热处理对Ni-P/纳米Al<sub>2</sub>O<sub>3</sub>复合镀层组织及耐腐蚀性能的影响

中国腐蚀与防护学报

2011, Vol. 31

Issue (3): 179-183

研究报告

本期目录 | 过刊浏览

热处理对Ni-P/纳米Al₂O₃复合镀层组织及耐腐蚀性能的影响

彭成章,朱玲玲

湖南科技大学湖南省机械设备健康维护重点实验室湘潭 411201

INFLUENCE OF HEAT TREATMENT ON MICROSTRUCTURE AND CORROSION RESISTANCE OF Ni-P/NANO-Al₂O₃ COMPOSITE COATING

PENG Chengzhang, ZHU Lingling

Hunan Provincial Key Laboratory of Health Maintenance for Mechanical Equipment, Hunan University of Science and Technology, Xiangtan 411201

全文: PDF(1363 KB)

摘要: 采用脉冲电沉积方法在Q235钢表面制备Ni-P/纳米Al₂O₃复合镀层，对复合镀层进行200~400℃的热处理。利用X射线衍射仪分析复合镀层的组织结构，用电化学极化曲线和扫描电镜(SEM)研究复合镀层在3.5% NaCl和10% H₂SO₄溶液中的腐蚀行为。结果表明，纳米Al₂O₃颗粒推迟热处理过程中复合镀层内Ni₃P相的析出，其晶化温度高于Ni-P合金镀层；镀态及300℃热处理复合镀层在两种腐蚀介质中均表现出优异的耐腐蚀性能，400℃热处理复合镀层的耐腐蚀性能下降，镀层表面发生点蚀。

关键词 ：热处理, 脉冲电沉积, Ni-P/纳米Al₂O₃复合镀层, 耐腐蚀性

Abstract：The Ni-P/nano-Al₂O₃ composite coating on Q235 steel was prepared by pulse electroplating, the composite coatings were heat-treated at temperature of 200-400 ℃. The microstructure of the composite coatings was identified by X-ray diffraction, the corrosion behavior of the composite coatings in 3.5% NaCl and 10% H₂SO₄ solutions was studied by the linear polarization measurements and scanning electron microscope (SEM). The results show that nano-Al₂O₃ particles retard precipitating of Ni₃P phase in composite coating, the crystallization temperature of the composite coating is higher than that of Ni-P alloy coating. The as-deposited and after 300℃ heat-treated composite coatings revealed better corrosion resistance in two corrosive solutions. The corrosion resistance of after 400℃ heat-treated composite coatings decreased. The corrosion behavior is pitting corrosion.

Key words： heat treatment pulse electroplating Ni-P/nano-Al₂O₃ composite coating corrosion resistance

收稿日期: 2010-12-06

ZTFLH:

TG176

基金资助:

国家自然基金资助项目(50764004)，湖南省科技计划项目(2010FJ3093)以及湖南省高校科技创新团队支持计划项目资助

通讯作者: 彭成章 E-mail: pcz2002@sohu.com

Corresponding author: PENG Chengzhang E-mail: pcz2002@sohu.com

作者简介: 彭成章，男，1965年生，副教授，博士，研究方向为材料成形与加工、材料表面改性技术

	服务

	把本文推荐给朋友
	加入引用管理器
	E-mail Alert
	RSS
	作者相关文章
	彭成章
	朱玲玲
44.8K

引用本文:

彭成章,朱玲玲. 热处理对Ni-P/纳米Al₂O₃复合镀层组织及耐腐蚀性能的影响[J]. 中国腐蚀与防护学报, 2011, 31(3): 179-183.
PENG Cheng-Zhang, ZHU Ling-Ling. INFLUENCE OF HEAT TREATMENT ON MICROSTRUCTURE AND CORROSION RESISTANCE OF Ni-P/NANO-Al₂O₃ COMPOSITE COATING. J Chin Soc Corr Pro, 2011, 31(3): 179-183.

