紫外光对涂层的老化作用

中国腐蚀与防护学报

2004, Vol. 24

Issue (3): 168-173

研究报告

本期目录 | 过刊浏览

紫外光对涂层的老化作用

徐永祥

北京航空材料研究所

UV PHOTO-DEGRADATION OF COATINGS

Yongxiang Xv

北京航空材料研究所

全文: PDF(230 KB)

摘要: 用人工加速的方法研究了紫外光对涂层的影响.用石英晶体微天平(QCM)测试发现老化后涂层对H2O和SO2的吸附率明显增大.电化学阻抗(EIS)测定发现孔隙率随光照射时间增加而增大，涂层电阻随光照时间增加而减小.傅利叶变换红外光谱(FTIR)分析表明，光照使涂层分子碳链断裂，醇酸涂层发生在芳香酯的C-O键，聚氨酯涂层发生在芳香酯的C-O键和氨酯键C-N，同时有一些亲水基团生成.用扫描电子显微镜(SEM)观察涂层表面产生了许多孔穴.涂层吸水率增加是由亲水基团增加和孔隙增加共同引起的，但孔隙增加的贡献更大.而涂层对SO2吸附率的增加是由双键α-H过氧化物的增加和孔隙的增加共同引起的，α-H过氧化物的增加的贡献更大.

关键词 ：涂层, 紫外光, 老化

Abstract：Photo-oxidation initiated by ultraviolet ray (UV) is a pivotal factor which affects degradation of the coatings.Quartz crystal microbalance (QCM) testing results show that the absorbance of water and SO2 in the coatings increases remarkably after exposure to UV.Changes in porosity after exposure were means of electrochemical impedance spectroscopy (EIS),and the results show that the porosity increases with the increase of exposure time.Fourier transform infrared spectroscopy (FTIR) analysis shows that reakdowoccurs in the C-chain of the coatings after exposure to UV,which occurs at C-O bond of aromaticester for the alkyd resin and at C-O bond of aromatic ester and C-N bond of urethane for the olyurethane resin.Some hydrophilic groups may be formed simultaneously.Scanning electron microscope (SEM) was employed to analyze the morphology of the coatings and the results show that many pores and holes were formed after exposure to UV.It was suggested that the increase of water is the cooperation of the increases both of the amount of hydrophilic groups and of the porosity of the coatings,but the contribution of the increase of porosity may be greater.The increase of absorbance of SO2 is the cooperation of the increase ofα-H peroxide and the increase of porosity,but the contribution of theincrease of α-H peroxide may be higher.

Key words： coatings photo-degradation EIS

收稿日期: 2002-10-08

ZTFLH:

TG174

通讯作者: 徐永祥

Corresponding author: Yongxiang Xv

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	徐永祥
44.8K

引用本文:

徐永祥 . 紫外光对涂层的老化作用[J]. 中国腐蚀与防护学报, 2004, 24(3): 168-173 .
Yongxiang Xv. UV PHOTO-DEGRADATION OF COATINGS. J Chin Soc Corr Pro, 2004, 24(3): 168-173 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2004/V24/I3/168

[1]ArmstrongRD ,JenkinsATA ,JohnsonBW .AninvestigationintotheUVbreakdownofthermosetpolyestercoatingsusingimpedancespectroscopy[J].Corros.Sci.,1995,37(10):1615-1625.
[2]BauerDR .Melamine/formaldehydecrosslinkers:characterization,networkformationandcrosslinkdegradation[J].Prog.Org.Coat.,1986,14:193.
[3]PappasSP .Weatheringofcoatings-formulationandevaluation[J].Prog.Org.Coat.,1989,17:107.
[4]OosterbroekM ,LarmmersRJ ,VanderVenLGJ,PereraDY .Crackformationandstressdevelopmentinanorganiccoating[J].J .Coat.Tech.,1991,63(797):55-60.
[5]OsterholdM ,GlocknerP .Influenceofweatheringonphysicalprop ertiesofclearcoats[J].Prog.Org.Coat.,2001,41:177-182
[6]XuYX ,YanCW ,DingJ ,etal.Diffusionandabsorptionofwatervaporinthecoatings[J].Corros.Sci.Prot.Technol.,2001,13(suppl.):493-496(徐永祥,严川伟,丁杰等.水汽在涂层中的扩散和吸收[J].腐蚀科学与防护技术,2001,第13卷增刊:493-496)
[7]XuYX .Studiesonthemechanismofdegradationoforganiccoatingsandunderfilmcorrosionofsubstrateinatmosphere[D ].Shenyang:InstituteofMetalResearch,TheChineseAcademyofSciences,2002(徐永祥.大气环境中涂层失效和涂层下金属腐蚀机理的研究[D].沈阳:中国科学院金属研究所,2002)
[8]ArmstrongRD ,JohnsonBW .Aninvestigationintothecathodicdelaminationofunpigmentedrubberfilms[J].Corros.Sci.,1991,32:303.
[9]ArmstrongRD ,JohnsonBW ,WrightJD .Aninvestigationintothecathodicdelaminationofepoxy-polyamineprotectivecoatings[J].Electrochim.Acta,1991,36:1915
[10]FeliuS ,GalvanJC ,MorcilloM .ThechargetransferreactioninNyquistdiagramsofpaintedsteel[J].Corros.Sci.,1990,30(10):989-998.
[11]MansfeldF ,KendigMW ,TsaiS .EvaluationofcorrosionbehaviorofcoatedmetalswithACimpedancemeasurements[J].Corrosion,1982,38(9):478.
[12]ArmstrongRD ,WrightJD .Polymerprotectivecoatings:Thedis tinctionbetweencoatingsporosityandthewettedmetalarea[J].Electrochim.Acta,1993,38(14):1799-1801
[13]YuZhaonian.PaintTechnology(Addition)Vol.2[M ].Beijing:ChemicalIndustryPress,1996(虞兆年主编.涂料工艺(增订本)第二分册[M ].北京:化学工业出版社,1996)
[14]BauerDR ,PaputaPeckMC ,CarterIIIRO .Evaluationofaccel eratedweatheringtestsforapolyester-urethanecoatingusingphotoacousticinfraredspectroscopy[J].J .Coat.Technol.,1987,59(755):103-109.
[15]MallegolJ,GononL ,CommeeucS ,VerneyV .Thermalandchemi cal(iodometrictitration)methodsforperoxidesmeasurementsinordertomonitordryingextentofalkydresins[J].Prog.Org.Coat.,2001,41:171-176.
[16]McEwenDJ,VermaMH ,TurnerRO .Acceleratedweatheringofautomotivepaintsmeasurementsbyglossandinfraredspectroscopy[J].J .Coat.Techn.,1987,59(755):123-129.
[17]WuJinguang.TechnologyandApplicationofModernFourierTransformInfraredSpectroscopy[M ].Beijing:LiteratureofSci enceandTechnologyPress,1994(吴瑾光主编.近代傅利叶变换红外光谱技术及应用[M ].北京:科学技术文献出版社,1994:573-648)

[1]	任岩, 钱余海, 张鑫涛, 徐敬军, 左君, 李美栓. 热震对包覆ZrB₂-SiC-La₂O₃/SiC涂层渗硅石墨力学性能的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 29-35.
[2]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3]	刘洋, 吴进怡, 闫小宇, 柴柯. 海洋环境中芽孢杆菌对聚氨酯清漆涂层分解的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 36-42.
[4]	曹京宜, 王智峤, 李亮, 孟凡帝, 刘莉, 王福会. 深海压力交变加速条件下改性石墨烯有机涂层的失效机制[J]. 中国腐蚀与防护学报, 2020, 40(2): 139-145.
[5]	师超,邵亚薇,熊义,刘光明,俞跃龙,杨志广,许传钦. 硅烷偶联剂改性磷酸锌对环氧涂层防腐性能的影响[J]. 中国腐蚀与防护学报, 2020, 40(1): 38-44.
[6]	赵书彦,童鑫红,刘福春,翁金钰,韩恩厚,郦晓慧,杨林. 环氧富锌涂层防腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 563-570.
[7]	王贵容,郑宏鹏,蔡华洋,邵亚薇,王艳秋,孟国哲,刘斌. 环氧防腐涂料在模拟海水干湿交替条件下的失效过程[J]. 中国腐蚀与防护学报, 2019, 39(6): 571-580.
[8]	余春堂,阳颖飞,鲍泽斌,朱圣龙. 先进高温热障涂层用高性能粘接层制备及研究进展[J]. 中国腐蚀与防护学报, 2019, 39(5): 395-403.
[9]	李烽杰,陈明辉,张哲铭,王硕,王福会. 金属搪瓷高温防护涂层的制备及其抗热震行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 411-416.
[10]	陈超,梁艳芬,梁天权,满泉言,罗毅东,张修海,曾建民. 稀土复合掺杂ZrO₂陶瓷涂层抗Na₂SO₄+NaVO₃热腐蚀性能的研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 291-298.
[11]	艾鹏,刘礼祥,李晓罡,姜文涛. TiAlSiN涂层对γ-TiAl基合金抗高温氧化性能的影响[J]. 中国腐蚀与防护学报, 2019, 39(4): 306-312.
[12]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[13]	王贵容,邵亚薇,王艳秋,孟国哲,刘斌. 阴极保护电位对破损环氧涂层阴极剥离的影响[J]. 中国腐蚀与防护学报, 2019, 39(3): 235-244.
[14]	虞礼嘉,梁文萍,林浩,缪强,黄彪子,崔世宇. 激光重熔YSZ热障涂层950 ℃的热腐蚀行为[J]. 中国腐蚀与防护学报, 2019, 39(1): 77-82.
[15]	陈浩,陈庆,辛丽,时龙,朱圣龙,王福会. DD98M纳米晶AlSi渗层制备及抗高温腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(1): 59-67.

Viewed

Full text

Abstract

Cited

Shared

Discussed