铜合金在海洋飞溅区的腐蚀

中国腐蚀与防护学报

2005, Vol. 25

Issue (2): 65-69

研究报告

本期目录 | 过刊浏览

铜合金在海洋飞溅区的腐蚀

黄桂桥

青岛海洋腐蚀研究所

CORROSION OF COPPER ALLOYS IN MARINE SPLASH ZONE

Guiqiao Huang

青岛海洋腐蚀研究所

全文: PDF(158 KB)

摘要: 研究了12种铜合金在青岛海域飞溅区暴露16年的腐蚀结果及其腐蚀行为和规律。铜合金在飞溅区的腐蚀率均较低。在飞溅区短期暴露，铜合金的腐蚀类型为均匀腐蚀，长期暴露的铜合金发生较轻的点蚀和缝隙腐蚀，黄铜有脱锌腐蚀倾6，白铜有脱镍腐蚀倾向。纯铜和青铜的腐蚀率随暴露时间增加而降低。HMn58-2和HSn62-1随暴露时间增加南而降低，长期暴露腐蚀率出现上升的趋势。HAl77-2和BFe10-1-1的腐蚀率随时间增加而略有增加。长期暴露的HAl77-2、BFe10-1-1和BFe30-1-1的耐蚀性比钝铜墙铁壁差。铜合金在飞溅区的腐蚀比全浸区、潮汐区轻，比海洋大气区重。

关键词 ：腐蚀, 铜, 海洋, 飞溅区

Abstract：Corrosion results of 12 types of copper alloys exposed to marine splash zone at Qingdao Sea area of China were reported. Corrosion behavior and law of copper alloys in splash zone was summarized. Corrosion rate of copper alloys in splash zone was low. Corrosion type of copper alloys was uniform corrosion in splash zone for short period exposure.Exposing to splash zone for long period,copper alloys occurred not serious pitting and crevice corrosion.Their maximum pitting depths in splash zone at Qingdao Sea area for 16 years were less than 0.3mm.Brass had tendency of dezincification corrosion; and Cu-Ni alloys took place denickel corrosion.Corrosion rate of pure copper and bronzes fell with exposure time.Corrosion rate of HMn58-2 and HSn62-1exposed to splash zone during 1~4years fell with exposure time,after which the corrosion rate raised with exposure time.Corrosion rate of HAl77-2 and BFe10-1-1rose slowly with exposure time.Exposing to splash zone for long time, xorrosion resistance of copper alloys in splash zone was better than that in full immersion zone and tide zone, and was poorer than that in marine atmosphere.

Key words： corrosion copper marine splash zone

收稿日期: 2003-09-19

ZTFLH:

TG172.5

通讯作者: 黄桂桥

Corresponding author: Guiqiao Huang

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	黄桂桥
44.8K

引用本文:

黄桂桥 . 铜合金在海洋飞溅区的腐蚀[J]. 中国腐蚀与防护学报, 2005, 25(2): 65-69 .
Guiqiao Huang. CORROSION OF COPPER ALLOYS IN MARINE SPLASH ZONE. J Chin Soc Corr Pro, 2005, 25(2): 65-69 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I2/65

[1]SchumacherM .SeawaterCorrosionHandbook[M ].ParkRideg,NewJersey:NoyesDataCorporation,1979,41-50:150-234
[2]HummerCW ,SoushwellCR ,AlexanderAL .Corrosionofmetalsintropicalenvironment-copperandwroughtcopperalloys[J].Mater.Prot.,1968,7(1):41-47
[3]BulowCL .Useofcopperbasealloysinmarineservices[J].NavalEngineersJrnl.,1965,77(4):470-482
[4]HuangGQ ,YouJT ,YuCJ .CorrosionandfoulingofcopperalloysexposedtoseawateratQingdaoSeaarea[J].Mater.Prot.,1997,30(2):7-9(黄桂桥,尤建涛,郁春娟.铜及其合金在青岛海域的腐蚀和污损[J].材料保护,1997,30(2):7-9)
[5]HuangGQ .Corrosionofnon-ferricmetalsinmarinetidalzone[A].In:LinChangjian,CaiWenda(ed).DevelopmentofMaterialsCorrosionandPreventionfortheTwainShoreoftheChannel[C].Xiamen:PressofXiamenUniversity,1998,316-318(黄桂桥.有色金属材料在海洋潮差区的腐蚀[A].林昌健,蔡文达编,海峡两岸材料腐蚀与防护研究进展[C].厦门:厦门大学出版社,1998,316-318)
[6]LiWJ ,LiuDY ,WeiKJ .Corrosionbehaviorofcopperalloysex posedinSouthChinaSeafor8years[J].Corros.Sci.Prot.Tech nol.,1995,7(3):232-236(李文军,刘大扬,魏开金.在南海海域铜合金8年腐蚀行为研究[J].腐蚀科学与防护技术,1995,7(3):232-236)
[7]HuangGQ ,YuCJ .Corrosionofmetalmaterialsinmarinesplashzone[J].Mate.Prot.,1999,32(2):28-30(黄桂桥,郁春娟.金属材料在海洋飞溅区的腐蚀[J].材料保护,1999,32(2):28-30)
[8]HuangGQ ,WangXR ,LinLY ,YuanYM .AstudyondealloyingcorrosioncharacterofcopperalloysexposedinQingdaoSeaarea[J].Corros.Sci.Prot.Technol.,1995,7(3):237-240(黄桂桥,王相润,林乐耘,严宇民.青岛海域铜合金脱成份腐蚀特征研究[J].腐蚀科学与防护技术,1995,7(3):237-240)

[1]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[2]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[3]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[4]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[5]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[6]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[7]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[8]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[9]	刘洋, 吴进怡, 闫小宇, 柴柯. 海洋环境中芽孢杆菌对聚氨酯清漆涂层分解的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[10]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[11]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[12]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[13]	王雷, 董俊华, 韩达, 梁坚坤, 李权, 柯伟. 含铜钢在1150 ℃高温保温条件下的铜偏聚现象[J]. 中国腐蚀与防护学报, 2020, 40(6): 545-552.
[14]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[15]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.

Viewed

Full text

Abstract

Cited

Shared

Discussed