低碳钢在H<sub>2</sub>S溶液中的腐蚀行为研究

中国腐蚀与防护学报

2010, Vol. 30

Issue (6): 465-468

研究报告

本期目录 | 过刊浏览

低碳钢在H₂S溶液中的腐蚀行为研究

张弦¹,杨淼¹,汪新¹,林安¹,甘复兴^1,2

1. 武汉大学资源与环境科学学院环境工程系武汉 430072
2. 中国科学院金属研究所金属腐蚀与防护国家重点实验室沈阳 110016

CORROSION BEHAVIOR OF MILD STEEL UNDER CONDITION OF H₂S SOLUTION

ZHANG Xian¹, YANG Miao¹, WANG Xin¹, LIN An¹, GAN Fuxing^1,2

1. Department of Environmental Engineering, School of Resource and Environmental Science, Wuhan University, Wuhan 430072
2. State Key Laboratory for Corrosion and Protection, Institute of Metal Research，Chinese Academy of Sciences, Shenyang 110016

全文: PDF(577 KB)

摘要: 通过腐蚀形貌分析、腐蚀产物分析和电化学测试多种分析测试手段，研究了干湿交替循环下低碳钢在H₂S溶液中的腐蚀行为。综合分析结果表明腐蚀初期产物较少，腐蚀速率与循环次数成正比；腐蚀后期，腐蚀产物较多，形成一层保护膜，阻碍腐蚀过程的进行，腐蚀速率与循环次数成反比。FeS的生成可能是腐蚀速率出现转折的一个因素。

关键词 ： H₂S, 低碳钢, 干湿交替循环, 腐蚀行为

Abstract：Corrosion behavior of mild steel in the condition of H₂S in wet/dry cycles was studied by corrosion analysis, corrosion product and morphology analysis and electrochemical measurement. The results show that the initial corrosion products are less, and corrosion rate is proportional to cycle times; with accumulation of more corrosion product, which possibly acts as corrosion barrier, corrosion rate is inversely proportional to cycle times based on comprehensive analysis. The formation of FeS may be a factor responsible for a turning point of corrosion rate.

Key words： H₂S mild steel wet/dry alternate cycles corrosion behavior

收稿日期: 2009-10-19

ZTFLH:

TQ153.7

通讯作者: 张弦 E-mail: jeffzx1214@163.com

作者简介: 张弦，女,1986年生,研究生,研究方向为电化学及材料保护

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张弦
44.8K

引用本文:

张弦,杨淼,汪新,林安,甘复兴. 低碳钢在H₂S溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2010, 30(6): 465-468.
ZHANG Xian. CORROSION BEHAVIOR OF MILD STEEL UNDER CONDITION OF H₂S SOLUTION. J Chin Soc Corr Pro, 2010, 30(6): 465-468.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2010/V30/I6/465

[1] Huang X, Cheng J, Yao Y G, et al. Effect of H₂S on corrosion behavior of low carbon steel in coke oven gas [J]. Iron Steel Vanadium Titanium, 1998, 19(4): 14-20

    (黄旭，陈杰，姚永国等. H₂S对低碳钢在焦炉煤气中腐蚀行为的影响 [J]. 钢铁钒钛, 1998, 19(4): 14-20)

[2] Gu H B, Xi A K, Qu J F, et al. Corrosion mechanism of the A3 steel gas tube [J]. J. Shanxi Univ. (Nat. Sci. Ed.), 1992, 15(l): 41-47

    (顾宏邦，郗安康，曲济方等. A3钢输煤气管道腐蚀穿孔机理的探讨 [J]. 山西大学学报(自然科学版), 1992, 15(l): 41-47)

[3] Medvedeva M L, Guryanov V V. On the corrosion state of plants for purifying natural gas from acid components [J]. Prot. Met.,2002, 38(3): 284-288

[4] Ma H Y, Cheng X L, Li G Q, et al. The influence of hydrogen sulfide on corrosion of iron under different conditions [J]. Corros.Sci., 2000, 42: 1669

[5] Polyakov S G. Specific features of the electrochemical behavior of steels under corrosion cracking of pipelines [J]. Mater.Sci., 1999, 35(5): 650-656

[6] Nishimura T, Katayama H, Noda K, et al. Electrochemical behavior of rust formed on carbon steel in a wet /dry environment condition chloride ions [J]. Corrosion, 2000,56: 935-941

[7] Dong J, Dong J H, Han E H, et al. Corrosion behavior of rusted mild steel under means of wet/dry alternate conditions [J]. Corros.Sci. Prot. Technol., 2006, 18(6): 414-417

    (董杰，董俊华，韩恩厚等.低碳钢带锈电极的腐蚀行为 [J]. 腐蚀科学与防护技术,2006, 18(6): 414-417)

[8] Li M, Li X G, Chen H. Review on corrosion behavior and mechanism of metal in wet H₂S [J]. Corros. Sci. Prot. Technol., 2005, 17(2): 107-111

    (李明，李晓刚，陈华. 在湿H₂S环境中金属腐蚀行为和机理研究概述 [J]. 腐蚀科学与防护技术, 2005, 17(2): 107-111)

[9] Li J, Li M, Sun Z. Development of an artificial climatic complex accelerated corrosion tester and investigation of complex accelerated corrosion test methods [J].Corrosion, 1999, 55: 498

[10] Liu Y H. Electrochemical Measurement Technology [M]. Beijing: Beihang University Press, 1987: 357-395

     (刘永辉. 电化学测试技术 [M]. 北京：北京航空学院出版社, 1987: 357-395)

[1]	艾芳芳, 陈义庆, 钟彬, 李琳, 高鹏, 伞宏宇, 苏显栋. T95油井管在酸性油气田环境中的应力腐蚀开裂行为及机制[J]. 中国腐蚀与防护学报, 2020, 40(5): 469-473.
[2]	李琳, 陈义庆, 高鹏, 艾芳芳, 钟彬, 伞宏宇, 杨颖. 除冰盐环境下桥梁钢的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[3]	张欣, 杨光恒, 王泽华, 曹静, 邵佳, 周泽华. 冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[4]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[5]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[6]	王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[7]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[8]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[9]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[10]	苏小红,胡会娥,孔小东. W颗粒/Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5基非晶复合材料在3%NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 70-74.
[11]	王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[12]	郭铁明,张延文,秦俊山,宋志涛,董建军,杨新龙,南雪丽. 桥梁钢Q345q在3种模拟大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 319-330.
[13]	黄博博,刘平,刘新宽,梅品修,陈小红. 新型HSn70-1铜网衣两年期海水腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
[14]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[15]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.

Viewed

Full text

Abstract

Cited

Shared

Discussed