链接本文:

https://www.jcscp.org/CN/ 或 https://www.jcscp.org/CN/Y2011/V31/I3/179

[1] Straffelini G, Colombo D, Molinari A. Surface durability of electroless Ni-P composite deposits [J]. Wear, 1999, 236: 179-188

[2] Liu L H, Zhang Z H, Yan J, et al. Corrosion behavior of autocatalytic plating Ni-P coating in marine atmospheric environment [J]. J. Chin. Soc. Corros. Prot., 2010, 30(5): 369-373

    (刘丽红, 张子华, 闫杰等. 化学镀镍磷合金在海洋环境中的腐蚀行为 [J]. 中国腐蚀与防护学报, 2010, 30(5): 369-373)

[3] Zhang H, Shen X M. Optimization of technology parameter of Ni-P/SiC wear resistance composite electroless plating [J]. J. Zhengzhou Univ., 2004, 36(3): 54-58

    (张恒, 沈献民. Ni-P/SiC耐磨性化学复合镀工艺参数优化 [J]. 郑州大学学报, 2004, 36(3): 54-58)

[4] Liu T H. Study on wear resistance of Ni-P-Cr₂O₃ composite electroless plating [J].Lubr. Eng., 2002, (6): 45-46

    (刘铁虎. Ni-P-Cr₂O₃化学复合镀层耐磨性的研究 [J]. 润滑与密封, 2002, (6): 45-46)

[5] Zhang Q D, Zhang L J, Song L Z, et al. Study of Ni-P-PTFE electroless [J]. J. Harbin Inst. Technol., 1999, 31(1): 127-129

    (张秋道, 张丽娟, 宋来洲等. 化学复合镀Ni-P-PTFE镀层性能的研究 [J]. 哈尔滨工业大学学报, 1999, 31(1): 127-129)

[6] Huang Z J, Xiong D S. Preparation and friction and wear performance of Ni-PS-MoS₂ composite coating [J]. J. Zhengzhou Univ., 2008, 29(4): 42-46

    (黄仲佳, 熊党生. Ni-PS-MoS₂复合镀层的制备及摩擦磨损性能 [J]. 郑州大学学报, 2008, 29(4): 42-46)

[7] Leon O A, Staia M H, Hintermann H E. Deposition of Ni-P-BN(h) composite autocatalytic coatings [J].Surf. Coat. Technol., 1998, 108-109: 461-465

[8] Abdel S H, Shoeib M A, Hady H, et al. Corrosion behavior of electroless Ni--P alloy coatings containing tungsten or nano-scattered alumina composite in 3.5% NaCl solution [J]. Surf. Coat. Technol., 2007, 202: 162-171

[9] Liu L Y, Guo Z C, Zhang H, et al. Study on the properties of electrodeposition Ni-W-P series multi-composite coatings [J]. J. Kunming Univ. Sci. Technol., 2004, 29(3): 21-25

    (刘龙玉, 郭忠诚, 张欢等. 脉冲电沉积Ni-W-P系多元复合镀层性能研究 [J]. 昆明理工大学学报, 2004, 29(3): 21-25)

[10] Yao S W, Mu G L, Zhang W G. Properties of electroless Ni-P/nano-Al₂O₃ composite coatings [J]. J.Mater. Prot., 2007, 40(10): 26-28

     (姚素薇, 穆高林, 张卫国. 化学镀Ni-P/纳米Al₂O₃复合镀层结构及性能研究 [J]. 材料保护, 2007, 40(10): 26-28)

[11] Shi S Y, Ma W Y, Chang L M, et al. Effects of different electro-deposition methods on microstructure and corrosion resistance of Ni-nano Al₂O₃ composite coating [J]. Chin. J. Appl. Chem.,2008, 25(12): 1499-1501

     (石淑云, 马文英, 常立民等. 电沉积方式对Ni-nano Al₂O₃复合镀层组织结构和耐蚀性能的影响 [J]. 应用化学, 2008, 25(12): 1499-1501)

[12] Gao J Q, Liu L, Shen B, et al. Crystallization behavior of nano-Al₂O₃ composite coatings prepared by electroless plating [J]. Chin. J. Nonferrous Met., 2004, 14(1): 64-68

     (高加强, 刘磊, 沈彬等. 纳米氧化铝粒子对化学镀镍-磷合金晶化行为的影响 [J]. 中国有色金属学报, 2004, 14(1): 64-68)

[13] Xu R D, Guo Z C, Zhu X Y, et al. A research on high-P amorphous Ni-P coating [J]. Electroplat. Pollut.Control, 2002, 22(3): 18-20

     (徐瑞东, 郭忠诚, 朱晓云等. 高磷非晶态镍磷合金镀层的研究 [J]. 电镀与环保, 2002, 22(3): 18-20)

[1]	韩月桐, 张鹏超, 史杰夫, 李婷, 孙俊才. 质子交换膜燃料电池中TA1双极板的表面改性研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 125-130.
[2]	史昆玉, 吴伟进, 张毅, 万毅, 于传浩. TC4表面沉积Nb涂层在模拟体液环境下的电化学性能研究[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[3]	马鸣蔚, 赵志浩, 荆思文, 于文峰, 谷义恩, 王旭, 吴明. 17-4 PH不锈钢在含SRB的模拟海水中的应力腐蚀开裂行为研究[J]. 中国腐蚀与防护学报, 2020, 40(6): 523-528.
[4]	杨寅初,傅秀清,刘琳,马文科,沈莫奇. 喷射电沉积Ni-P-BN(h)-Al₂O₃复合镀层的耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2020, 40(1): 57-62.
[5]	张瑞,李雨,关蕾,王冠,王福雨. 热处理对激光选区熔化Ti6Al4V合金电化学腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[6]	肖金涛,陈妍,邢明秀,鞠鹏飞,孟引根,王芳. 工艺参数对2195铝锂合金阳极氧化膜的耐蚀性影响[J]. 中国腐蚀与防护学报, 2019, 39(5): 431-438.
[7]	欧阳跃军,胡婷,王佳音,谢治辉. 镁合金表面层状双氢氧化物的电化学沉积和表征[J]. 中国腐蚀与防护学报, 2019, 39(5): 453-457.
[8]	史昆玉,张进中,张毅,万毅. Nb₂N涂层制备及其耐腐蚀性能研究[J]. 中国腐蚀与防护学报, 2019, 39(4): 313-318.
[9]	冯旭,费敬银,李倍,张嫚,郭琪琪. 组分调制Ni/Cr多层膜合金化制备Ni-Cr合金覆盖层的耐腐蚀特性[J]. 中国腐蚀与防护学报, 2019, 39(2): 167-175.
[10]	蒋光锐, 刘广会. Zn-Al-Mg合金的凝固组织及其耐腐蚀性能[J]. 中国腐蚀与防护学报, 2018, 38(2): 191-196.
[11]	牛振国, 郭浦山, 叶宏, 杨丽景, 许赪, 宋振纶. Zn-7Mg合金热处理显微组织演变及耐蚀性能研究[J]. 中国腐蚀与防护学报, 2017, 37(4): 347-353.
[12]	崔明君,任思明,张广安,刘栓,赵海超,王立平,薛群基. 六方氮化硼掺杂水性环氧树脂耐腐蚀性能的研究[J]. 中国腐蚀与防护学报, 2016, 36(6): 566-572.
[13]	马旭,李全安,井晓天. 热处理对Mg-10Gd-2.5Nd-0.5Zr合金组织和耐蚀性能的影响[J]. 中国腐蚀与防护学报, 2016, 36(2): 143-149.
[14]	郭跃岭,韩恩厚,王俭秋. 锻后热处理对核级316LN不锈钢在沸腾MgCl₂溶液中应力腐蚀行为的影响[J]. 中国腐蚀与防护学报, 2015, 35(6): 488-495.
[15]	刘胤, 刘时美, 于鲁萍, 刘军, 姜伟. 镁合金的腐蚀与微弧氧化膜层研究[J]. 中国腐蚀与防护学报, 2015, 35(2): 99-105.

Viewed

Full text

Abstract

Cited

Shared

Discussed