EFFECT OF PROTON IRRADIATION ON CORROSION BEHAVIOR OF AUSTENITE STAINLESS STEEL AL-6XN IN HIGH TEMPRATURE HIGH PRESSURE WATER

Journal of Chinese Society for Corrosion and protection

2012, Vol. 32

Issue (5): 381-387 DOI:

Current Issue | Archive | Adv Search

EFFECT OF PROTON IRRADIATION ON CORROSION BEHAVIOR OF AUSTENITE STAINLESS STEEL AL-6XN IN HIGH TEMPRATURE HIGH PRESSURE WATER

QIAO Yanxin^1,2, REN Ai¹, LIU Feihua¹, ZHENG Yugui², TANG Rui³, JIN Shuoxue⁴, GUO Liping⁴

1. Suzhou Nuclear Power Research Institute, Suzhou 215004
2. State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016
3. Nuclear Power Institute of China, Chengdu 610041
4. School of Physics and Technology, Wuhan University, Wuhan 430072

Download:

PDF(3081KB)
Export: BibTeX | EndNote (RIS)

Abstract

The corrosion behavior of austenite stainless steel Al-6XN exposed in high temperature high pressure water for different periods was investigated. The results showed that compact oxide scale could form on unirradiation sample in sub- and supercritical water. The oxide scale formed on irradiation sample exhibited obvious dissolution in sub-critical water and oxide scale exfoliated in supercritical water. Proton irradiation could not alter the chemical elements and phase structure of the oxide film. The oxide scale exfoliation model for the protons irradiated austenitic stainless steel exposed in high temperature water was proposed.

Key words: supercritical water coolant reactor irradiation corrosion oxide scale

Received: 25 October 2011

ZTFLH:

TG172.82

Corresponding Authors: QIAO Yanxin E-mail: qiaoyanxin2009@cgnpc.com.cn

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	QIAO Yanxin
	REN Ai
	LIU Feihua
	ZHENG Yugui
	TANG Rui
	JIN Shuoxue
	GUO Liping

Cite this article:

QIAO Yanxin, REN Ai, LIU Feihua, ZHENG Yugui, TANG Rui, JIN Shuoxue, GUO Liping. EFFECT OF PROTON IRRADIATION ON CORROSION BEHAVIOR OF AUSTENITE STAINLESS STEEL AL-6XN IN HIGH TEMPRATURE HIGH PRESSURE WATER. Journal of Chinese Society for Corrosion and protection, 2012, 32(5): 381-387.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2012/V32/I5/381

[1] Allen T R, Sridharan K, Tan L, et al. Materials challenges for generation IV nuclear energy systems [J]. Nucl. Technol., 2008, 162: 342-457

[2] Zhou R S, West E A, Jiao Z J, et al. Irradiation-assisted stress corrosion cracking of austenitic alloys in supercritical water [J]. J. Nucl. Mater., 2009, 395: 11-22

[3] Was G S, Ampornrat P, Gupta G, et al. Corrosion and stress corrosion cracking in supercritical water [J]. J. Nucl. Mater., 2007, 371: 176-201

[4] Yin K J, Qiu S Y, Tang R, et al. Corrosion behavior of ferritic/martensitic steel P92 in supercritical water [J]. J. Super. Flu., 2009, 50: 235-239

[5] Zhu F W, Zhang L F, Tang R, et al. Corrosion behavior of austenitic 304NG stainless steel in supercritical water at 550℃/25MPa [J]. Atom. Energ. Sci. Tech., 2009, 46: 518-522

    (朱发文, 张乐福, 唐睿等. 奥氏体304NG不锈钢在550℃/25 MPa超临界水中的腐蚀行为[J]. 原子能科学技术, 2009, 46: 518-522)

[6] Jiang E, Wen Y, Liu R C, et al. Research on general corrosion property of 304NG stainless steel [J]. Nucl. Power Eng., 2007, 26: 390-392

    (姜峨, 文燕, 刘然超等. 304NG不锈钢均匀腐蚀性能研究[J]. 核动力工程, 2007, 26: 390-392)

[7] Bai X D, Chen X W, Xu J, et al. Corrosion resistance and microstructure of zircaloy-4 subjected to ion irradiation [J]. Nucl. Ins. Meth. Phy. Res. B, 2005, 217: 293-299

[8] Wan Q, Bai X D, Zhang X Y. Impact of high dose krypton ion irradiation on corrosion behavior of laser beam welded zircaloy-4 [J]. Mater. Res. Bull., 2006, 41: 387-395

[9] Teysseyre S, Was G S. Stress corrosion cracking of austenitic alloys in supercritical water [J]. Corrosion, 2006, 62: 1100-1116

[10] Was G S, Teysseyre S, Jiao Z. Corrosion of austenitic alloys in supercritical water [J]. Corrosion, 2006, 62: 989-1005

[11] MacDonald D D. Effect of pressure on the rate of corrosion of metals in high subcritical and supercritical aqueous systems [J]. J. Super. Flu., 2004, 30: 375-382

[12] Yi Y S, Lee B H, Kim S H, et al. Corrosion and corrosion fatigue behaviors of 9Cr steel in a supercritical water condition [J]. Mater. Sci. Eng.,2006, A429: 161-168

[13] Ehlers J, Young D J, Smaardijk E J, et al. Enhanced oxidation of the 9%Cr steel P91 in water vapor containing environments [J]. Corros. Sci., 2006, 48: 3428-3454

[14] Essuman E, Meier G H, Zurek J, et al. The effect of water vapor on selective oxidation of Fe-Cr alloys [J]. Oxid. Met., 2008, 69:143-162

[15] Jin S X, Guo L P, Yang Z, et al. Microstructural evolution in nickel alloy C-276 after Ar⁺ ion irradiation [J]. Nucl. Ins. Meth. Phy. Res. B, 2011, 269: 209-215

[16] Characterization of Neutron-Irradiated 300-Series Stainless Steels to Assess Mechanisms of Irradiation-Assisted Stress Corrosion Cracking: Volume 1: LWR-Irradiated Type 304 and 316SS Heats with Established IASCC Susceptibility [M]. Palo Alto: EPRI, 2001

[17] Panter J, Viguier B, Cloue J M, et al. Influence of oxide films on primary water stress corrosion cracking initiation of alloy 600 [J]. J. Nucl. Mater., 2006, 348: 213-221

[18] Yin K J. Corrosion behavior of candidate material for supercritical water reactor [D]. Beijing: Nuclear Power Institute of China, 2011

     (尹开锯. 超临界水堆(SCWR)候选材料腐蚀行为研究[D]. 北京: 中国核动力研究设计院, 2011)

[1]	HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	DONG Xucheng, GUAN Fang, XU Liting, DUAN Jizhou, HOU Baorong. Progress on the Corrosion Mechanism of Sulfate-reducing Bacteria in Marine Environment on Metal Materials[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[3]	TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[4]	HAN Yuetong, ZHANG Pengchao, SHI Jiefu, LI Ting, SUN Juncai. Surface Modification of TA1 Bipolar Plate for Proton Exchange Membrane Fuel Cell[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[5]	ZHANG Yuxuan, CHEN Cuiying, LIU Hongwei, LI Weihua. Research Progress on Mildew Induced Corrosion of Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[6]	RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[7]	BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[8]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[10]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[11]	SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[12]	ZHENG Li, WANG Meiting, YU Baoyi. Research Progress of Cold Spraying Coating Technology for Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[13]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[14]	YU Hongfei, SHAO Bo, ZHANG Yue, YANG Yange. Preparation and Properties of Zr-based Conversion Coating on 2A12 Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[15]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed