AZ31B镁合金表面电镀铝锰合金的耐蚀性

张吉阜,张伟,杜克勤,严川伟,王福会

中国科学院金属研究所金属腐蚀与防护国家重点实验室沈阳 110016

IMPROVED CORROSION RESISTANCE OF AZ31B MAGNESIUM ALLOY BY ELECTROPLATING OF Al-Mn ALLOY

ZHANG Jifu, ZHANG Wei, DU Keqin, YAN Chuanwei, WANG Fuhui

State Key Laboratory for Corrosion and Protection, Institute of Metal Research, Chinese Academy of Sciences, Shenyang 110016

全文: PDF(2323 KB)

摘要:

在镁合金AZ31B表面通过预镀锌处理后采用无机熔盐电沉积铝锰合金。使用SEM、EDX和XRD分析镀层的表面形貌、成分和组织，采用动电位极化曲线及表面显微硬度测量考察了镀层对镁合金耐蚀耐磨性的影响。结果表明，熔盐成分、电流密度和熔体温度等典型工艺参数对铝锰合金镀层的形貌、成分和组织都具有重要的影响，进而影响了镀层的耐蚀性。镁合金电镀铝锰合金后，腐蚀电位有很大的提高, 而腐蚀电流密度大幅度的下降；同时铝锰合金镀层表现出很高的硬度，显著的提高了镁合金的耐蚀耐磨性。

关键词 ：镁合金, 电镀, 铝锰合金, 耐蚀性

Abstract：

Al-Mn alloy coatings were deposited on zinc pre-plated magnesium alloy AZ31B from a bath of inorganic molten salts. Then the microstructure, composition and phase constituents of the coatings were investigated by scanning electron microscopy (SEM), energy-dispersive X-ray spectrometry (EDX), and X-ray diffraction (XRD). The corrosion and wear resistance of the coatings was evaluated by potentiodynamic polarization and microhardness measurements, respectively. The results indicated that the typical processing parameters such as composition of molten salts, cathode currency density and temperature had important effect on the morphology and chemical composition of the Al-Mn alloy, and the alloy coating with various composition present different phase constitution. It showed that the Al-Mn alloy coating exhibited a much higher corrosion potential and lower corrosion rate than that of Mg alloy AZ31B, so it can well protect the magnesium alloy AZ31B against corrosion.

Key words： magnesium alloy electroplating Al-Mn alloy corrosion resistance

收稿日期: 2009-07-03

ZTFLH:

TG174.4

基金资助:

国家重点基础研究发展规划项目（6133003）资助

通讯作者: 严川伟 E-mail: cwyan@imr.ac.cn

Corresponding author: YAN Chuanwei E-mail: cwyan@imr.ac.cn

作者简介: 张吉阜，男，1981年生，博士生，研究方向为腐蚀与防护

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	张吉阜
44.8K

引用本文:

张吉阜,张伟,杜克勤,严川伟,王福会. AZ31B镁合金表面电镀铝锰合金的耐蚀性[J]. 中国腐蚀与防护学报, 2010, 30(4): 300-305.

链接本文:

https://www.jcscp.org/CN/Y2010/V30/I4/300

[1] Gray J E, Luan B. Protective coatings on magnesium and its alloy-a critical review [J]. J. Alloys Compd., 2002, 336 (1-2):88-113 [2] Zhang J, Sun Z F, Study of hot-spray aluminium coating on AZ91D magnesium alloy [J]. China Mech. Eng., 2002, 13(23): 2057-2058 (张津, 孙智富. AZ91D镁合金表面热喷涂铝涂层研究 [J].中国机械工程, 2002, 13(23): 2057-2058) [3] Chiu L H, Chen C C, YangC F. Improvement of corrosion properties in an aluminum-sprayed AZ31 magnesium alloy by a post-hot pressing and anodizing treatment [J].Surf. Coatings Technol., 2005, 191(2-3): 181-187 [4] Liu Y, Yuan X G, Lu N. Wear behavior of cold spray In-Al coating on magnesium alloy [J]. J. Shenyang Univ. Technol., 2003, 191(2-3): 181-187 (刘彦学, 袁晓光, 吕楠. 镁合金表面锌铝合金冷喷涂层的磨损行为 [J].沈阳工业大学学报, 2005, 27(4): 385-388) [5] Dube D, Fiset M, Couture A. Characterization and performance of laser melted AZ91D and AM60B [J]. Mater. Sci. Eng., 2001, A299(1-2): 38-41 [6] Hazra M, Mondal A K, Kumar S, et al. Laser surface cladding of MRI 153M magnesium alloy with (Al+Al₂O₃)[J]. Surf. Coat. Technol., 2009,203(16): 2292-2299 [7] Shigematsu I, Nakamura M, Saitou N, et al. Surface treatment of AZ91D magnesium alloy by aluminum diffusion coating [J]. J. Mater. Sci. Lett., 2000, 19(6): 473-475 [8] Zhang M X, Kelly P M. Surface alloying of AZ91D alloy by diffusion coating [J]. J. Mater. Res., 2002, 17(10): 2477-2479 [9] Zhu L Q, Song G L.Improved corrosion resistance of AZ91D magnesium alloy by an aluminium-alloyed coating [J]. Surf. Coat. Technol., 2006, 200(8):2834-2840 [10] Chang J K, Chen S Y, Tsai W T, et al.Electrodeposition of aluminum on magnesium alloy in aluminum chloride (AlCl₃)-1-ethyl-3-methylimidazolium chloride (EMIC) ionic liquid and its corrosion behavior [J]. Electrochem. Comm., 2007, 9(7):1602-1606 [11] Zhang J F, Yan C W, Wang F H. Electrodeposition of Al-Mn alloy on AZ31B magnesium alloy in molten salts [J]. Appl.Surf. Sci., 2009, 255(9): 4926 [12] Stafford G R. Electrodeposition of an aluminum-mang-anese metallic glass from molten salts [J].J. Electrochem. Soc., 1989, 136 (3): 635-639

[1]	黄鹏, 高荣杰, 刘文斌, 尹续保. 盐溶液刻蚀-氟化处理制备X65管线钢镀镍超双疏表面及其耐蚀性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 96-100.
[2]	郑黎, 王美婷, 于宝义. 镁合金表面冷喷涂技术研究进展[J]. 中国腐蚀与防护学报, 2021, 41(1): 22-28.
[3]	魏征, 马保吉, 李龙, 刘潇枫, 李慧. 镁合金表面超声滚压预处理对微弧氧化膜耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 117-124.
[4]	包任, 周根树, 李宏伟. 恒电位脉冲电沉积高锡青铜耐蚀镀层工艺研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 585-591.
[5]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[6]	岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[7]	刘海霞, 黄峰, 袁玮, 胡骞, 刘静. 690 MPa级高强贝氏体钢在模拟乡村大气中的腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 416-424.
[8]	李聪玮, 杜双明, 曾志琳, 刘二勇, 王飞虎, 马付良. 电流密度对Ni-Co-B镀层微观结构及磨蚀性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(5): 439-447.
[9]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[10]	曹京宜, 方志刚, 陈晋辉, 陈志雄, 殷文昌, 杨延格, 张伟. 5083铝合金表面单致密微弧氧化膜的制备及其性能研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 251-258.
[11]	王英君, 刘洪雷, 王国军, 董凯辉, 宋影伟, 倪丁瑞. 新型高强稀土Al-Zn-Mg-Cu-Sc铝合金的阳极氧化及其抗腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 131-138.
[12]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[13]	王乐,易丹青,刘会群,蒋龙,冯春. Ru对Ti-6Al-4V合金腐蚀行为的影响及机理研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 25-30.
[14]	武栋才,韩培德. 中温时效处理对SAF2304双相不锈钢耐蚀性的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 51-56.
[15]	郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.

Viewed

Full text

Abstract

Cited

Shared

Discussed