Hot Corrosion Behavior of Four Modified Aluminide Coatings on DZ38G Alloy

WU Duoli, ZHANG Hongyu, WEI Hua(

), ZHENG Qi, JIN Tao, SUN Xiaofeng

Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016, China

全文: PDF(6251 KB) HTML

摘要:

在DZ38G高温合金表面制备了NiCr-CrAl,Co-Al,Al-Si和Al-Ti 4种改性的铝化物涂层,对比研究了4种涂层的组织结构和在900 ℃下的涂盐 (25%NaCl(质量分数)+75%Na₂SO₄ (质量分数)) 热腐蚀行为。结果表明：在4种涂层中,Al-Ti涂层表面腐蚀产物连续致密,而且与基体结合紧密,表现出最优异的抗热腐蚀性能。

关键词 ：高温合金, 涂层, 热腐蚀

Abstract：

Four modified aluminide coatings were prepared on superalloy DZ38G, which include a two step co-cementation coating NiCr-CrAl and three one step co-cementation coatings Co-Al, Al-Si and Al-Ti. Then their microstructure and hot corrosion behavior in a salt melt of 25%NaCl (mass fraction)+75%Na₂SO₄ (mass fraction) at 900 ℃ were investigated. The results show that a continuously compact scale of corrosion products with good adhesion to the matrix could form on Ti-Al coating during corrosion, therefore, the Al-Ti coating may provide much better protectiveness to the alloy rather than the other three coatings in this kind of salt mixture.

Key words： superalloy coating hot corrosion

ZTFLH:

TG174.3

基金资助:国家自然科学基金项目 (51371173) 资助

作者简介: null

吴多利，男，1987年生，硕士，研究方向为高温合金及其腐蚀防护

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	吴多利
	张洪宇
	韦华
	郑启
	金涛
	孙晓峰
44.8K

引用本文:

吴多利, 张洪宇, 韦华, 郑启, 金涛, 孙晓峰. 4种改性的铝化物涂层对DZ38G合金热腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2014, 34(6): 502-506.
Duoli WU, Hongyu ZHANG, Hua WEI, Qi ZHENG, Tao JIN, Xiaofeng SUN. Hot Corrosion Behavior of Four Modified Aluminide Coatings on DZ38G Alloy. Journal of Chinese Society for Corrosion and protection, 2014, 34(6): 502-506.

链接本文:

https://www.jcscp.org/CN/10.11902/1005.4537.2013.232 或 https://www.jcscp.org/CN/Y2014/V34/I6/502

表1 4种涂层外层元素的含量

图1 DZ38G合金表面4种涂层在900 ℃的热腐蚀动力学曲线

图2 DZ38G合金表面4种涂层在900 ℃热腐蚀100 h后的XRD谱

图3 DZ38G合金表面NiCr-CrAl涂层热腐蚀100 h后的表面形貌

图4 DZ38G合金表面Co-Al涂层热腐蚀100 h后的表面形貌

图5 DZ38G合金表面Al-Si涂层热腐蚀100 h后的表面形貌

图6 DZ38G合金表面Al-Ti涂层热腐蚀100 h后的表面形貌

图7 DZ38G合金表面不同涂层热腐蚀100 h后的剖面形貌

[1]	Li M H, Sun X F, Jin T, et al. Oxidation behavior of a single-crystal Ni-base superalloy in air-II: At 1000, 1100, and 1150 ℃[J]. Oxid. Met., 2003, 60(1/2): 195-210
[2]	Li M H, Sun X F, Li J G, et al. Oxidation behavior of a single-crystal Ni-base superalloy in air-I: At 800 and 900 ℃[J]. Oxid. Met., 2003, 59(5/6): 591-605
[3]	Guo J T. Development report of superalloy [A]. National Conference on Superalloy [C]. Dalian, 2004
[3]	(郭建亭. 高温合金的发展报告 [A]. 全国高温合金会议 [C]. 大连, 2004)
[4]	Li M S. High Temperature Corrosion of Metals[M]. Beijing: Metallurgical Industry Press, 2001: 410-433
[4]	(李美栓. 金属的高温腐蚀[M]. 北京: 冶金工业出版社, 2001: 410-443)
[5]	Schneider K, Grunling H W. Mechanical aspects of high temperature coatings[J]. Thin Solid Films, 1983, 107(4): 395-416
[6]	Veys J M, Meverel R. Influence of protective coatings on the mechanical properties of CMSX-2 and Cotan784[J]. Mater. Sci. Eng., 1987, 88: 253-260
[7]	Meetham G W. High temperature materials in gas turbine engines[J]. Mater. Des., 1988, 9(4): 213-219
[8]	Itoh Y, Saitoh M, Ishiwata Y. Influence of high-temperature protective coatings on the mechanical properties of nickel-based superalloys[J]. J. Mater. Sci., 1999, 34(16): 3957-3966

[1]	姜伯晨, 曹将栋, 曹雪玉, 王建涛, 张少朋. Gd₂(Zr_1-_xCe_x)₂O₇热障涂层陶瓷层材料的CMAS热腐蚀行为研究[J]. 中国腐蚀与防护学报, 2021, 41(2): 263-270.
[2]	曹京宜, 杨延格, 方志刚, 寿海明, 李亮, 冯亚菲, 王兴奇, 褚广哲, 赵伊. 淡水舱涂层在不同水环境中的失效行为研究[J]. 中国腐蚀与防护学报, 2021, 41(2): 209-218.
[3]	栾浩, 孟凡帝, 刘莉, 崔宇, 刘叡, 郑宏鹏, 王福会. 间苯二胺-氧化石墨烯/有机涂层的制备及防腐性能研究[J]. 中国腐蚀与防护学报, 2021, 41(2): 161-168.
[4]	刘洋, 吴进怡, 闫小宇, 柴柯. 海洋环境中芽孢杆菌对聚氨酯清漆涂层分解的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[5]	任岩, 钱余海, 张鑫涛, 徐敬军, 左君, 李美栓. 热震对包覆ZrB₂-SiC-La₂O₃/SiC涂层渗硅石墨力学性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 29-35.
[6]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[7]	曹京宜, 王智峤, 李亮, 孟凡帝, 刘莉, 王福会. 深海压力交变加速条件下改性石墨烯有机涂层的失效机制[J]. 中国腐蚀与防护学报, 2020, 40(2): 139-145.
[8]	师超,邵亚薇,熊义,刘光明,俞跃龙,杨志广,许传钦. 硅烷偶联剂改性磷酸锌对环氧涂层防腐性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 38-44.
[9]	赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[10]	王贵容,郑宏鹏,蔡华洋,邵亚薇,王艳秋,孟国哲,刘斌. 环氧防腐涂料在模拟海水干湿交替条件下的失效过程[J]. 中国腐蚀与防护学报, 2019, 39(6): 571-580.
[11]	余春堂,阳颖飞,鲍泽斌,朱圣龙. 先进高温热障涂层用高性能粘接层制备及研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 395-403.
[12]	李烽杰,陈明辉,张哲铭,王硕,王福会. 金属搪瓷高温防护涂层的制备及其抗热震行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 411-416.
[13]	陈超,梁艳芬,梁天权,满泉言,罗毅东,张修海,曾建民. 稀土复合掺杂ZrO₂陶瓷涂层抗Na₂SO₄+NaVO₃热腐蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 291-298.
[14]	艾鹏,刘礼祥,李晓罡,姜文涛. TiAlSiN涂层对γ-TiAl基合金抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[15]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.

Viewed

Full text

Abstract

Cited

Shared

Discussed