中国的酸雨对材料腐蚀的经济损失估算

张学元;韩恩厚;李洪锡

中科院金属所金属腐蚀与防护国家重点实验室

ESTIMATION OF THE CORROSION LOSSES BY THE ACIDIC RAIN IN CHINA

Xueyun Zhang;Enhou Han;Hongxi Li

中科院金属所金属腐蚀与防护国家重点实验室

全文: PDF(155 KB)

摘要: 阐述了酸雨的形成和定义,酸雨在中国的分布与危害.根据传统的经验方法和Uhlig方法保守的估计了中国酸雨在1999年对材料的直接经济损失大约30亿元.间接损失要远高于这个数字.

关键词 ：酸雨, 腐蚀, 材料

Abstract：The formation and definition of acidic rain are des cribed respectively.Usually the rain with the pH value less than 5.6 is called a cidic rain.The corrosion due to the acidic rain is the most important type of th e atmosphere corrosion.The area where acidic rain falls covers one third of all over Chinese areas.With the developments of Chinese economy,acid precipitation a rea increased,the corrosion loss also increased.The direct corrosion loss due to the acidic rain on the material in 1999 was estimated to be 3.0 billion RMB or so by the experience estimation and Uhlig method.

Key words： acidic rain corrosion material

收稿日期: 2000-12-30

ZTFLH:

TG172.3

通讯作者: 张学元

Corresponding author: Xueyun Zhang

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张学元
	韩恩厚
	李洪锡
44.8K

引用本文:

张学元; 韩恩厚; 李洪锡 . 中国的酸雨对材料腐蚀的经济损失估算[J]. 中国腐蚀与防护学报, 2002, 22(5): 316-319 .
Xueyun Zhang, Enhou Han, Hongxi Li. ESTIMATION OF THE CORROSION LOSSES BY THE ACIDIC RAIN IN CHINA. J Chin Soc Corr Pro, 2002, 22(5): 316-319 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2002/V22/I5/316

[1]ChenZhiyuan.ResearchontheChineseAcidicRain[M].Beijing:Chi neseEnvironmentScienceHouse,1997(陈志远.中国酸雨研究[M].北京:中国环境科学出版社,1997)
[2]YinYaode.TheestimationonthecorrosionlossduetotheacidicraininthetwoprovincesofsouthwesternChina[J].Corros.Sci.Prote.Tech nol.,1991,3(1):37(银耀德.西南两省酸雨对材料腐蚀的经济损失估算[J].腐蚀科学与防护技术,1991,3(1):37)
[3]WangMingxing.AtmosphereChemistry[M ].Beijing:MeteorologicalHouse,1991(王明星.大气化学[M].北京:气象出版社,1991)
[4]StateEnvironmentalProtectionBureau.BulletinofChineseenvironmen talstatusin1999[J].EnvironmentalProtection,2000,7:3(国家环境保护总局.1999年中国环境状况公报[J].环境保护,2000,7:3)
[5]CorrosionandProtectionCommitteeofJapan.Corrosionlossinthechem icalplantsofChugokuShikokuDistrictofJapan[J].MaterialandEnvi ronment,2000,49(7):394
[6]HuTieqi,ZuoDanjiang,FanHongyi,TanPeizhen.ThedevelopmentandunbalanceofChineseplating[J].MaterialsProtection,2000,33(2):8.(胡铁骑,左丹江,范宏义,谭沛真.中国电镀行业的发展与不平衡[J].材料保护,2000,33(2):8)
[7]GengBingxi.IncreasingthedevelopmentofChinesezincplatingsteeltograspthechance[J].MetallurgicalInformation,2000,4:6.(耿炳玺.抓住机遇加快我国镀锌板的发展[J].冶金信息,2000,4:6)
[8]WangShuqiang.Researchonthesalesandserviceofcoating[J].Chi neseCoating,2000,1:23(王树强.涂料行业销售与服务模式的探讨[J].中国涂料,2000,1:23)
[9]Headsoffactoriesexchanginggroups.AnalysesontheeconomicsrunningofsomeChinesecoatingcompanies[J].ChineseCoating,2000,3:12(厂际交流组厂长.涂料行业部分企业经济运行分析[J].中国涂料,2000,3:12)
[10]RomualdJuchniewicz.ThecorrosionPreventionStrategyinthePolishE conomy[J].CorrosionReviews,1998,16(3):285
[11]Theanticorrosionsociety.ReportoftheCorrosionLossinJapan[J].An ticorrosionTechniques,1977,26(7):401
[12]RobertBaboian,MaterialsDegradationCausedbyAcidRain[M ].Washington:AmericanChemicalSociety,1986
[13]Theanticorrosionsociety.CorrosionlossinthechemicalplantsofChugokuShikokuDistrictofJapan[J].MaterialandEnvironment,2000,49(7):394
[14]HeWenle.CorrosionRatesandRunoffRatesofCopperandZincasRoofingMaterials[M].Stockholm:RoyalInstituteofTechnology,2000.
[15]WangGuangyong,WangHaijiang,LiXinglian,YinYaode.CorrosionandProtectionintheNaturalEnvironment[M ].Beijing:ChemicalIn dustryHouse,1997(王光雍,王海江,李兴濂,银耀德.自然环境的腐蚀与防护[M].北京:化学工业出版社,1997)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[10]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[11]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[12]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[13]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[14]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[15]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.

Viewed

Full text

Abstract

Cited

Shared

Discussed