常用铸铁材料海水腐蚀行为的研究

中国腐蚀与防护学报

2003, Vol. 23

Issue (2): 99-102

研究报告

本期目录 | 过刊浏览

常用铸铁材料海水腐蚀行为的研究

夏兰廷;韦华;朱宏喜

太原重型机械学院

STUDY OF CORROSION BEHAVIOR ON COMMON CAST IRON MATERIALS EXPOSED TO SEAWATER

Lanting Xia;Hua Wei;Hongxi Zhu

太原重型机械学院

全文: PDF(136 KB)

摘要: 对常用铸铁材料在实海和流动海水条件下的腐蚀性能进行了测试，分析了铸铁中不同石墨形态、基体组织、低合金化对铸铁腐蚀性能的影响机理.结果表明：片状石墨铸铁耐腐蚀性能优于球状石墨的铸铁；球状石墨铸铁平均腐蚀率最小，但具有强烈的点蚀倾向；铸铁在实海中的腐蚀行为以化学-电化学溶解为主，流动海水中的冲蚀-磨蚀进一步加剧其化学-电化学溶解.

关键词 ：实海, 流动海水, 腐蚀行为, 石墨形态, 点蚀

Abstract：The corrosion properties of common cast iron materi als in static (flowing velocity is about 0.1 m/s)and flowing seawater were teste d,and effects of graphite morphology,matrix microstructure and low alloying trea tment on corrosion properties of cast irons were analyzed.The experimental resul ts indicate that the corrosion-resistance property of flake graphite samples is superior to that of spherical graphite samples.The average corrosion rate of sph erical graphite samples,compared with other samples,was little,but its tendency of pitting corrosion is intensively obvious.For samples in static and low flowin g seawater (flowing velocity is more than 3 m/s),chemistry-electrochemistry d issolution mechanism is almost wholly responsible for their corrosion behavior.A s to sampl es in high flowing seawater (flowing velocity is equal to or more than 7 m/s),er osion-ablation behavior further accelerates chemical-electrochemical dissolution .

Key words： static seawater flowing seawater corrosion behavior gr aphite morphology pitting corrosion

收稿日期: 2002-04-28

ZTFLH:

TG172.82

通讯作者: 夏兰廷 E-mail: yjszsb@tyhmi.edu.cn

Corresponding author: Lanting Xia E-mail: yjszsb@tyhmi.edu.cn

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	夏兰廷
	韦华
	朱宏喜
44.8K

引用本文:

夏兰廷; 韦华; 朱宏喜 . 常用铸铁材料海水腐蚀行为的研究[J]. 中国腐蚀与防护学报, 2003, 23(2): 99-102 .
Lanting Xia, Hua Wei, Hongxi Zhu. STUDY OF CORROSION BEHAVIOR ON COMMON CAST IRON MATERIALS EXPOSED TO SEAWATER. J Chin Soc Corr Pro, 2003, 23(2): 99-102 .

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2003/V23/I2/99

[1]FuShenghua,HuDeli.Alloyingcastsformedself-grownprotectionscaleinseawater[J].Foundry,1995,217,2:29-32(付圣华,胡德利.在海水中形成自生保护膜的合金铸铁[J].铸造,1995,(2版社,1995)
[2]Panmu, Luozhiping .Science and Engineering ,1999,17,1:92-96?1999,17,1:92-96(潘牧,罗志平.材料的冲蚀问题[J].材料科学与工程,1999(17):92-96)
[3]YangWu,GuRuiyang,Xiaojingguang.LocalizedCorrosionofMet als[M ].Beijing:PublishingHouseofChemicalIndustry,1995(杨武,顾睿祥,肖景光.金属的局部腐蚀[M ].北京:化学工业出版社,1995)
[4]OrenkD ,JayaramanA ,WoodTK ,etal.Pittingcorrosioncontrolusingregenerativebiofilmsonaluminum2024inartificialseawater[J].Corros.Sci.,2001,43,11:2121-2133
[5]LeBozecN ,CompereC ,HerML ,etal.Influenceofstainlesssteelsurfacetreatmentontheoxygenreductionreactioninseawater[J].Corros.Sci.,2001,43,4:765-786
[6]LittleBJ,WagnerPA .Theinterrelationshipbetweenmarinebio foulingcathodicprotectionandmiscrobiologicallyinfluencedcorro sion[J].MaterialSocialForum,1995,433:192-194
[7]WeiHua.Corrosionbehavior& protectionofcommoncastironma terialsexposedtoseawater[D].Taiyuan:Master’sdissertationofTaiyuanHeavyMachineryInstitute,2000(韦华.铸铁在海水中的腐蚀行为及其防护措施[D].太原:太原重型机学院硕士学位论文,2000)
[8]YunSooLin,JoungSooKin,SeJimAhn,HyukSangKwon,Ya suyukiKatada.Theinfluenceofmicrostructureandnitrogenalloyingonpittingcorrosionoftype316Land20Wt.%Mnsubstitutedtyped316Lstainlesssteels[J].Corros.Sci.,2001,43,1:53-68

[1]	李琳, 陈义庆, 高鹏, 艾芳芳, 钟彬, 伞宏宇, 杨颖. 除冰盐环境下桥梁钢的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[2]	张欣, 杨光恒, 王泽华, 曹静, 邵佳, 周泽华. 冷拉拔变形过程中含稀土铝镁合金腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[3]	胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[4]	王新华, 杨永, 陈迎春, 位凯玲. 交流电流对X100管线钢在库尔勒土壤模拟液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[5]	胡玉婷, 董鹏飞, 蒋立, 肖葵, 董超芳, 吴俊升, 李晓刚. 海洋大气环境下TC4钛合金与316L不锈钢铆接件腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[6]	张尧, 郭晨, 刘妍慧, 郝美娟, 成世明, 程伟丽. 挤压态Mg-2Sn-1Al-1Zn合金在模拟体液中的电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(2): 146-150.
[7]	苏小红,胡会娥,孔小东. W颗粒/Zr_41.2Ti_13.8Cu_12.5Ni₁₀Be_22.5基非晶复合材料在3%NaCl溶液中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 70-74.
[8]	王勤英,裴芮,西宇辰. 镍基激光熔覆层冲刷腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[9]	郭铁明,张延文,秦俊山,宋志涛,董建军,杨新龙,南雪丽. 桥梁钢Q345q在3种模拟大气环境中的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 319-330.
[10]	彭文山,侯健,丁康康,郭为民,邱日,许立坤. 深海环境中304不锈钢腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(2): 145-151.
[11]	黄博博,刘平,刘新宽,梅品修,陈小红. 新型HSn70-1铜网衣两年期海水腐蚀行为研究[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
[12]	孙艳, 吴佳佳, 张盾, 陈士强. 不同海域、不同腐蚀区带Q235碳钢实海挂片腐蚀产物层内微生物调查[J]. 中国腐蚀与防护学报, 2018, 38(4): 333-342.
[13]	曹海娇, 魏英华, 赵洪涛, 吕晨曦, 毛耀宗, 李京. Q345钢预热时间对熔结环氧粉末涂层防护性能的影响II：涂层体系失效行为分析[J]. 中国腐蚀与防护学报, 2018, 38(3): 255-264.
[14]	张杰, 胡秀华, 郑传波, 段继周, 侯保荣. 海洋微藻环境中钙质层对Q235碳钢腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2018, 38(1): 18-25.
[15]	张子阳,王善林,章恒瑜,柯黎明. AZ31镁合金搅拌摩擦焊接头腐蚀行为[J]. 中国腐蚀与防护学报, 2017, 37(2): 117-125.

Viewed

Full text

Abstract

Cited

Shared

Discussed