中国腐蚀与防护学报  2004, Vol. 24 Issue (2): 65-70     
  研究报告 本期目录 | 过刊浏览 |
316不锈钢在模拟冷却水中的钝化模型
葛红花;周国定;吴文权
上海电力学院环境工程系国家电力公司热力设备腐蚀与防护重点实验室
PASSIVATION MODEL OF STAINLESS STEEL IN SIMULATED COOLING WATER
Ge Honghua;Zhou Guoding; Wu Wenquan
上海电力学院环境工程系国家电力公司热力设备腐蚀与防护重点实验室
全文: PDF(192 KB)  
摘要: 测定了316不锈钢在模拟冷却水中长期浸泡(1~65d)和短期浸泡(1h内)过程中的电化学阻抗谱,并用4种钝化模型进行了拟合,确定了适合本体系的钝化模型。拟合结果显示,在长期浸泡过程中,浸泡初期电荷转移电阻R1较小,而反映双电层电容的Y01值较大,随浸泡时间增加,R1、Y01值趋于稳定;膜电阻R2在电极浸泡过程中不断增大,膜电容Y02值则不断减小,显示钝化膜的增厚和致密;8d后R2比R1约大4个数量级。短期浸泡过程中,浸泡5min时,R1与R2数值接近;随浸泡时间延长,R1变化不大,而R2在15min内增大了一个数量级,并不断随时间延长而增大。
关键词 不锈钢钝化膜电化学阻抗谱拟合    
Abstract:The electrochemical impedance spectroscopy for stainless steel in simulated cooling water during long time immersion (1~65 days) and short time immersion (in one hour) are measured. The data are fitted using four models, and a suitable model is selected. The fitting results appear that, during the long time immersion period, the charge-transfer resistance R1 is relatively small and the double layer capacity Y01 is relatively large at the beginning of the immersion. When the immersion time increases, the values of R1 and Y01 stabilize. The film resistance R2 increases while the value of Y02 decreases continuously with the immersion, indicating that the passive film is getting thicker and more compact. The value of R2 is about four orders larger than R1 after 8 days' immersion. During the short time immersion period, R1 is close to R2 at 5 min; R1 changes little with time, but R2 increases by one order at 15 min and rises continuously with the immersion.
Key wordsstainless steel    electrochemical impedance spectroscopy    passive film    fitting
收稿日期: 2003-12-17     
ZTFLH:  TG174.2+1  
通讯作者: 葛红花     E-mail: honghge@2hotmail.com

引用本文:

葛红花; 周国定; 吴文权 . 316不锈钢在模拟冷却水中的钝化模型[J]. 中国腐蚀与防护学报, 2004, 24(2): 65-70 .
Ge Honghua, Zhou Guoding, Wu Wenquan. PASSIVATION MODEL OF STAINLESS STEEL IN SIMULATED COOLING WATER. J Chin Soc Corr Pro, 2004, 24(2): 65-70 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2004/V24/I2/65

