大块涂层缺陷对碳钢腐蚀特性及阴极保护效果的影响

中国腐蚀与防护学报

2005, Vol. 25

Issue (2): 74-78

研究报告

本期目录 | 过刊浏览

大块涂层缺陷对碳钢腐蚀特性及阴极保护效果的影响

宋义全;杜翠薇;李晓刚;武俊伟;阎永贵

北科大腐蚀与防护中心北京市腐蚀、磨蚀与表面工程重点实验室

THE INFLUENCE OF HUNK OF COATING DEFECT ON CORROSIVE CHARACTERISTIC OF CARBON STEELS AND EFFECTIVENESS OF CATHODIC PROTECTION

Yiquan Song;Cuiwei Du;Xiaogang Li;Junwei Wu;Yonggui Yan

北科大腐蚀与防护中心北京市腐蚀、磨蚀与表面工程重点实验室

全文: PDF(180 KB)

摘要: 采用了环氧煤沥青作为涂层材料，研究了大块涂层缺陷对碳钢腐蚀特性及阴极保护效果的影响，测定了具有面积比例为4。91%大块涂层缺陷的Q235钢于3.5%NaCl水溶液中的交流阻抗谱.结果表明,随着浸泡时间的延长,在自然腐蚀电位下,存在剥离涂层缺陷时碳钢的腐蚀程度高于破损涂层缺陷时碳钢的腐蚀程度;在阴极极化条件下具有剥离涂层缺陷的碳钢阴极保护效果随时间延长逐渐降低直至最后消失,而具有破损涂层缺陷时阴极保护效果随时间延长优于剥离涂层缺陷;电解质溶液向涂层内部的渗透以及涂层缺陷与钢基本间的缝隙腐蚀是导致具有大块涂层缺陷碳钢腐蚀的主要原因.

关键词 ：大块涂层缺陷, 电化学阻抗谱, 阴极保护, 缝隙

Abstract：Taking epoxy coal tar as material of coating,the influene of hunk of coating defect on corrosive characteristic of carbon steels and effectiveness of cathodic protection has been investigated.EIS of Q235 steel in 3.5% NaCl water solution with hunk of coating defect was determined.Experiments have shown that,on free corrosion potential,the corrosion of carbon steels with disbonding defect of coating os heavier than that of breaking defect of coating with times.On cathodic polarization poteneial,the effectiveness of cathodic protection of carbon steels with disbonding defect of coating gradually weaens with times and loses eventually.The effection of cathodic protection of carbon steels with breaking defect of coating is better than that of carbon steels with disbonding defect of coating.Penetration of electrolyte solution into coating and the creice corrosion between coating defect and surface of steel matrix is main reason of corrosion on carbon steels with hunk of coating defects.

Key words： hunk of coating defect EIS cathodic protection crevice corrosion

收稿日期: 2003-09-12

ZTFLH:

TG171

通讯作者: 宋义全 E-mail: syqrylss@163.com

Corresponding author: Yiquan Song E-mail: syqrylss@163.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	宋义全
	杜翠薇
	李晓刚
	武俊伟
	阎永贵
44.8K

引用本文:

宋义全; 杜翠薇; 李晓刚; 武俊伟; 阎永贵 . 大块涂层缺陷对碳钢腐蚀特性及阴极保护效果的影响[J]. 中国腐蚀与防护学报, 2005, 25(2): 74-78 .
Yiquan Song, Cuiwei Du, Xiaogang Li, Junwei Wu, Yonggui Yan. THE INFLUENCE OF HUNK OF COATING DEFECT ON CORROSIVE CHARACTERISTIC OF CARBON STEELS AND EFFECTIVENESS OF CATHODIC PROTECTION. J Chin Soc Corr Pro, 2005, 25(2): 74-78 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2005/V25/I2/74

[1]HanXP .Techniquefordetectingcorrosionandcoatingflowofburiedpipelines[J].NaturalGasIndustry,2001,21(1):108(韩兴平.埋地管线腐蚀、涂层缺陷检测技术[J].天然气工业,2001,21(1):108)
[2]SongSZ .InvestigativeMethodsofCorrosiveElectrochemistry[M ].Beijing:ChemistryIndustryPress,1988:167(宋诗哲.腐蚀电化学研究方法[M ].北京:化学工业出版社,1988:167)
[3]SongSZ ,SongXP ,etal.Electrochemicalmeasurementsofdefec tivecoatingonburiedsteelsubstrates[J].Electrochemistry,1999,5(2):162(宋诗哲,宋小平等.土壤中钢铁表面防护层缺陷的电化学检测[J].电化学,1999,5(2):162)
[4]GanF ,SunZW ,SabdeG ,ChinDT .Cathodicprotectiontomiti gateexternalcorrosionofundergroundsteelpipebeneathdisbondedcoating[J].Corrosion,1994,50(2):804
[5]ZhuRZ ,etal.CorrosionofMetals[M ].Beijing:MetallurgicalIn dustryPress,1993,103-107(朱日彰等.金属腐蚀学[M ].北京:冶金工业出版社,1993,103-107)
[6]BarloTJ,FesslerRR .Interpretationoftruepipe to soilpotentialsoncoatedpipelineswithholidays[J].Corrosion,1983,292:313
[7]MurrJN ,MoranPJ .AnEISstudyofthecorrosionbehaviorofpolyethylenecoatingholidaysinnaturalsoilconditions[J].Corro sion,1989,45(11):885

[1]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[2]	赵柏杰, 范益, 李镇镇, 张博威, 程学群. 不同类型接触面对316L不锈钢缝隙腐蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 332-341.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	梁毅, 杜艳霞. 交流干扰和阴极保护协同作用下的腐蚀评判标准与机理研究进展[J]. 中国腐蚀与防护学报, 2020, 40(3): 215-222.
[5]	解璇, 刘莉, 王福会. TiO₂的制备及表面修饰工艺对其光电化学阴极保护性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(2): 123-130.
[6]	赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[7]	王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[8]	达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[9]	王贵容,邵亚薇,王艳秋,孟国哲,刘斌. 阴极保护电位对破损环氧涂层阴极剥离的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 235-244.
[10]	达波,余红发,麻海燕,吴彰钰. 阻锈剂的掺入方式对全珊瑚海水混凝土中钢筋锈蚀的影响[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.
[11]	王长罡,魏洁,魏欣,穆鑫,薛芳,董俊华,柯伟,李国平. 几种超级不锈钢在模拟烟气脱硫环境中的缝隙腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 43-50.
[12]	廖彤,马峥,李蕾蕾,马秀敏,王秀通,侯保荣. Fe₂O₃/TiO₂纳米复合材料对304不锈钢的光生阴极保护性能[J]. 中国腐蚀与防护学报, 2019, 39(1): 36-42.
[13]	邓培昌, 刘泉兵, 李子运, 王贵, 胡杰珍, 王勰. X70管线钢在热带海水-海泥跃变区的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(5): 415-423.
[14]	邓三喜, 闫小宇, 柴柯, 吴进怡, 史洪微. 假单胞菌对聚硅氧烷树脂清漆涂层分解及防腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(4): 326-332.
[15]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.

Viewed

Full text

Abstract

Cited

Shared

Discussed