中国腐蚀与防护学报  2004, Vol. 24 Issue (5): 289-292     
  研究报告 本期目录 | 过刊浏览 |
渗铝304不锈钢不同实验方法的SCC敏感性评价
高红霞
郑州轻工业学院机电系
The Appraisal on SCC Susceptibility of Aluminized 304 Stainless Steel by Different Test Means
Hongxia Gao
郑州轻工业学院机电系
全文: PDF(173 KB)  
摘要: 采用恒载荷试验方法及慢应变速率试验(SSRT)方法研究了渗铝304奥氏体不锈钢在沸腾42%MgCl2溶液中的应力腐蚀破裂(SCC)性能,分析了渗铝不锈钢SCC机理,讨论了不同试验方法对渗铝不锈钢SCC敏感性评价的影响。试验表明:渗铝处理可明显提高304钢抗SCC性能,其机理为渗铝层的环境遮断作用及对基体的电化学保护作用。两种方法在评价各种渗铝钢材料SCC性能方面有统一性:恒载荷试验中SCC敏感性指标σth高的材料,SSRT中SCC敏感性指标δi也相对较高。但两种方法中渗铝试样的断口形态表现出差异:恒载荷试验为穿晶型SCC断口,而SSRT无SCC断口特征,为韧性断口。
关键词 渗铝不锈钢SCC敏感性试验方法    
Abstract:By means of constant load tests and slow strain rate tests(SSRT), the SCC behavior of aluminized 304 stainless steel in boiling 42% MgCl2 solution was studied. The SCC mechanism of aluminized 304 steel has been analyzed This paper mainly discusses the influence of different test means on the evaluation SCC susceptibility of aluminized 304 steel. Two test methods both show that aluminizing treatment improved the resistance to SCC of SUS 304, the mechanisms were the environment covering action and the electrochemical protective action of the aluminized layer. The two methods were the same in appraisal of SCC properties of aluminized 304 steel, the more the SCC target of constant load test(σth ),the more the SCC target of SSRT( δi),but the two means was different in the formation of fracture surface. The fracture of constant load tests was transgranular SCC mode, whereas the SSRT fracture surface was tough and without SCC fracture characteristics.
Key wordsaluminizing    stainless steel    SCC susceptibility    experimental method
收稿日期: 2003-01-25     
ZTFLH:  TG172.9  
通讯作者: 高红霞   
Corresponding author: Hongxia Gao   

引用本文:

高红霞 . 渗铝304不锈钢不同实验方法的SCC敏感性评价[J]. 中国腐蚀与防护学报, 2004, 24(5): 289-292 .
Hongxia Gao. The Appraisal on SCC Susceptibility of Aluminized 304 Stainless Steel by Different Test Means. J Chin Soc Corr Pro, 2004, 24(5): 289-292 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2004/V24/I5/289

[1]MasamichiKowaka,KazuoYamanaka.Theeffectofalloyingele mentsandtestingmethodsonintergranularfractureinchloridestresscorrosioncrackingofausteniticstainlesssteels[J].Anticorro sionTechnology,1980,29:449-456(小若正伦,山中和夫.ォ-ステナィト系ステンレス钢の盐化物应力腐食割わにおける粒界割わ出现に及ぼす负荷方法·合金元素の影响[J].防食技术,1980,29:449-456)
[2]TadakazuOhnishi.Testmethodsforstresscorrosioncracking[J].LightMetal,1984,34(2):132-147(大西忠一.应力腐食割わ试验法[J].轻金属,1984,34(2):132-147)
[3]GaoHX .TheInfluenceofslurryaluminisingonSCCbehaviorof304steel[D].Zhengzhou:MastershipTreatiseofZhengzhouInsti tuteofIndustry,1990(高红霞.料浆渗铝对奥氏体不锈钢SCC的影响[D].郑州:郑州工学院硕士学位论文,1990年)
[4]WangZ ,GaoHX ,WangSY .TheinfluenceofslurryaluminisingonSCCof304stainlesssteel[J].J.Chin.Soc.Corros.Prot.,1992,12(2):154-159(王正,高红霞,.王素英.料浆渗铝对304不锈钢应力腐蚀开裂的影响[J].中国腐蚀与防护学报,1992,12(2):154-159)
[5]WangZQ ,WuYL ,JiXC .StudyonthemechanismofSCCtoausteniticstainlesssteelinboiling42%MgCl2 solution[J].J.Chin.Soc.Corros.Prot.,1984,4(3):187-197(王正樵,吴幼林,纪晓春.奥氏体不锈钢在沸腾42%MgCl2溶液中应力腐蚀破裂过程的研究[J].中国腐蚀与防护学报,1984,4(3):187-197)
[6]MasamichiKowaka.CorrosionWreckageandAnticorrosionTech nologyofMetal[M ].Beijing:ChemicalIndustryPress,1998:26-28(小若正伦.金属的腐蚀破坏与防蚀技术[M ].北京:化学工业出版社,1998:26-28)
[1] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2] 左勇, 曹明鹏, 申淼, 杨新梅. MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3] 王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4] 张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe3+对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5] 马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[6] 赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[7] 胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[8] 秦越强, 左勇, 申淼. FLiNaK-CrF3/CrF2氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[9] 何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[10] 武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[11] 骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[12] 付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.
[13] 孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[14] 李雨,关蕾,王冠,张波,柯伟. 机械应力对不锈钢点蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 215-226.
[15] 李兆登,崔振东,侯相钰,高丽丽,王维珍,尹建华. 核级316LN不锈钢焊接接头在高温高压水中的腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 106-113.