盐雾环境下高强度铝合金的点蚀行为

中国腐蚀与防护学报

2010, Vol. 30

Issue (3): 197-202

研究报告

本期目录 | 过刊浏览

盐雾环境下高强度铝合金的点蚀行为

崔继红, 蔡建平,贾成厂

1. 北京科技大学材料科学与工程学院　北京 100083
2. 北京航空材料研究院　北京 100095

PITTING CORROSION OF HIGH STRENGTH ALUMINUM ALLOYS IN SALT SPRAY TEST

CUI Jihong^1,2, CAI Jianping², JIA Chengchang¹

1. School of Materials Science and Engineering, University of Science &Technology Beijing, Beijing 100083
2. Beijing Institute of Aeronautical Materials, Beijing 100095

全文: PDF(2289 KB)

摘要:

采用断面金相法和局部交流阻抗技术对高强度航空铝合金7B04在连续盐雾腐蚀试验下的点蚀行为进行分析。试验结果表明，合金表面点蚀呈现腐蚀速度快速憎加，到腐蚀中期减缓，后期又急剧增加的趋势；但最大点蚀深度始终呈线性增长, 点蚀坑的形成机理主要有：阴极相粒子周围基体的溶解、铝本身的去合金化及腐蚀残留物Cu粒子的二次点蚀，其中AlCu和AlCuMg第二相粒子阴极相是其点蚀形成的诱因。局部交流阻抗技术可以提供微小区域阻抗变化的有效信息，适合用于研究点蚀发展的溶解动力学。

关键词 ：点蚀, 铝合金, 盐雾试验, 局部交流阻抗技术, 最大点蚀深度

Abstract：

Salt fog spray test is used to accelerate the corrosion of 7B04 aluminum alloy. The pitting corrosion of this alloy was investigated by using metallographic method and localized electrochemical impedance spectroscopy (LEIS). It was concluded that the corrosion rate of the alloy increased sharply, but was retarded at the middle stage of exposure. The maximum depth of the pitting was linearly growing in the whole process. The pitting mechanism was mainly attributed to the dissolving the surrounding matrix of cathode-phase particles, dissolving aluminum itself or secondary pitting of Cu particles which is the corrosion residues. While the cathode phase of AlCu or AlCuMg second-phase particles was the main initiation cause. Localized electrochemical impedance spectroscopy (LEIS) which is suitable to follow changes in the dissolution kinetics during pit growth, could provide valuable information on the changes of the impedance on a small area.

Key words： pitting corrosion aluminum alloy salt spray test localized electrochemical impedance spectroscopy(LEIS) maximum pit depth

收稿日期: 2009-02-20

ZTFLH:

TG172.3

基金资助:

国防科工委技术基础科研项目（H052006A004和H052006A006）资助

通讯作者: 蔡建平 E-mail: jpcai2001@yahoo.com.cn

Corresponding author: CAI Jianping E-mail: jpcai2001@yahoo.com.cn

作者简介: 崔继红，女，1983年生，硕士研究生，研究方向为金属及涂层的加速腐蚀试验

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	崔继红
44.8K

引用本文:

崔继红, 蔡建平,贾成厂. 盐雾环境下高强度铝合金的点蚀行为[J]. 中国腐蚀与防护学报, 2010, 30(3): 197-202.
CUI Ji-Hong. PITTING CORROSION OF HIGH STRENGTH ALUMINUM ALLOYS IN SALT SPRAY TEST. J Chin Soc Corr Pro, 2010, 30(3): 197-202.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2010/V30/I3/197

[1]	Li J F, Zheng Z Q, Ren W D. Mechanism of action of second-phase on the localized corrosion of aluminum alloys [J]. J. Mater.,2005, 19(2): 81-83
	(李劲风，郑子 ,任文达．第二相在铝合金局部腐蚀中的作用机制 [J]．材料导报，2005，19(2)：81-83)
[2]	Hu L H, Du N, Wang M F, et al. Monitoring the initial pitting behaviors of 1Cr18Ni9Ti stainless steel by electrochemical noise and electrochemical impedance spectroscopy [J]. J. Chin. Soc. Corros.Proc., 2007, 27(4): 233-237
	胡丽华，杜楠，王梅丰等. 电化学噪声和电化学阻抗谱监测1Cr18Ni9Ti不锈钢的初期点蚀行为 [J]. 中国腐蚀与防护学报, 2007, 27(4):233-237 浏览
[3]	Zhang Z, Zhang J Q, Wang J M. Pitting corrosion of Al2024-T3 in sodium chloride solution [J]. Trans. Nonferrous Met. Soc. China, 2001,11(5): 748-753
[4]	Campestrini P, Van Westing E P M, De Wit J H W. Influence of surface preparation on performance of chromate conversion coatings on Al clad 2024 aluminum alloy-Part II: EIS investigation [J]. Electrochem. Acta, 2001, 46(17):2631-2647
[5]	Shi Y Y, Zhang Z, Su J X, et al. EIS study on 2024-T3 aluminum alloy corrosion in simulated acid rain under cyclic wet-dry conditions [J]. Mater. Corros, 2005, 56(10):701-706
[6]	Zheludkevich M L, Yasakau K A, Poznyak S K, et al. Triazole and thiazole derivatives as corrosion inhibitors for AA2024 aluminum alloy [J]. Corros. Sci, 2005, 47(12):3368-3383
[7]	Moutarlier V, Gigandet M P, Normand B, et al. EIS characterization of anodic films formed on 2024 aluminum alloy in sulfuric acid containing molybdate or permanganate species [J]. Corros. Sci, 2005, 47(4):937-951
[8]	Annergren I, Zou F. Application of localized electrochemical techniques to study kinetics of initiation and propagation during pit growth [J]. Electrochim. Acta, 1999, 44:4383-4393
[11]	Zhang N, Sun Z H, Zhang Q, et al. Application of local electrochemical impedance spectroscopy(LEIS) on accessing the environmental failure of organic coatings [J]. Equip. Environ. Eng., 2007, 4(1): 75-78
	(章妮，孙志华，张琦等．局部阻抗测试技术在评定有机涂层环境失效中的应用 [J]．装备环境与工程，2007，4(1)：75-78)
[12]	Wu L, Sun Q, Guo Y N. Accelerated corrosion tests of high strength 7075 aluminum alloy in salt water spray [J]. J. Mech. Strength, 2006, 28(1): 138-140
	(毋玲，孙秦，郭英男．高强度铝合金盐雾加速腐蚀试验研究 [J]. 机械强度，2006，28(1)：138-140)
[13]	Buchheit R G, Grant R P, Hlava P F. Local dissolution phenomena associated with S phase(Al₂Cu Mg) particles in aluminum alloy 2024-T3 [J]. J. Electrochem. Soc, 1997, 144(8):2621-2628
[14]	Wang Y W, Wang Y F, Huang X P, et al. A simplified maximum pit depth model of mild and low alloy steels in marine immersion environments [J]. J. Ship Mech., 2008, 12(3): 403-417
[15]	Zhu D Q, Van Ooij W. Corrosion protection of AA2024-T3 by bis-[3-(tri ethoxysilyl)propyl] tetra sulfide in neutral sodium chloride solutionPart 1: corrosion of AA2024-T3 [J]. Corros. Sci, 2003, 45:2163-2175

[1]	张雨轩, 陈翠颖, 刘宏伟, 李伟华. 铝合金霉菌腐蚀研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 13-21.
[2]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[3]	于宏飞, 邵博, 张悦, 杨延格. 2A12铝合金锆基转化膜的制备及性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 101-109.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[6]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[7]	张欣, 杨光恒, 王泽华, 曹静, 邵佳, 周泽华. 冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[8]	贺三, 孙银娟, 张志浩, 成杰, 邱云鹏, 高超洋. 20#钢在含饱和CO₂的离子液体醇胺溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 309-316.
[9]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[10]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[11]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[12]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[13]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[14]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[15]	苏小红,胡会娥,孔小东. W颗粒/Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5基非晶复合材料在3%NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 70-74.

Viewed

Full text

Abstract

Cited

Shared

Discussed