanzhouUniv.Technol.,2006,32(1):41-45(陈奎,杨瑞成,吴明亮等.聚合物/蒙脱土剥离型纳米复合材料逾渗理论分析[J].兰州理工大学学报,2006,32(1):41-45)
[7]Chen K,Yang R C,Cheng S W.The kinetic analysis of thermaldecomposition of PMMA/MMT nanocomposites[J].Key Eng.Mater.,2007,353-358:1366-1369
[8]Chen K,Yang R C,Zhang T Y.Preparation and friction and wearbehavior of PMMA/OMMT composites[J].Tribology,2007,27(2):187-191(陈奎,杨瑞成,张天云.PMMA/纳米OMMT复合材料的制备及其摩擦磨损性能研究[J].摩擦学学报,2007,27(2):187-191)
[9]Wagner C D,Davis L E,Zeller M V,et al.Empirical atomic sen-sitivity factors for quantitative analysis by electrospectroscopy forchemical analysis[J].Surf.Int.Anal.,1981,3(5):211-225

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[4]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[5]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[6]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[7]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[8]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[10]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed