低碳钢在富含H2S乙醇胺溶液中的腐蚀及缓蚀剂抑制

周欣;杨怀玉;蔡铎昌;沈长斌;陶晓杰;韩冬云

中科院金属所（南区）

THE CORROSION AND INHIBITION OF MILD STEEL IN MONOETHANOLAMINE SOLUTION ABOUNDED WITH H2S

Xin Zhou;Huaiyu Yang;Duochang Cai;Changbin Shen;Xiaojie Tao;Dongyun Han

中科院金属所（南区）

全文: PDF(154 KB)

摘要: 利用失重、腐蚀电化学方法和表面分析技术研究了碳钢在富含H2S的乙醇胺（MEA）溶液中的腐蚀行为，以及添加缓蚀剂后对其电化学行为的影响。讲座讨论了IMC-C5缓蚀剂对该体系的缓蚀作用机理。结果表明，脱硫系统中吸收了硫化氢的乙醇胺溶液对碳钢的腐蚀十分严重，IMC-C5缓蚀剂能有效控制碳钢在该体系中的腐蚀，其缓蚀作用主要来自于吸附缓蚀剂分子对腐蚀阳极过程的抑制，为阳极吸附型缓蚀剂。

关键词 ：乙醇胺, 缓蚀剂, 缓蚀机理, 低碳钢

Abstract：The corrosion behavior and the effect of the corrosion inhibitor on those behavor of carbon steel in MEA solution abounded with H2S was investigated by static weight loss test, electrochemical method and surface analytical techniques.The inhibitive mechanisms of IMC-C5 inhibitor under the circumstance were discussed.The results show that mild steel was severely damaged in MEA solution abounded with H2S and IMC-C5 inhibitor has an excellent inhibitive performance mainl from the strong retardation to the anodic process.The corrosion inhibitor is an anodic adsorption type inhibitor.

Key words： monoethanolamine(MEA) corrosion inhibitor mechanism mild steel

收稿日期: 2003-09-19

ZTFLH:

TG174.42

通讯作者: 周欣

Corresponding author: Xin Zhou

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	周欣
	杨怀玉
	蔡铎昌
	沈长斌
	陶晓杰
	韩冬云
44.8K

引用本文:

周欣; 杨怀玉; 蔡铎昌; 沈长斌; 陶晓杰; 韩冬云 . 低碳钢在富含H2S乙醇胺溶液中的腐蚀及缓蚀剂抑制[J]. 中国腐蚀与防护学报, 2005, 25(2): 79-83 .
Xin Zhou, Huaiyu Yang, Duochang Cai, Changbin Shen, Xiaojie Tao, Dongyun Han. THE CORROSION AND INHIBITION OF MILD STEEL IN MONOETHANOLAMINE SOLUTION ABOUNDED WITH H2S. J Chin Soc Corr Pro, 2005, 25(2): 79-83 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I2/79

[1]HanXP .Techniquefordetectingcorrosionandcoatingflowofburiedpipelines[J].NaturalGasIndustry,2001,21(1):108(韩兴平.埋地管线腐蚀、涂层缺陷检测技术[J].天然气工业,2001,21(1):108)
[2]SongSZ .InvestigativeMethodsofCorrosiveElectrochemistry[M ].Beijing:ChemistryIndustryPress,1988:167(宋诗哲.腐蚀电化学研究方法[M ].北京:化学工业出版社,1988:167)
[3]SongSZ ,SongXP ,etal.Electrochemicalmeasurementsofdefec tivecoatingonburiedsteelsubstrates[J].Electrochemistry,1999,5(2):162(宋诗哲,宋小平等.土壤中钢铁表面防护层缺陷的电化学检测[J].电化学,1999,5(2):162)
[4]GanF ,SunZW ,SabdeG ,ChinDT .Cathodicprotectiontomiti gateexternalcorrosionofundergroundsteelpipebeneathdisbondedcoating[J].Corrosion,1994,50(2):804
[5]ZhuRZ ,etal.CorrosionofMetals[M ].Beijing:MetallurgicalIn dustryPress,1993,103-107(朱日彰等.金属腐蚀学[M ].北京:冶金工业出版社,1993,103-107)
[6]BarloTJ,FesslerRR .Interpretationoftruepipe to soilpotentialsoncoatedpipelineswithholidays[J].Corrosion,1983,292:313
[7]MurrJN ,MoranPJ .AnEISstudyofthecorrosionbehaviorofpolyethylenecoatingholidaysinnaturalsoilconditions[J].Corro sion,1989,45(11):885[1]SongHJ,GaoXD ,DuJ.CorrosionofdesulfurizationsystemofRFCCgasseparationandcontrol[J].PetrochemicalCorros.Prot.,2002,19(1):10-12(宋洪建,高东进,杜进.RFCC气体分离脱硫系统的腐蚀与控制[J].石油化工腐蚀与防护,2002,19(1):10-12)
[2]WuXC ,ShiLQ ,QinLM ,LiuYQ .Corrosionofregenerationsys temofgasdesulfurizationandcountermeasures[J].PetrochemicalCorros.Prot.,2001,18(3):18-20(伍习初,史烈庆,秦利梅,刘元倩.气体脱硫系统腐蚀原因及对策[J].石油化工腐蚀与防护,2001,18(3):18-20)
[3]LiuHB ,MoSM .Corrosionofpipingwethydrogensulfideenviro mentandprotection[J].PetrochemicalCorros.Prot.,2001,18(5):30-33(刘海滨,莫少明.湿硫化氢环境下的管线的腐蚀与防护[J].石油化工腐蚀与防护,2001,18(5):30-33)
[4]JiXJ.Analysisofcrackingofregenerationtowerwallandcounter measures[J].PetrochemicalCorros.Prot.,1999,16(3):22-24(姬晓军.再生塔塔壁开裂原因分析及对策[J].石油化工腐蚀与防护,1999,16(3):22-24)
[5]VazquezRC ,RiosG .Aggressivecorrosionof316ssinanaminicu nit:causeandcures[A].Corrosion/2000[C].NACE ,696
[6]FuJS .Analysisofcorrosionofbottomreboilerofregenerationtow erof gas pesulfurizationunit[J].PetrochemicalCorros.Prot.,1999,16(1):6-7(傅俊松.气体脱硫再生塔底重沸器腐蚀分析[J].石油化工腐蚀与防护,1999,16(1):6-7)
[7]JayaramanA ,SaxenaRC .Corrosionanditscontrolinpetroleumre fineries—areview[J].CorrosionPreventionandControl,1995,12:123
[8]FengXW ,GuoXP .StudyonthecorrelationbetweenCO2 absorp tionmechanismsandcorrosionbehaviorofalkanolaminesolutions[J].J.Chin.Soc.Corros.Prot.,2003,23(2):79-83(冯绪文,郭兴蓬.烷醇胺水溶液的CO2吸收机理及其腐蚀行为的相关性研究[J].中国腐蚀与防护学报,2003,23(2):79～83)
[9]CummingsAL ,VeatchFV ,KellerAE .CorrosionandcorrosioncontrolmethodsinaminesystemscontainingH2S [A].Corrosion/97[C].NACE ,696
[10]CaoCN .CorrosionElectrochemistry[M ].Beijing:ChemicalIn dustryPress,1994,128(曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994,128)

[1]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[2]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[3]	邵明鲁, 刘德新, 朱彤宇, 廖碧朝. 乌洛托品季铵盐缓蚀剂的合成与复配研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 244-250.
[4]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[5]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[6]	吕祥鸿,张晔,闫亚丽,侯娟,李健,王晨. 两种新型曼尼希碱缓蚀剂的性能及吸附行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 31-37.
[7]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[8]	刘建国,高歌,徐亚洲,李自力,季菀然. 咪唑啉类衍生物缓蚀性能研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 523-532.
[9]	李亚琼,马景灵,王广欣,朱宇杰,宋永发,张景丽. NaPO₃与SDBS缓蚀剂对AZ31镁合金空气电池在NaCl电解液中放电性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(6): 587-593.
[10]	孔佩佩, 陈娜丽, 白德忠, 王跃毅, 卢勇, 冯辉霞. 壳聚糖及其衍生物的制备与缓蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2018, 38(5): 409-414.
[11]	马景灵, 通帅, 任凤章, 王广欣, 李亚琼, 文九巴. L-半胱氨酸/ZnO缓蚀剂对3102铝合金在碱性溶液中电化学性能的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 351-357.
[12]	彭晚军, 丁纪恒, 陈浩, 余海斌. 生物基缓蚀剂糠醇缩水甘油醚的缓蚀性能及机理[J]. 中国腐蚀与防护学报, 2018, 38(3): 303-308.
[13]	钱备, 刘成宝, 宋祖伟, 任俊锋. 纳米容器改性环氧涂层对Q235碳钢的防腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 133-139.
[14]	周勇, 左禹, 闫福安. 缓蚀性组分对金属小孔腐蚀的缓蚀作用与机制[J]. 中国腐蚀与防护学报, 2017, 37(6): 487-494.
[15]	陈振宁,陈日辉,潘金杰,滕艳娜,雍兴跃. L921A钢在3.5%NaCl溶液中的有机/无机复配缓蚀剂研究[J]. 中国腐蚀与防护学报, 2017, 37(5): 473-478.

Viewed

Full text

Abstract

Cited

Shared

Discussed