OBSERVATION OF THE EFFECT OF SHOT BLASTED ON STEAM OXIDATIONRESISTANCE OF TP304H STEEL BOILER TUBING

J Chin Soc Corr Pro

2003, Vol. 23

Issue (3): 171-174 DOI:

Research Report

Current Issue | Archive | Adv Search

OBSERVATION OF THE EFFECT OF SHOT BLASTED ON STEAM OXIDATIONRESISTANCE OF TP304H STEEL BOILER TUBING

Xingeng Li;Jiawen He

西安交通大学

Download:

PDF(179KB)
Export: BibTeX | EndNote (RIS)

Abstract TP304H(0Cr19Ni9)steels with and without shot blast ing were tested in a reheater of 1000 t/h boiler for 7552 hours.The results sho w that shot blasting can decrease the thickness of oxide scale,and enhance the c ompactness of oxidation layer.Cr concentrating in the surface can prevent the ou t diffusion of Fe,and decrease the oxidation speed,thus effectively improve the steam oxidation resistance.The effects of shot blasted on oxidation mechanism ar e analyzed,and the oxidation process of the scale phase is also discussed.

Key words: boiler shot blasted steam oxidation refr actory steel corrosion

Received: 26 June 2002

ZTFLH:

TG174.44

Corresponding Authors: Xingeng Li E-mail: lxgeng204@sohu.com

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Xingeng Li
	Jiawen He

Cite this article:

Xingeng Li; Jiawen He. OBSERVATION OF THE EFFECT OF SHOT BLASTED ON STEAM OXIDATIONRESISTANCE OF TP304H STEEL BOILER TUBING. J Chin Soc Corr Pro, 2003, 23(3): 171-174 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I3/171

[1]MinamiYusuke,TooyamaAkira,SekiMikihito,NonakaKazuo,Ko gaKunitoshi.Steam-oxidationresistanceofshotblastedstainlesssteeltubingafter10-yearservice[J].NKKTechnicalRev.,1996(75)1:10
[2]LiXingeng,WangXuegang,HeJiawen.Thepropertyofwaterva poroxidationresistanceofT91steeltreatedbyshotblastedandelectrophoresisdepositedRecoating[J].J.Chin.Soc.Corros.Prot.,2002,22(2):101-104(李辛庚,王学刚,何家文.喷丸与电泳沉积稀土薄膜复合处理提高T91钢抗水蒸气氧化性能的研究[J].中国腐蚀与防护学报,2002,22(2):101-104)
[3]IsaoSaeki,HiroakiTakeda,RyusaburoFuruichi.Effectofchromi umontheformationofchromiumrichoxidefilmonFe-Cralloysatelevatedtemperatures[A].ProceedingsoftheInternationalSym posiumonHigh-TemperatureCorrosionandProtection2000[C].ToshioNarita,HokkaidoJapan.2000,109:114
[4]ShenJia′nian,ZhouLongjian,LiTiefan.EffectofwatervaporonhightemperatureoxidationofFe-Cralloys[J].Chin.J .Mater.Res.,1998,12(2):128-132(沈嘉年,周龙江,李铁藩.水蒸气加速Fe-Cr合金高温氧化的作用[J].材料研究学报,1998,12(2):128-132)
[5]FujiiCT ,MeussnerRA .Themechanismofthehigh-temperatureoxidationofiron-chromiumalloysinwatervapor[J].J.Elec trochem.Soc.,1964,111:1215-1221
[6]NinomiyaS .CorrosionofpowerplantsanditspreventionⅡ[J].TheThermalandNuclearPower,1996,47(5):69-87
[7]MitsutoshiUeda,MakotoNanko,Ken-ichiKawamura,ToshioMarugama.Microstructuredevelopmentofscalesformedintheear lystageofsteamoxidationofFe-Crferriticalloysatelevatedtem perature[A].ProceedingsoftheInternationalSymposiumonHigh-TemperatureCorrosionandProtection2000[C].ToshioNarita,HokkaidoJapan,2000,73:77

[1]	HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	DONG Xucheng, GUAN Fang, XU Liting, DUAN Jizhou, HOU Baorong. Progress on the Corrosion Mechanism of Sulfate-reducing Bacteria in Marine Environment on Metal Materials[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[3]	TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[4]	HAN Yuetong, ZHANG Pengchao, SHI Jiefu, LI Ting, SUN Juncai. Surface Modification of TA1 Bipolar Plate for Proton Exchange Membrane Fuel Cell[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[5]	ZHANG Yuxuan, CHEN Cuiying, LIU Hongwei, LI Weihua. Research Progress on Mildew Induced Corrosion of Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[6]	RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[7]	BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[8]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[10]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[11]	SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[12]	ZHENG Li, WANG Meiting, YU Baoyi. Research Progress of Cold Spraying Coating Technology for Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[13]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[14]	YU Hongfei, SHAO Bo, ZHANG Yue, YANG Yange. Preparation and Properties of Zr-based Conversion Coating on 2A12 Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[15]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed