CORROSION PRODUCTION ON ARCHAEOLOGICAL BRONZE SURFACE AND ITS DISTRIBUTION WITH DEPTH

J Chin Soc Corr Pro

2005, Vol. 25

Issue (3): 163-166 DOI:

Research Report

Current Issue | Archive | Adv Search

CORROSION PRODUCTION ON ARCHAEOLOGICAL BRONZE SURFACE AND ITS DISTRIBUTION WITH DEPTH

;;

北京化工大学

Download:

PDF(135KB)
Export: BibTeX | EndNote (RIS)

Abstract The results of cycle voltammetry(CV) experimentation in simulated environment medium and XRD test are that main oxidation process is harmful patina CuCl formation and reduction process is CuCl reduced or deoxidised to pure Cu.The reaction current is so high that severely damages to bronze substrate.When bronze was corroded respectively at several potentials there exist elements Cu,Sn,Cl,O,C,S in corrosion production on bronze surface with SIMS observation.From high to low the relative content of anions is Cl,O,C,S.Cu/Sn value from outside and in corrosion production is always less than that in alloy.The relative content of Cu is basically stead,Sn fluctuates,Cl or O a little falls.

Key words: SIMS archaeological bronze environment corrosion

Received: 24 December 2003

ZTFLH:

TG174

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors

Cite this article:

. CORROSION PRODUCTION ON ARCHAEOLOGICAL BRONZE SURFACE AND ITS DISTRIBUTION WITH DEPTH. J Chin Soc Corr Pro, 2005, 25(3): 163-166 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2005/V25/I3/163

[1]RobbiolaL,BlenginoJ,FiaudC.Morphologyandmechanismoffor mationofnaturalpatinasofarchaeologicalCu-Snalloys[J].Cor ros.Sci.,1998,40(12):2083
[2]ChenYuansheng,XieYulin.Studiesonmuseumenvironmentstan dards[J].SciencesofConservationandArchaeology,2002,14(12):152(陈元生,解玉林.博物馆文物保存环境质量标准研究[J].文物保护与考古科学,2002,14(12),152)
[3]DavidAScott.Anexaminationofthepatinaandcorrosionmorphol ogyofsomeromanbronzes[J].J.theAmericanInstituteforCon servation,1994,33(1):1
[4]BenninghovenA,RudenauderFG,WernerHW.SecondaryIonMassSpectrometry[M].JohnWiley&Sons,1987
[5]ChaLZ,LuJH,ChenCY.ModernAnalyzingTechnology[M].Beijing:QinghuaUniversityPublishingCompany,1995(查良镇,陆家和,陈长彦.现代分析技术[M].北京:清华大学出版社,1995)
[6]ChaLZ,GuiD,ZhuYJ.Latestprogressinsecondaryionmass spectroscopy[J].VacuumScienceandTechnology(China),2001,21(2):129(查良镇,桂东,朱怡静.二次离子质谱的新进展[J].真空科学与技术,2001,21(2):129)
[7]HallettK,ThickettD,McPhailDS.ApplicationofSIMStosilver tarnishattheBritishmuseum[J].AppliedSurfaceScience,2003,203-204:789
[8]GasparP,HubbardC,McPhailDS.Topographicalassessmentand comparisonofconservationcleaningtreatments[A].Acceptedfor theProceedingsofLacona(lasersinconservationofartworks)IV[C].Lacona,2001
[9]SokhanM,GasparP,McPhailDS.Initialresultsonlasercleaningat theVictoriaandAlbertmuseum,naturalhistorymuseumandtate gallery[A].AcceptedfortheProceedingsofLacona(lasersincon servationofartworks)IV[C].Lacona,2001
[10]ConstantinidesI,AdriaensA,AdamsF.Surfacecharacterizationof artificialcorrosionlayersoncopperalloyreferencematerials[J].Ap pliedSurfaceScience,2002,90-101:189
[11]XuChunchun,WangJulin.Investigationofthechemicalandelec trochemicalbehaviourofmasstransferatanarchaeologicalbronze/soilinterface[J].Anti-CorrosionMethodsandMaterials.2003,50(5):326
[12]LiangHD,YuCH,ZhouQ.SIMSstudiesonsinglegraininfur nacedustofsteelfactory[J].MiningSafetyandEnvironmentPro tection,2001,28(3):4(梁汉东,于春海,周强.钢铁厂平炉尘单颗粒物的二次离子质谱研究[J].矿业安全与环保.2001,28(3):4)
[13]ZhaoJ,LuHQ,LiXY.SIMSanalysisonTe-Cd-Hgbodyma terialinjectedbyAsion[J].J.InfraredMillim.Waves,2000,19(4):281(赵军,陆慧庆,李向阳.砷离子注入体材料碲镉汞的二次离子质谱分析[J].红外与毫米波学报,2000,19(4):281)

[1]	HUANG Peng, GAO Rongjie, LIU Wenbin, YIN Xubao. Fabrication of Superamphiphobic Surface for Nickel-plate on Pipeline Steel by Salt Solution Etching and Its Anti-corrosion Properties[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	DONG Xucheng, GUAN Fang, XU Liting, DUAN Jizhou, HOU Baorong. Progress on the Corrosion Mechanism of Sulfate-reducing Bacteria in Marine Environment on Metal Materials[J]. 中国腐蚀与防护学报, 2021, 41(1): 1-12.
[3]	TANG Rongmao, ZHU Yichen, LIU Guangming, LIU Yongqiang, LIU Xin, PEI Feng. Gray Correlative Degree Analysis of Q235 Steel/conductive Concrete Corrosion in Three Typical Soil Environments[J]. 中国腐蚀与防护学报, 2021, 41(1): 110-116.
[4]	HAN Yuetong, ZHANG Pengchao, SHI Jiefu, LI Ting, SUN Juncai. Surface Modification of TA1 Bipolar Plate for Proton Exchange Membrane Fuel Cell[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[5]	ZHANG Yuxuan, CHEN Cuiying, LIU Hongwei, LI Weihua. Research Progress on Mildew Induced Corrosion of Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[6]	RAN Dou, MENG Huimin, LIU Xing, LI Quande, GONG Xiufang, NI Rong, JIANG Ying, GONG Xianlong, DAI Jun, LONG Bin. Effect of pH on Corrosion Behavior of 14Cr12Ni3WMoV Stainless Steel in Chlorine-containing Solutions[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[7]	BAI Yunlong, SHEN Guoliang, QIN Qingyu, WEI Boxin, YU Changkun, XU Jin, SUN Cheng. Effect of Thiourea Imidazoline Quaternary Ammonium Salt Corrosion Inhibitor on Corrosion of X80 Pipeline Steel[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[8]	ZUO Yong, CAO Mingpeng, SHEN Miao, YANG Xinmei. Effect of Mg on Corrosion of 316H Stainless Steel in Molten Salts MgCl₂-NaCl-KCl[J]. 中国腐蚀与防护学报, 2021, 41(1): 80-86.
[9]	WANG Yating, WANG Kexu, GAO Pengxiang, LIU Ran, ZHAO Dishun, ZHAI Jianhua, QU Guanwei. Inhibition for Zn Corrosion by Starch Grafted Copolymer[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[10]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[11]	SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[12]	LIU Yang, WU Jinyi, YAN Xiaoyu, CHAI Ke. *Effect of Bacillus flexus* on Degradation of Polyurethane Varnish Coating in Marine Environment**[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[13]	ZHENG Li, WANG Meiting, YU Baoyi. Research Progress of Cold Spraying Coating Technology for Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[14]	WEI Zheng, MA Baoji, LI Long, LIU Xiaofeng, LI Hui. Effect of Ultrasonic Rolling Pretreatment on Corrosion Resistance of Micro-arc Oxidation Coating of Mg-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[15]	YU Hongfei, SHAO Bo, ZHANG Yue, YANG Yange. Preparation and Properties of Zr-based Conversion Coating on 2A12 Al-alloy[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed