新型巯基三唑化合物对HCl介质中碳钢的缓蚀作用研究
王慧龙
大连理工大学化学系288信箱
Corrosion Inhibition Effect of Triazole Derivatives to Carbon Steel in Hydrochloric Acid Solution
Huilong Wang
大连理工大学化学系288信箱
全文: PDF(173 KB)  
摘要: 合成了两种新型巯基三唑化合物,分别采用腐蚀失重法、动电位扫描极化曲线和交流阻抗法研究了其在1.0mol/L HCl介质中对Q235钢的缓蚀作用,分析了缓蚀作用机理。结果表明,对碳钢在1.0mol/L HCl溶液中,合成的巯基三唑化合物是性能优异的缓蚀剂。
关键词 三唑化合物碳钢腐蚀缓蚀剂    
Abstract:Two kinds of new triazole compounds were synthesized. Their inhibiting behavior on carbon steel in 1.0mol/L hydrochloric acid solutio was investigated by means of weight loss, potentiodynamic polarization and AC impedance methods. The results show that the triazole derivatives suppress both the anosic and cathodic process and the inhibition effect is caused by geometrical blocking of the metal surface by adsorbed inhibiting species. The investigated triazole compounds inhibit corrosion by adsorption mechanis and the adsorption leads to the formation of a protective chemisorbed film on the metal surface which suppresses the corresponding corrosion reaction. The synthesized triazole compounds are found to be excellent corrosion inhibitor for carbon steel in hydrochloric acid.
Key wordstriazole compound    carbon steel    corrosion    inhibitor
收稿日期: 2003-04-28     
ZTFLH:  TG174.42  
通讯作者: 王慧龙     E-mail: hlwang@dlut.edu.cn
Corresponding author: Huilong Wang     E-mail: hlwang@dlut.edu.cn

引用本文:

王慧龙 . 新型巯基三唑化合物对HCl介质中碳钢的缓蚀作用研究[J]. 中国腐蚀与防护学报, 2004, 24(5): 306-310 .
Huilong Wang. Corrosion Inhibition Effect of Triazole Derivatives to Carbon Steel in Hydrochloric Acid Solution. J Chin Soc Corr Pro, 2004, 24(5): 306-310 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2004/V24/I5/306

[1]BentissF ,TraisnelM ,GengembreL ,etal.Inhibitionofacidiccorro sionofmildsteelby3,5-diphenyl-4H -1,2,4-triazole[J].Ap pl.Surf.Sci.,2000,161:194-202
[2]ElHajjajiS ,LgarnriA ,AzianeD ,etal.Synthesisandevaluationoftheinhibitioneffectofanewclassoftriazolecompounds[J].ProgressinOrganicCoatings,2000,38(3/4):207-212
[3]MernariB ,El-AttariH ,TraisnelM ,etal.Inhibitingeffectsof3,5-bis(n-pyridyl)-4-amino-1,2,4-triazoleonthecorrosionformildsteelin1MHClmedia[J].Corros.Sci.,1998,40(2/3):391-399
[4]QuraishiMA ,MuralidharanS ,IyerSVK .Influenceof4-amino-5-mercapto-3n-propyl-1,2,4-triazoleonthecorrosionandpermeationthroughmildsteelinacidicsolutions[J].Anti-Cor rosionMethodsandMaterials,2000,47(6):354-358
[5]VaralakshmiC ,RaoBVAppa.Inhibitionofcorrosionofcopperby5-mercapto-3-p-nitrophenyl-1,2,4-triazoleinaqueousen vironment[J].Anti-CorrosionMethodsandMaterials,2001,48(3):171-180
[6]QuraishiMA ,AhmadS ,AnsariMQ .Inhibitionofsteelcorrosionbysomenewtriazolederivativesinboilinghydrochloricacid[J].Br.Corros.J.,1997,32(4):297-300
[7]QuraishiMA ,JamalDanish.CorrosioninhibitionofN -80steelandmildsteelin15%boilinghydrochloricacidbyatriazolecom pound-SAHMT [J].MaterialsChemistryandPhysics,2001,68:283-287
[8]BentissF ,LagreneeM ,TraisnelM .Thecorrosioninhibitionofmildsteelinacidicmediabyanewtriazolederivative[J].Corros.Sci.,1999,41(4):789-803
[9]DubeySN ,KaushikB .Triazolesascomplexingagent:synthesis&characterisationofcobalt(Ⅱ),nickel(Ⅱ),copper(Ⅰ),copper(Ⅱ),zinc(Ⅱ)&cadmium(Ⅱ)complexeswith4-amino-5-mercapto-3-n-propyl-5-triazole&5-mercapto-3-n-propyl-4-salicylidineamino-s-triazole[J].Ind.J .Chem.,1985,24A(11):950-953
[10]CaoChu’nan.Ontheelectrochemicaltechniquesforinvestigationofinhibitors[J].Corros.Sci.Prot.Technol.,1990,2(1):1-8(曹楚南.关于缓蚀剂研究的电化学方法[J].腐蚀科学与防护技术,1990,2(1):1-8)
[11]CaoChu’nan.Studyontheelectrodeprocessesatmixedpotentials[J].Corros.Sci.Prot.Technol.,1998,10(1):1-5(曹楚南.混合电位下的电极过程研究[J].腐蚀科学与防护技术,1998,10(1):1-5)
[12]BastidasJM ,DeDamboreneaJ ,V偄zquezAJ.Butylsubstituentsinn-butylamineandtheirinfluenceonmildsteelcorrosioninhibitioninhy drochloricacid[J].J.Appl.Electrochem.,1997,27(3):345-349
[1] 董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2] 唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3] 韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4] 张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6] 白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[7] 左勇, 曹明鹏, 申淼, 杨新梅. MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[8] 王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[9] 王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[10] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[11] 郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[12] 于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[13] 贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[14] 赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[15] 马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.