铀合金的大气腐蚀和应力腐蚀研究

中国腐蚀与防护学报

2004, Vol. 24

Issue (2): 112-115

研究报告

本期目录 | 过刊浏览

铀合金的大气腐蚀和应力腐蚀研究

许明;佘淑华;罗天元;杨晓然;龙文斌;张伦武

西南技术工程研究所

ATMOSPHERIC CORROSION AND STRESS CORROSION FOR URANIUM ALLOY

;;Tianyuan Luo;;;

西南技术工程研究所

全文: PDF(145 KB)

摘要: 概述了U-0.75Ti铀合金在典型大气环境中长期曝露和贮存时的腐蚀行为及应力腐蚀敏感性研究的一些主要结果,得到了铀合金在长期贮存条件下，能够长期保持极低的腐蚀速率和不存在明显的大气应力腐蚀的重要规律.论文讨论了铀合金在不同环境条件下的大气腐蚀的主要特点、规律和环境影响；讨论了铀合金大气应力腐蚀的特点、对环境条件的依存关系和有关的原因。

关键词 ：铀合金, 腐蚀, 应力腐蚀

Abstract：The corrosion property of U-0.75Ti uranium alloy that chronically exposed and stored in the typical atmosphere is summarized in this paper. Some main results of sensitivity study for stress corrosion are also summarized. Significant rules that the uranium alloy can chronically preserve very low corrosion rate and obvious atmosphere stress corrosion does not present on the condition that it had been stored chronically are gained. The main characteristic, rule, and environment influence of atmosphere corrosion for uranium alloy on the different condition are discussed in this paper. The characteristic of atmosphere stress corrosion for uranium alloy, the dependence connection with environment condition, and the concerned reason are discussed too.

Key words： uranium alloy corrosion stress corrosion

收稿日期: 2003-12-17

ZTFLH:

TG172.3

通讯作者: 许明 E-mail: zhang@public.chongqing.cngb.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	许明
	佘淑华
	罗天元
	杨晓然
	龙文斌
	张伦武
44.8K

引用本文:

许明; 佘淑华; 罗天元; 杨晓然; 龙文斌; 张伦武 . 铀合金的大气腐蚀和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2004, 24(2): 112-115 .
Tianyuan Luo. ATMOSPHERIC CORROSION AND STRESS CORROSION FOR URANIUM ALLOY. J Chin Soc Corr Pro, 2004, 24(2): 112-115 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I2/112

[1]ZabielskiCV ,etal.Corrosionofhighdensitykineticenergypene tratormaterials[A].AD -A249439MTL -TR ,92-17,1992
[2]KogerJW .Summarizeofcorrosion,anticorrosionandstresscorro sionforuraniumanduraniumalloy[A].TranslatedbyLiuming,Y/DV -202,1981,44-67(KogerJW .关于铀及铀合金的腐蚀、防腐和应力腐蚀问题概述[J].刘明译,Y/DV -202,1981,44-67)
[3]PowellGL ,etal.Hydrogeninuraniumalloys[A].Y -DA -5317,1973
[4]HemperlyVC .EffectoftherelativehumidityintestatmospheresonU -0.75TiandU -2.25Nb[A].Y -2043,1976
[5]NagelbergAS ,etal.CorrosionbehavioroflowTi-Uraniumalloy[J].TranslatedbyZhangjing,SAND 80-8215,1980(NagelbergAS等.低钛铀合金的腐蚀行为[J].张晶译,SAND80-8215,1980
[6]MagnaniNJ,etal.TheeffectofchlorideionsonthesusceptibilitytostresscorrosioncrackingofU -0.75Nb-2.5ZrandU -4.5Nballoys[A].SC -RR -70-860,1970
[7]MagnaniNJ.StresscorrosioncrackinginquenchedandinunderageU -67Nb[A].SAND -75-0191,1975
[8]MagnaniNJ .Thestress-corrosioncrackingbehavioroftwourani umalloyarmorpenetratormaterials[A].SLA -74-0304
[9]JohnsonHR ,DiniJW .OntheembrittlementofUandU -0.8Tialloysbyhydrogenandwater[A].SLL -73-5300
[10]MullerJF .Theeffectsofprocessingvariablesonthehydrogencontentandresultantmechanicalpropertiesofuraniumandurani um-3/4wt%titaniumalloy[A].LA -UR -80-3176
[11]KatyJJ ,etal.UraniumChemistry.Vo.1[M ].TranslatedbyRenliping,Fanyixian.Originaleditionin1951,Beijing:ChemicalIn dustryPress,1959(KatyJJ著.任丽素,范毅先译.铀化学·卷一[M ].1951年原版.北京:化学工业出版社,1959)
[12]McdBaterM ,etal.Uranium+waterreaction,Part1Kinetics,productsandmechanism[J].Trans.FaradySoc.62,1966,2513-2530

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed