不锈钢载波钝化膜的光电化学研究

颜立成;张俊喜;魏增福;张鉴清

杭州师范学院

PHOTOELECTROCHEMICAL INVESTIGATION OF A.V.PASSIVE FILM ON 304 STAINLESS STEEL

Licheng Yan;Junxi Zhang;Zengfu Wei;Jianqing Zhang

杭州师范学院

全文: PDF(136 KB)

摘要: 采用光电化学方法研究了304不锈钢载波钝化膜在硼酸/硼砂溶液中的光电化学性质.通过测量钝化膜的光电流与入射光光子能量的关系和光电流与测量电位的关系，结合半导体理论，对载波钝化膜的半导体特性和结构进行了分析.结果表明，载波钝化膜是一高度无序的非晶态半导体膜且具有p型半导体特性.膜层的光电流对测量电位的响应在一定范围内符合Poole-Frenkel效应，但在其它范围内则具有一定的复杂性.

关键词 ：载波钝化, 光电化学, 半导体性质, 钝化膜, 不锈

Abstract：A Photoelectrochemical investigation has been carried out on 304 stainless steel alternating voltage (A.V.) passive films in 005mol/L H3BO3+005mol/L Na2B4O7·10H2O solution.The dependences of photocurrent on the measuring potential (E) and the wavelength of incident light have been studied.Results show that the A.V.passive film is a highly disordered amorphous state.The photoelectrochemical behavior of passive film indicates that the passive film is p-type semiconductor.The relationship betweeniph and E is conformity with Poole-Frenkel effect in short potential range,while,it is complicated in the rest potential range owing to the changing of its composition with potential.

Key words： Photoelectrochemical A.V. Passivation Semiconducting Properties Passive Film Stainless Steel

收稿日期: 2004-10-14

ZTFLH:

TG178

通讯作者: 颜立成 E-mail: yanlicheng@163.com

Corresponding author: Licheng Yan E-mail: yanlicheng@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	颜立成
	张俊喜
	魏增福
	张鉴清
44.8K

引用本文:

颜立成; 张俊喜; 魏增福; 张鉴清 . 不锈钢载波钝化膜的光电化学研究[J]. 中国腐蚀与防护学报, 2005, 25(4): 209-212 .
Licheng Yan, Junxi Zhang, Zengfu Wei, Jianqing Zhang. PHOTOELECTROCHEMICAL INVESTIGATION OF A.V.PASSIVE FILM ON 304 STAINLESS STEEL. J Chin Soc Corr Pro, 2005, 25(4): 209-212 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I4/209

[1]SatoN.Anod CahanBD,ChenCT.Thenatureofthepassivefilmoniron.-Ⅲ.thesemiconductormodelandfurthersupportingevidence[J].J.Electrochem.Soc.,1982,129(5):921
[3]HakikiNE,BoudinS,RinditB,etal.Theelectronicstructureof passivefilmsformedonstainlesssteels[J].Corros.Sci.,1995,37(11):3821
[4]DuTB,CaoCN,YuJK,etal.Aphotoelectrochemicalinvestiga tionofA.C.modulatedpassivefilmon304stainlesssteelinweak-alkalineandneutralsolution[J].Electrochemistry,1995,1(14):402(杜天保,曹楚南,余家康等.在弱碱性及中性介质中AISI304不锈钢载波钝化膜光电化学研究[J].电化学,1995,1(14):402)
[5]StimmingU.Photoelectrochemicalstudiesofpassivefilms[J].Elec trochim.Acta,1986,31:415
[6]PaolaAD,QuartoFD,SunseriC.Aphotoelectrochemicalcharac terizationofpassivefilmsonstainlesssteels[J].Corros.Sci.,1986,26(11):935
[7]YangMZ,WeiP.AphotoelectrochemicalinvestigationofZirconi umoxidefilm[J].Electrochemistry,1995,1:30(杨迈之,韦平.锆表面氧化膜的光电化学研究[J].电化学,1995,1:30)
[8]SchmukiP,B hniH.Metastablepittingandsemiconductiveproper tiesofpassivefilms[J].J.Electrochem.Soc.,1992,139(7):1908
[9]ZhangGD.Photoelectrochemicalinvestigationofpassivefilmon iron[J].ActaPhysico-ChimicaSinica,1991,7(3):366(张国栋.铁钝化膜半导体特性的光电化学研究[J].物理化学学报,1991,7(3):366)
[10]ZengYM,QiaoLJ,GuoXZ,LiJX.EffectofHydrogenonthe electronicpropertiesofpassivefilm310stainlesssteel[J].Acta Metall.Sin.,2001,37(1):67(曾一民,乔利杰,郭献忠,李金许.氢对310不锈钢钝化膜半导体性质的影响[J],金属学报,2001,37(1):67)
[11]ZhangJX,WeiZF,QiaoYN,ZhouGD.Anewprocessforstain lesssteel[J].Corros.Prot.,2004,25:13(张俊喜,魏增福,乔亦男,周国定.不锈钢着色的“绿色”工艺研究[J].腐蚀与防护,2004,25:13)
[12]LiYC,YanCW,DuanHP.Investigationontherepairingeffect ofalternatingvoltageelectricfieldonthepittedNiCralloyelec trode[J].J.Chin.Soc.Corros.Prot.,2003,23(2):92(李运超,严川伟,段红平.交变电场对镍铬合金点蚀破坏的再钝化修复研究[J],中国腐蚀与防护学报,2003,23(2):92)
[13]ZhangJX,QiaoYN,CaoCN,ZhangJQ,etal.Semiconducting propertiesofpassivefilmformedonstainlesssteelbyusingA.V.passivation[J].ActaChimiaSinica,2002,60:30(张俊喜,乔亦男,曹楚南,张鉴清等.不锈钢载波钝化膜的半导体性质[J],化学学报,2002,60:30)
[14]ZhangJX,ChenJ,ChengSS,QiaoYA,CaoCN.Growthmech anismofcolorpassivefilmformedonSS304byusingA.V.passi vation[J].J.Chin.Soc.Corros.Prot.,1999,19(3):167(张俊喜,陈健,程胜松,乔亦男,曹楚南.不锈钢载波钝化着色膜的形成机理研究[J].中国腐蚀与防护学报,1999,19(3):167)
[15]WilhelmSM,TanizawaY,HackermanN.Photoelectrochemical characterizationofpassivefilmoniron[J].Corros.Sci.,1982,22:791
[16]PaolaAD.Semiconductingpropertiesofpassivefilmsonstainless steel[J].Electrochim.Acta.,1989,34(2):203)

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[5]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[6]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[7]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[8]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[9]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[10]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[11]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[12]	张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[13]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[14]	付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[15]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.

Viewed

Full text

Abstract

Cited

Shared

Discussed