[1]HakikiNE ,CunhaBeloMDa,SimoesAMP ,etal.Semiconduct ingpropertiesofpassivefilmsformedonstainlesssteels[J].J.Electrochem.Soc.,1998,145(11):3821-3829
[2]MontemorMF ,FerreiraMGS ,HakikiNE ,etal.Chemicalcon positionandelectronicstructureoftheoxidefilmsformedon316Lstainlesssteelandnickelbasedalloysinhightemperatureaqueousenvironments[J].Corros.Sci.,2000,42:1635-1650
[3]SchultzeJW ,LohrengelMM .Stability,reactivityandbreakdownofpassivefilms.problemsofrecentandfutureresearch[J].Elec trochim.Acta,2000,45:2499-2513
[4]BlenginoJM ,keddamM ,LabbeJP ,RobbiolaL .Physico-chemi calcharacterizationofcorrosionlayersformedonironinasodiumcarbonate-bicarbonatecontainingenvironment[J].Corros.Sci.,1995,37(4):621-643
[5]Horvat-RadosevicV ,KvastekK ,HodkoD ,PravdicV .ImpedanceofanodicallypassivatedFe80B20overpotentialsfrompassivestatetooxygenevolution[J].Electrochim.Acta,1994,39(1):119-130
[6]GaberscekM ,PejovnikS .Impedancespectroscopyasatechniqueforstudyingthespontaneouspassivationofmetalsinelectrolytes[J].Electrochim.Acta,1996,41(7/8):1137-1142
[7]CastroEB ,VilcheJR .Investigationofpassivelayersonironandiron-chromiumalloysbyelectrochemicalimpedancespectroscopy[J].Electrochim.Acta,1993,38(11):1567-1572
[8]MacDonaldDD .Reviewofmechanisticanalysisbyelectrochemicalimpedancespectroscopy[J].Electrochim.Acta,1990,35(10):1509-1525
[9]ArmstrongRD ,EdmondsonK .Theimpedanceofmetalsinthepassiveandtranspassiveregions[J].Electrochim.Acta,1973,18:937-943
[10]YinQ ,KelsallGH ,VaughanDJ ,etal.Mathematicalmodelsfortime-dependentimpedanceofpassiveelectrodes[J].J.Elec trochem.Soc.,2001,148(3):A200-A208
[11]HongT ,WalterGW ,NagumoM .Theobservationoftheearlystagesofpittingonpassivatedtype304stainlesssteelina0.5mol/LNaClsolutionatlowpotentialsinthepassiveregionbyus ingtheacimpedancemethod[J].Corros.Sci.,1996,38(9):1525-1533
[12]GonzalezJEG ,SantanaFJH ,Mirza-RoscaJC .Effectofbacte rialbiofilmon316SScorrosioninnaturalseawaterbyEIS[J].Corros.Sci.,1998,40(12):2141-2154
[13]ChaoCY ,LinLF ,MacDonaldDD .Apointdefectmodelforan odicpassivefilms.Ⅲ.Impedanceresponse[J].J .Electrochem.Soc.,1982,129(9):1874-1879
[14]MacDonaldDD .Thepointdefectmodelforthepassivestate[J].J .Electrochem.Soc.,1992,139(12):3434-3449
[15]MartiniEMA ,MullerIL .Characterizationofthefilmformedinironinboratesolutionbyelectrochemicalimpedancespectroscopy[J].Corros.Sci.,2000,42(3):443-454
[16]JamnikJ,MaierJ ,PejovnikS .Apowerfulelectricalnetworkmodelfortheimpedanceofmixedconductors[J].Electrochim.Acta,1999,44:4139-4145
[17]ItagakiM .Measurementandinterpretationofelectrochemicalimpedance[J].Corros.Eng.,1999,48:905-913
[18]AzumiK ,OhtsukaT ,SatoN .Impedanceofironelectrodepassivat edinborateandphosphatesolutions[J].TransactionsoftheJapanInstituteofMetals,1986,27(5):382-392
[19]GaberscekM ,PejovnikS .Impedancespectroscopyasatechniqueforstudyingthespontaneouspassivationofmetalsinelectrolytes[J].Electrochim.Acta,1996,41(7/8):1137-1142
[1] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2] 左勇, 曹明鹏, 申淼, 杨新梅. MgCl2-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[3] 王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[4] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[5] 张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe3+对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[6] 马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[7] 赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[8] 胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[9] 胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[10] 秦越强, 左勇, 申淼. FLiNaK-CrF3/CrF2氧化还原缓冲熔盐体系对316L不锈钢耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 182-190.
[11] 何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[12] 武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[13] 张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[14] 骆鸿,高书君,肖葵,董超芳,李晓刚. 磁控溅射工艺对CrN薄膜及其腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[15] 付安庆,赵密锋,李成政,白艳,朱文军,马磊,熊茂县,谢俊峰,雷晓维,吕乃欣. 激光表面熔凝对超级13Cr不锈钢组织与性能的影响研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 446-452.