三种缓蚀性阴离子对碳钢在NaHCO3-NaCl溶液中点蚀的抑制作用

中国腐蚀与防护学报

2004, Vol. 24

Issue (3): 174-178

研究报告

本期目录 | 过刊浏览

三种缓蚀性阴离子对碳钢在NaHCO3-NaCl溶液中点蚀的抑制作用

赵景茂

北京化工大学材料科学与工程学院23信箱

Jingmao Zhao

北京化工大学材料科学与工程学院23信箱

全文: PDF(173 KB)

摘要: 利用动电位扫描法、恒电流模拟闭塞电池研究了MoO2-4、Cr2O2-7、PO3-4等3种离子对A3钢在NaHCO3-NaCl溶液中点蚀形核和点蚀发展的影响以及作用机理.结果表明，MoO2-4和PO3-4都对小孔形核和发展起到抑制作用，而Cr2O2-7仅对小孔形核起到抑制作用，对小孔生长则起到促进作用.进一步的研究表明，造成这种差别的主要原因是它们在蚀孔闭塞区内对溶液pH的影响是不一样的.MoO2-4和PO3-4进入闭塞区后，能提高pH，抑制了阴极过程；而Cr2O2-7使pH下降，促进了阴极过程.

关键词 ：阴离子, 缓蚀剂, 点蚀, 碳钢, NaHCO3-NaCl溶液

Abstract：The effects of molybdate,phosphate and dichromate anions on pit propagation of mild steel in aHCO3-NaCl solution were investigated by electrochemical measurements.MoO2-4 and PO3-4 ions suppressed both pit ucleation and propagation.Cr2O2-7 ion suppressed pit nucleation,but stimulated pit growth.The further study showed that the different effects of the three anions on pit propagation could be explained by their effects on pH value within pits.The pH value increased after adding molybdate or phosphate in the pit simulated solution as a result of polymerization of MoO2-4 or the hydrolysis of PO3-4,while pH value decreased after adding dichromate anions due to hydrolysis of Fe3+and Cr3+ which were the produ cts of oxide-reducing reactions between Cr2O2-7 and Fe2+ions.

Key words： anions corriosion inhibitior pitting corrosion carbon steel NaHCO3-NaCl solution

收稿日期: 2002-10-08

ZTFLH:

TG174.42

通讯作者: 赵景茂 E-mail: jingmaozhao@sohu.com

Corresponding author: Jingmao Zhao E-mail: jingmaozhao@sohu.com

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	赵景茂
44.8K

引用本文:

赵景茂 . 三种缓蚀性阴离子对碳钢在NaHCO3-NaCl溶液中点蚀的抑制作用[J]. 中国腐蚀与防护学报, 2004, 24(3): 174-178 .
Jingmao Zhao. . J Chin Soc Corr Pro, 2004, 24(3): 174-178 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I3/174

[1]YangWu.LocalizedCorrosionofMetal[M ].Beijing:ChemicalIn dustryPress,1995,104(杨武.金属的局部腐蚀[M ].北京:化学工业出版社,1995,104)
[2]LiJQ ,ZhouDR ,XuHT .AstudyofthemechanismforinhibitionpittingofGCr15steelbysodiummolybdate[J].J .Chin.Soc.Cor ros.Prot.,1986,6(1):15-21(利建强,周德瑞,徐海涛.钼酸钠抑制GCr15钢点蚀机理的研究[J].中国腐蚀与防护学报,1986,6(1):15-21)
[3]ChenXJ,WangHL ,ChenZJ.Mechanismofmolybdateforinhibi tionofpittingcorrosionofstainlesssteel[J].J .Chin.Soc.Corros.Prot.,1992,12(3):213-220(陈旭俊,王海林,陈振家.钼酸盐对不锈钢孔蚀抑制作用机理的研究[J].中国腐蚀与防护学报,1992,12(3):213-220)
[4]FujiokaE ,NishiharaH ,AramakiK .TheinhibitionofpitnucleationandgrowthonthepassivesurfaceofironinaboratebuffersolutioncontainingCl- byoxidizinginhibitors[J].Corros.Sci.,1996,38(11):1915-1933
[5]ZuoJY ,JinZQ .Investigationofchemicalandelectrochemicalchangeswithincorrosioncracks[J].J.ChemicalIndustryandEngi neering,1982,4(4):291-309(左景伊,金志强.腐蚀裂纹内化学和电化学状态之探索[J].化工学报,1982,4(4):291-309)
[6]XuCC ,FuXP ,LiuYP .Migrationofvariousinorganicanionsandtheireffectsonoccludedcorrosioncell[J].Corros.Sci.Prot.Tech nol.,2000,12(3):130-133(许淳淳,傅晓萍,刘幼平.几种无机阴离子的电迁移及其对闭塞区的影响[J].腐蚀科学与防护技术,2000,12(3):130-133)
[7]GrewoodNN ,EarnshawA .ChemistryoftheElements[M ].Bei jing:AdvancedEducationPress,1996,153(GrewoodNN ,EarnshawA .元素化学[M ].北京:高等教育出版社,1996,153)
[8]ZuoY ,WangHT ,ZhaoJM ,XiongJP .Theeffectsofsomeanionsonthemetastablepittingof316Lstainlesssteel[J].Corros.Sci.,2002,44(1):13-24

[1]	冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2]	白云龙, 沈国良, 覃清钰, 韦博鑫, 于长坤, 许进, 孙成. 硫脲基咪唑啉季铵盐缓蚀剂对X80管线钢腐蚀的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 60-70.
[3]	王亚婷, 王棵旭, 高鹏翔, 刘冉, 赵地顺, 翟建华, 屈冠伟. 淀粉接枝共聚物对Zn的缓蚀性能[J]. 中国腐蚀与防护学报, 2021, 41(1): 131-138.
[4]	张浩, 杜楠, 周文杰, 王帅星, 赵晴. 模拟海水溶液中Fe³⁺对不锈钢点蚀的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[5]	于浩冉, 张文丽, 崔中雨. 4种镁合金在Cl^--NH₄⁺-NO₃^-溶液体系中的腐蚀行为差异研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 553-559.
[6]	戴明杰, 刘静, 黄峰, 胡骞, 李爽. 基于正交方法研究阴极保护电位波动下X100管线钢的点蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(5): 425-431.
[7]	张欣, 杨光恒, 王泽华, 曹静, 邵佳, 周泽华. 冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[8]	贺三, 孙银娟, 张志浩, 成杰, 邱云鹏, 高超洋. 20#钢在含饱和CO₂的离子液体醇胺溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 309-316.
[9]	李清, 张德平, 王薇, 吴伟, 卢琳, 艾池. L80油管钢实际腐蚀状况评估及室内电化学和应力腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 317-324.
[10]	郏义征, 王保杰, 赵明君, 许道奎. 固溶处理制度对挤压态Mg-Zn-Y-Nd镁合金在模拟体液中腐蚀和析氢行为的影响规律研究[J]. 中国腐蚀与防护学报, 2020, 40(4): 351-357.
[11]	邵明鲁, 刘德新, 朱彤宇, 廖碧朝. 乌洛托品季铵盐缓蚀剂的合成与复配研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 244-250.
[12]	贾巧燕, 王贝, 王赟, 张雷, 王清, 姚海元, 李清平, 路民旭. X65管线钢在油水两相界面处的CO₂腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(3): 230-236.
[13]	张晨, 陆原, 赵景茂. CO₂/H₂S腐蚀体系中咪唑啉季铵盐与3种阳离子表面活性剂间的缓蚀协同效应[J]. 中国腐蚀与防护学报, 2020, 40(3): 237-243.
[14]	吕祥鸿,张晔,闫亚丽,侯娟,李健,王晨. 两种新型曼尼希碱缓蚀剂的性能及吸附行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 31-37.
[15]	何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.

Viewed

Full text

Abstract

Cited

Shared

Discussed