N80油管钢CO2腐蚀点蚀行为

陈长风;路民旭;赵国仙

北京科技大学材料科学与工程学院

BEHAVIOR OF CO2 PITTING CORROSION OF N80 STEEL

Changfeng Chen;Minxv Lu;Guoxian Zhao

北京科技大学材料科学与工程学院

全文: PDF(187 KB)

摘要: 在模拟油田CO2腐蚀环境下，利用XRD、EDS和SEM研究了N8 0钢点蚀坑的形成与发展.结果表明，Cl-会在腐蚀产物膜与金属界面处富积成核，加速该区域的阳极溶解，促使点蚀坑的形核；点蚀坑内也有Cl-富积，在膜与基体界面处形成厚度为3 μm的富积层，加速点蚀坑内基体的腐蚀，使得点蚀坑进一步发展.同时，讨论了阳极反应与点蚀坑形貌之间的关系.

关键词 ： CO2, 腐蚀, 点蚀, N80钢, 腐蚀产物膜

Abstract：In simulating the environment of CO2 corrosion in oilfield,the XRD，EDS and SEM techniques were adopted to study the formation an d development of CO2 pitting corrosion on N80 steel.The results demonstrated t hat Cl- anions could be enriched and nucleated at the interface between corros ion scale and matrix,which subsequently catalyzed the formation of pitting.Where as pits could also be enriched by Cl- forming approximately 3 μm enrichment l ayer at interface,thus leading to the further development of pitting.In present case,the relationship between mechanisms of anodic reaction and morphology of pi tting was discussed.

Key words： CO2 corrosion pitting N80 steel corrosion scale

收稿日期: 2001-04-04

ZTFLH:

TG174

通讯作者: 陈长风

Corresponding author: Changfeng Chen

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	陈长风
	路民旭
	赵国仙
44.8K

引用本文:

陈长风; 路民旭; 赵国仙 . N80油管钢CO2腐蚀点蚀行为[J]. 中国腐蚀与防护学报, 2003, 23(1): 21-25 .
Changfeng Chen, Minxv Lu, Guoxian Zhao. BEHAVIOR OF CO2 PITTING CORROSION OF N80 STEEL. J Chin Soc Corr Pro, 2003, 23(1): 21-25 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I1/21

[1]ZhangXY ,DiC ,LeiLC .CO2CorrosionandControl[M ].Beijing:ChemicalIndustryPress,2000(张学元,邸超,雷良才.二氧化碳腐蚀与控制[M ].北京:化学工业出版社,2000)
[2]ChenCF ,ZhaoGX ,YanML ,etal.StudyofCO2 corrosionscalesonN80steel[J].J .ChineseSocietyforCorrosionandProtection,2002,22(3):143(陈长风,赵国仙,严密林.N80钢CO2腐蚀产物膜研究[J].中国腐蚀与防护学报,2002,22(3):143)
[3]YangW ,GuJX ,LiQS ,XiaoJX .LocalCorrosionofMetal[M ].Beijing:ChemicalIndustryPress,1995,44-46(杨武,顾氵睿祥,黎樵焱木,肖京先.金属的局部腐蚀[M ].北京:化学工业出版社,1995,44-46)
[4]NorioSato.Towardamorefundamentalunderstandingofcorrosionprocesses[J].Corrosion,1989,45(5):354-368
[5]MaoX ,LiuX ,RevieXW .Pittingcorrosionofpipelinesteelindi lutebicarbonatesolutionwithchlorideions[J].Corrosion,1994,50(9):651-657
[6]PalaciosCA ,ShadleyJR .CharacteristicsofcorrosionscalesonsteelsinCO2-saturatedNaCIbrine[J].Corrosion,1991,47(2):122-127
[7]LinterBR ,BursteinGT .Reactionofpipelinesteelsincarbondiox idesolutions[J].Corros.Sci.,1999,42(2):117-139
[8]DaviesDH ,BursteinGT .Theeffectsofbicarbonateonthecorro sionandpassivationofiron[J].Corrosion,1980,36(8):416-422
[9]OgundeleGI,WhiteWE .Someobservationoncorrosionofcarbonsteelinaqueousenvironmentscontainingcarbondioxide[J].Corro sion,1986,42(2):71-76
[10]CroletJL ,BonisMR .PHmeasurementsinaqueousCO2 solutionunderhighpressureandtemperature[J].Corrosion,1983,39(2):39-46
[11]ShanghaiPharmaceuticalIndustryDesignInstitute.HandbookforChemicalEngineeringTechnologyDesign[M ].Beijing:ChemicalIndustryPress,1996,2-364(上海医药设计院编.化工工艺设计手册[M ].北京:化学工业出版社,1996,2-364)

[1]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[2]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[3]	董续成, 管方, 徐利婷, 段继周, 侯保荣. 海洋环境硫酸盐还原菌对金属材料腐蚀机理的研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[4]	唐荣茂, 朱亦晨, 刘光明, 刘永强, 刘欣, 裴锋. Q235钢/导电混凝土在3种典型土壤环境中腐蚀的灰色关联度分析[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[5]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[6]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[7]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[8]	左勇, 曹明鹏, 申淼, 杨新梅. MgCl₂-NaCl-KCl熔盐体系中金属Mg对316H不锈钢的缓蚀性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	王欣彤, 陈旭, 韩镇泽, 李承媛, 王岐山. 硫酸盐还原菌作用下2205双相不锈钢在3.5%NaCl溶液中应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[10]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[11]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[12]	贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[13]	赵鹏雄, 武玮, 淡勇. 空间分辨技术在金属腐蚀原位监测中的应用[J]. 中国腐蚀与防护学报, 2020, 40(6): 495-507.
[14]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[15]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.

Viewed

Full text

Abstract

Cited

Shared

Discussed