硝酸铀酰溶液中不锈钢电极表面沉积氧化膜的行为研究

廖俊生;孙颖;陆春海

中国工程物理研究院

BEHAVIOR RESEARCH OF OXIDE FILM FORMED ON THE SURFACEOF STAINLESS STEEL ELECTRODE IN URANYL NITRATE SOLUTION

Junsheng Liao;Ying Sun;Chunhai Lu

中国工程物理研究院

全文: PDF(139 KB)

摘要: 用动电位极化法研究了不锈钢(1Cr17)电极在NaCl-UO2(NO 3)2溶液中的电化学行为.在阴极反应区，由于氢的不断释放，导致铀酰离子在不锈钢电极上析出.随着极化电位向阳极区移动，不锈钢电极发生阳极氧化，形成了氧化铀沉积膜. SEM对析出物和沉积膜的形貌进行了分析.AES深度剖析沉积膜的厚度约为40 nm.XPS分析证实不锈钢腐蚀电极表面沉积膜中铀为U(Ⅵ).

关键词 ：硝酸铀酰溶液, 不锈钢, 动电位极化, 表面分析

Abstract：The potentiodynamic polarization method has been us ed to investigate the electrochemical behavior of 1Cr17 stainless steels in NaCl -UO2(NO3)2 solution.The hydrogen gas was evolved in the cathodic reaction region,and led to the evolution of uranyl ion hydrolysis.The film formed on t he stainless steel electrode under the potentiodynamic polarization with increas ing sweep potential.SEM observation revealed image from the surface of the speci men.The deposit film was measured by Ar ion gun sputter,and the thickness was ab out 40 nm.The XPS analysis indicated that the surface region of film formed on the stainless steel electrode is composed of U(Ⅵ).The forming mechanism of depo sit film was initially discussed.

Key words： uranyl nitrate solution stainless steel potentiodyna mic polarization surface analysis

收稿日期: 2002-12-23

ZTFLH:

TG174.4

通讯作者: 廖俊生 E-mail: liao.jsh@163.com

Corresponding author: Junsheng Liao E-mail: liao.jsh@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	廖俊生
	孙颖
	陆春海
44.8K

引用本文:

廖俊生; 孙颖; 陆春海 . 硝酸铀酰溶液中不锈钢电极表面沉积氧化膜的行为研究[J]. 中国腐蚀与防护学报, 2003, 23(5): 282-285 .
Junsheng Liao, Ying Sun, Chunhai Lu. BEHAVIOR RESEARCH OF OXIDE FILM FORMED ON THE SURFACEOF STAINLESS STEEL ELECTRODE IN URANYL NITRATE SOLUTION. J Chin Soc Corr Pro, 2003, 23(5): 282-285 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I5/282

[1]SuterT ,BohniH .Anewmicroelectrochemicalmethodtostudypitinitiationonstainlesssteels[J].Electrochim.Acta,1997,42(20-22):3275-3280
[2]TsaiWenta,ChenMingshan.Stresscorrosioncrackingbehaviorof2205duplexstainlesssteelinconcentratedNaClsolution[J].Cor ros.Sci.,2000,42:545-559
[3]MartinBojinov,GunillaFabricius,TimoLaitinen.Conductionmech anismoftheanodicfilmonFe-Cralloysinsulfatesolutions[J].J .Electrochem.Soc.,1999,146(9):3238-3247
[4]LegrandL ,SavoyeS ,ChausseA ,etal.Studyofoxidationproductsformedonironinsolutionscontainingbicarbonate/carbonate[J].Electrochim.Acta,2000,46:111-117
[5]ChengYF ,LuoJL .Passivityandpittingofcarbonsteelinchro matesolutions[J].Electrochim.Acta,1999,44:4795-4804
[6]VargaK ,BarradlaiP ,HirschbergG ,etal.Corrosionbehaviorofstainlesssteelsurfacesformeduponchemicaldecontamination[J].Electrochim.Acta,2001,46:3783-3790
[7]EngelhardtJ,etal.Contactcorrosionmeasurementonthe pairUO2+xandcarbonsteel1.0330inbrinesandbentoniteporewaterwithrespecttodirectwastedisposal[J].J .NuclearMaterials,1999,264:161-168
[8]GuibertS ,GuittetMJ,BarreB ,etal.DissolutionofUO2 inboomclaywaterinoxidizingconditions:anXPSstudy[J].J .NuclearMa terials,2000,282:75-82

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[7]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[8]	秦越强, 左勇, 申淼. FLiNaK-CrF₃/CrF₂氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[10]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[11]	骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[12]	付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[13]	孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[14]	李雨,关蕾,王冠,张波,柯伟. 机械应力对不锈钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 215-226.
[15]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.

Viewed

Full text

Abstract

Cited

Shared

Discussed