热处理对铅锡青铜耐腐蚀性能的影响

凡小盼;王昌燧;金普军

中国科学技术大学

The Heat Treatment and the Corrosive Prevention of Bronz

;;

中国科学技术大学

全文: PDF(946 KB)

摘要: 利用传统浇铸技术铸造含15％ Sn的Cu-Sn-Pb青铜合金。经不同温度热处理及未经热处理的样品在酸性含Cl- 环境中进行腐蚀试验，用金相和XRD分析两者的耐腐蚀性能。结果表明：经过热处理后，其内部的晶间组织结构发生改变，δ相分解或减少，α相再结晶。选择合适的热处理温度可以增强青铜的耐腐蚀能力，达到控制" 粉状锈"的效果。

关键词 ：青铜合金, 腐蚀, 金相, 晶间结构, 热处理

Abstract：This paper presents an analytical study on two ternary Cu-Sn-Pb systems forged by using the Chinese traditional casting technique with difference in the amount of tin 15%. We had some of these copper alloys heat?鄄ed under different temperatures, then kept all the heated and unheated samples under an acid and chlorine-rich environment for several days.With the combined use of XRD analysis and metallographic examination, corrosion resistance of copper alloys was carefully discussed. The delta phase decomposed or diminished while the alpha phase recrystallized. When a proper temperature was chosen for reheating, the delta phase was found eliminated and the intergranular structure changed again. This experiment indicates that by doing so the corrosion resistance of copper alloys can be greatly improved, which in return helps controlling the outbreak of bronze disease.

Key words： bronze alloy corrosion microstructure intergranular structure heat treatment

收稿日期: 2006-07-26

通讯作者: 凡小盼 E-mail: fanxp@mail.ustc.edu.cn；fxp_1983@126.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	凡小盼
	王昌燧
	金普军
44.8K

引用本文:

凡小盼; 王昌燧; 金普军 . 热处理对铅锡青铜耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2008, 28(2): 112-115 .

链接本文:

https://www.jcscp.org/CN/Y2008/V28/I2/112

[1]Liu Y,Yuan S X,Zhang X M.Research on the corrosion of bronze wares excavated from Tianma Qucun site of Jin state in Zhou Dy-nasty[J].Sciences of Conservation and Archaeology,2002,12(2):9-18(刘煜,原思训,张晓梅.天马一曲村周代晋国墓地出土青铜器锈蚀研究[J].文物保护与考古科学,2002,12(2):9-18)
[2]Luoyang Copper Processing Factory.Metallographic Graphs of Copper and Copper Alloys[M].Luoyang:Metallurgical Industry Publishing Company,1983(洛阳铜加工厂中心试验室金相组.铜及铜合金金相谱图[M].洛阳:冶金工业出版社,1983)
[3]Wang C S,Yuan M,Xiong Y H.Bronze composition and the for-mation of powdery corrosion[J].J.China Univ.Sci.Technol.,1995,25(4):448-453(王昌燧,袁玫,熊永红.青铜合金成分与粉状锈的生成[J].中国科学技术大学学报,1995,25(4):448-453)
[4]Zhang C Q,Wu Y S,Fang M X,et al.The anodic behavior of alloy and ingredient of bronze alloy[J].J.Mater.Eng.,1999,11:23-26(张长桥,吴佑实,方梅仙等.青铜合金成分与合金的阳极行为[J].材料工程,1999,11:23-26)
[5]Zhang X M,Yuan S X.Research on the corrosion of bronzes from Zhouyuan site and Yu state cemeteries[J].Sciences of Conserva-tion and Archaeology,1999,11(2):7-18(张晓梅,原思训.周原遗址及渔国墓地出土青铜器锈蚀研究[J].文物保护与考古科学,1999,11(2):7-18)
[6]Wu Y S,Fan C Z,Minoru Suzuki.A calculation of quantum-me-chanics for the preferential corrosion on the crystal edge of bronzealloy[J].Sciences of Conservation and Archaeology,1994,6(1):1-8(吴佑实,范崇政,铃木稔.青铜合金表面晶体棱角处优先生锈的量子力学证明[J].文物保护与考古科学,1994,6(1):1-8)
[7]Fan C Z,Wu Y S,Wang C S.The electro-chemical corroding of powder-corrosion and analysis of valent-electron structure[J].Chin.J.Chem.Phys.,1992,5(6):479-484(范崇政,吴佑实,王昌燧等.粉状锈生成的电化学腐蚀及价电子结构分析[J].化学物理学报,1992,5(6):479-484)
[8]Zhang L J,Sun S Y,Yin W Z,et al.Study of element and mi-crostructure of bronze excavated from Yans′tombs at Liulihe,Bei-jing[J].Cultural Relics,2005,6:82-91(张利洁,孙淑云,殷玮璋等.北京琉璃河燕国墓地出土铜器的成分和金相研究[J].文物,2005,6:82-91)
[9]Tian C H.The Technical History of Ancient Chinese Metals[M].Sichuan:Sichuan Science and Technology Publishing Company,1988(田长浒.中国金属技术史[M].四川:四川科技出版社,1988)
[10]He T K.On simulated tests for the heat treatment of ancient bronzemirrors[J].Studies in the History of Sciences,1994,13(1):76-78(何堂坤.古青铜热处理模拟试验[J].自然科学史研究,1994,13(1):76-78)
[11]Fan C Z,Wang C S,Wang S J,et al.Study of formation mecha-nism of bronze powder corrosion[J].China Science(Series B),1991,3:239-245(范崇政,王昌燧,王胜君等.青铜器粉状锈生成机理研究[J].中国科学(B辑),1991,3:239-245)
[12]Fan C Z,Hu K L,Xing J Y,et al.A follow-observation on the de-veloping process of the powder corrosion[J].Sciences of Conser-vation and Archaeology,1997,9(1):19-24(范崇正,胡克良,邢锦云等.青铜粉状锈生长过程的跟踪观测[J].文物保护与考古科学,1997,9(1):19-24)
[13]Fan C Z,Wu Y S,Wang C S,et al.The dynamics of developing process of the powder corrosion[J].China Science(Series B),1992,5:479-484(范崇政,吴佑实,王昌燧等.青铜器粉状锈生长过程的动力学研究[J].中国科学(B辑),1992,5:479-484)

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[4]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[5]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[6]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[7]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[8]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[10]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed