中国腐蚀与防护学报  2000, Vol. 20 Issue (5): 287-292     
  研究报告 本期目录 | 过刊浏览 |
H2S水溶液中的腐蚀与缓蚀作用机理的研究 Ⅳ、碱性硫化物溶液中Cl-对碳钢钝化行为的影响
杨怀玉;陈家坚;曹楚南
中科院金属所金属腐蚀与防护国家重点实验室
CORRODION AND INHIBITION MECHANISM IN H2S AQUEOUS SOLUTONS Ⅳ The Effects of Cl- on the Behavior of Passivity of Carbon Steel in Alkaline Solutions Containing Sulfide
Huiyu Yang;;;
中科院金属所金属腐蚀与防护国家重点实验室
全文: PDF(170 KB)  
摘要: 利用交流阻抗和动电位极化技术,在碱性硫化物溶液中,分别研究了阳极极化电位下Cl-对低碳钢钝化过程阻抗行为的影响,钝化膜临界孔蚀电位Eb与Cl-浓度的关系以及临界Cl-浓度随温度的变化。结果表明,在除氧的碱性硫化物溶液中,阳极极化的初期阻抗具有两个时间常驻数,随极化电位的升高,钝化膜逐步趋于完整;在点蚀的形成过程中,容抗弧半径逐渐变小,当极化电位为-600mV时容抗弧半径大幅度下降,并出现低频实部电感性收缩现象;在点蚀形成后的发展阶段,容Cl-浓度增加,电极表面的钝化颁向降低,临界孔蚀电位随Cl-浓度增加而线性正移。
关键词 阻抗极化曲线钝化局部腐蚀    
Abstract:The effects of Cl- on the AC impedance features of carbon steel under anodic polarization conditions, and the critical pitting potential (Eb) at different temperature have been investigated respectively by EIS and potentiodynamic polarizaton in alkaline solutions containing H2S.The results indicate that the carbon steel gets into stage of passivity with increasing of polarization potential at the initial stage of anodic polarization During the pitting initiation, the Nyquist diagram has a shrinkage of real part at low frequency and the polarization resistance sharply decreases.The Nyquist diagram is composed of two capacitive loops during the pits propagation.With increasing of polarization potential, the capacitive loop of high frequency disappwars.With increasing of Cl- concentration at different temperature, the passivity trend of mild steel decreases.The relationship beetween Eb and Cl- concentration at different temperature follows the Eb=a + blnCcl-
Key wordsEIS    potentiodynamic polarization    pitting    Cl-
收稿日期: 1999-08-27     
ZTFLH:  TG172  
通讯作者: 杨怀玉   
Corresponding author: Huiyu Yang   

引用本文:

杨怀玉; 陈家坚; 曹楚南 . H2S水溶液中的腐蚀与缓蚀作用机理的研究 Ⅳ、碱性硫化物溶液中Cl-对碳钢钝化行为的影响[J]. 中国腐蚀与防护学报, 2000, 20(5): 287-292 .
Huiyu Yang. CORRODION AND INHIBITION MECHANISM IN H2S AQUEOUS SOLUTONS Ⅳ The Effects of Cl- on the Behavior of Passivity of Carbon Steel in Alkaline Solutions Containing Sulfide. J Chin Soc Corr Pro, 2000, 20(5): 287-292 .

链接本文:

https://www.jcscp.org/CN/      或      https://www.jcscp.org/CN/Y2000/V20/I5/287

[1]曹楚南,王佳,林海潮.氯离子对钝态金属电极阻抗谱的影响[J].中国腐蚀与防护学报, 1989,9(4):261
[2] Mansfeld F,Kendig M W,Tsai S.Recording and analysis of AC impedance data for corrosion studiesⅡ.Experimental approach and results[J]. Corrosion,1982,38:570
[3]王佳,曹楚南,林海潮.孔蚀发展期的电极阻抗频谱特征[J].中国腐蚀与防护学报,1989,9(4):271
[4] Ferreira M G S, Dawson J L. Electrochemical studies of the pitting of the pitting of austenitic stainless steel[J]. Corrosion Science,1986,26:1009
[5] 兴户政正纯。木村孔,冲猛雄。Impedance response of iron chromium and SUS430 steel electrodes in neutral Na2SO4 solution[J].日本金属会志,1988,49:112
[6] Schutt H U, Rhodes P R. Corrosion in an aqueous hydrogen sulfide, ammonia and oxygen system[J]. Corrosion,1996, 52(12):947
[7] French E C, Fahey W. Water soluble filming inhibitor system for corrosion control in crudeu unit overhead[J]. Materials Performance,1983, (9):9.
[8] Merrick R D, Auerbach . crude unit overhead corrosion control[J].Materials Performance, 1983,(9):15
[9]杨怀玉,陈家坚,曹楚南,曹殿珍.H2S溶液中的腐蚀与缓蚀作用机理的研究.I酸性H2S溶液中碳钢的腐蚀行为及硫化 物的生长[J].中国腐蚀与防护学报,2000,20(1):1
[10]曹楚南.腐蚀电化学[M].北京:化学工业出版社,1994.164
[11] Okada I.The rate of passive metal dissolution in relation to the presence of transitional halide complexes in halide solutions[J].Corrosion Science, 1986, 26:839.
[12]杨怀玉.碳钢在H2S溶液中的腐蚀及咪唑啉缓蚀作用的研究[D].沈阳:中科院金属腐蚀与防护研究所[博士论文]. 1999.659
[1] 冉斗, 孟惠民, 刘星, 李全德, 巩秀芳, 倪荣, 姜英, 龚显龙, 戴君, 隆彬. pH对14Cr12Ni3WMoV不锈钢在含氯溶液中腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2021, 41(1): 51-59.
[2] 史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3] 贾世超, 高佳祺, 郭浩, 王超, 陈杨杨, 李旗, 田一梅. 再生水水质因素对铸铁管道的腐蚀研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 569-576.
[4] 岳亮亮, 马保吉. 超声表面滚压对AZ31B镁合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(6): 560-568.
[5] 李子运, 王贵, 罗思维, 邓培昌, 胡杰珍, 邓俊豪, 徐敬明. 热带海洋大气环境中EH36船板钢早期腐蚀行为研究[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[6] 胡露露, 赵旭阳, 刘盼, 吴芳芳, 张鉴清, 冷文华, 曹发和. 交流电场与液膜厚度对A6082-T6铝合金腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[7] 孙硕, 杨杰, 钱薪竹, 常人丽. Ni-Cr-P化学镀层的制备与电化学腐蚀行为[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[8] 何壮,王兴平,刘子涵,盛耀权,米梦芯,陈琳,张岩,李宇春. 316L和HR-2不锈钢在盐酸液膜环境中的钝化与点蚀[J]. 中国腐蚀与防护学报, 2020, 40(1): 17-24.
[9] 张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[10] 郏义征, 赵明君, 程世婧, 王保杰, 王硕, 盛立远, 许道奎. 模拟人体体液中镁合金的腐蚀行为研究[J]. 中国腐蚀与防护学报, 2019, 39(6): 463-468.
[11] 史伟宁,杨树峰,李京社. 不锈钢中诱发局部腐蚀的贫Cr区研究进展[J]. 中国腐蚀与防护学报, 2019, 39(4): 281-290.
[12] 孙晓光,韩晓辉,张星爽,张志毅,李刚卿,董超芳. 超低碳奥氏体不锈钢焊接接头耐腐蚀性及环保型化学钝化工艺研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 345-352.
[13] 王霞,任帅飞,张代雄,蒋欢,古月. 豆粕提取物在盐酸中对Q235钢的缓蚀性能[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[14] 达波,余红发,麻海燕,吴彰钰. 等效电路拟合珊瑚混凝土中钢筋锈蚀行为的电化学阻抗谱研究[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[15] 王保杰,栾吉瑜,王士栋,许道奎. 镁合金应力腐蚀开裂行为研究进展[J]. 中国腐蚀与防护学报, 2019, 39(2): 89-95.