燃煤流化床中氯对碳钢腐蚀的影响机制

彭晓

中科院金属所

Effect of Chlorine on the Degradation of a Carbon Steel in a Coal-Fired Fluidized-Bed Combustor

Xiao Peng

中科院金属所

全文: PDF(292 KB)

摘要: 在小规模流化床（FBC）中燃烧一种低S高Cl煤1000h后，对放置于接近沸腾床位置的A210-C碳钢管腐蚀情况进行分析，发瑞碳钢管表面温度为470℃-560℃的区域腐蚀产物（主要为Fe2O3）严重剥落，剥落的腐蚀产物表面覆盖一层沉积盐，部分区域发现有（K，Na）Cl，对残留在钢管表面的腐蚀层进行分析，发现在腐蚀层—碳钢界面或其附近的基体中出现局部氯化，导致形成FeCl2层；局部快速腐蚀，形成向基体一侧的腐蚀突体；形成内部空洞这三种腐蚀形态，并对此现象的产生及Cl2的影响机制进行了详细探讨。

关键词 ：流化床, 碳钢, 腐蚀, 氯化

Abstract：Corrosion of A210-C carbon steel tube has been investigated after 1000h exposure at the place close to the bubbling bed of a bench-scale fluidized-bed combustor during firing a coal of low sulfur and high chlorine. It was foound that a heavily exfoliation of the wastage occurred in locations with the tube surface temperature of 460℃-560℃.The spalled wastage was mainly composed of hematite(Fe2O3) covered by a layer of deposits. (K,Na)Cl was locally detected in the deposits layer. By investigation of the residual wastage on the carbon steel tube,some locations at/near the interface of the wastage and the metal substrate did appear chlorization, which led to three different consequences:(1)formation of FeCl2 layer underneath the eastage,(2)rapid local corrosion,causing protrusions into the metal,(3)appearance of internal pores in the metal. The generation of the different morphologies above and effect of chlorine were both discussed in detail.

Key words： fluidized-bed combustor carbon steel corrosion chlorization

收稿日期: 2003-01-06

ZTFLH:

TG172.3

通讯作者: 彭晓

Corresponding author: Xiao Peng

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	彭晓
44.8K

引用本文:

彭晓 . 燃煤流化床中氯对碳钢腐蚀的影响机制[J]. 中国腐蚀与防护学报, 2004, 24(4): 193-197 .
Xiao Peng. Effect of Chlorine on the Degradation of a Carbon Steel in a Coal-Fired Fluidized-Bed Combustor. J Chin Soc Corr Pro, 2004, 24(4): 193-197 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I4/193

[1]StringerJ ,WrightIG .Currentlimitationsofhightemperaturealloysinpracticalapplications[J].Oxid.Met.,1995,44(1/2):265-308.
[2]JamesPJ,PinderLW .Theimpactoffuelchlorineonthefiresidecorro sionofboilertubing:aUKperspective[J].Mat.High.Temp.,1997,14(3):117-126
[3]GuttmannV ,SteinK ,BakkerWT .Deformation-corrosioninteractionsinselectedadvancedhightemperaturealloys[J].Mat.High.Temp.,1997,14(3):127-136
[4]ReeseE ,GrabkeHE .Effectsofchloridesontheoxidationof21/4Cr-1Mosteel[J].WerkstUndKorrosion,1992,43:547-557
[5]GrabkeHE ,ReeseE ,SpiegelM .Theeffectsofchlorides,hydrogen-chloride,andsulfurdioxideintheoxidationofsteelsbelowdeposits[J].Corros.Sci.,1995,37:1023-1043
[6]PengX ,LiuK ,HackP ,etal.TechnicalMeetingofCentralStatesSectiononCombustionFundamentsandApplications[M].Indianapolis,Indiana,USA ,April16-18,2000,p80
[7]PengX ,PanWP ,RileyJT .HightemperaturecorrosionofA210-Ccarbonsteelinsimulatedcoalcombustionatmospheres[J].Oxid.Met.,submittedforpublication
[8]XieW ,LiuK ,PanWP ,RileyJT .InteractionbetweenemissionsofSO2andHClinfluidizedbedcombustors[J].Fuel,1999,78:1425
[9]PengX ,PanWP ,RileyJT .Adegradationmodeofacarbonsteelduringthermalcyclingunderasimulatedcombustionenvironment[J].Mater.Sci.Eng.,2002,A332:270-275

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed