CORROSION BEHAVIOR OF Fe-10Cr NANOCRYSTALLINE COATINGS ( I ) THE PASSIVE BEHAVIOR OF Fe-10CrNANOCRYSTALLINE COATINGS IN ACIDIC SOLUTION
;;
哈尔滨工程大学材料科学与化学工程学院
Download:  PDF(1831KB) 
Export:  BibTeX | EndNote (RIS)      
Abstract  Fe-10Cr nanocrystalline ( nc ) coating with the grain size about 20 nm to 30 nm was fabricated on a glass substrate by magnetron sputtering technique.The corrosion behavior of the Fe-10Cr nc coating and its counterpart alloys were investigated in 0.05 mol/L H2SO4+0.25 mol/L Na2SO4 solution by polarization curves.The results showed that the active dissolution of Fe-10Cr nc coating was accelerated as comparing with its counterpart Fe-10Cr cast alloy.For Fe-10Cr nc coating,it had a higher tendency to passive in acid solution and the passive current density was lower as compaed with its counterpart alloy.The further average active energy measurement,EIS measurement and Mott-Schottky analysis revealed that the average active energy for the dissolving reaction of the Fe-10Cr nc coating was higher.This is attributed to the higher defect density on the nc coating.On the other hand,even though the same n type semiconductor passive film was formed on both nc sputtering coating and its counterpart alloy,but Cr was easier to accumulate in the passive film of Fe-10Cr nc coating and the donor density in its passive film was lower.The higher passive ability of the nc sputtering coating was attributed to the more Cr accumulated in the passive film and the higher chemical stability of the passivity film.
Key words:  nanocystalline      grain size      corrosion behavior      passive      passive film      
Received:  26 July 2005     
ZTFLH:  TG17.1  
Service
E-mail this article
Add to citation manager
E-mail Alert
RSS
Articles by authors

Cite this article: 

. CORROSION BEHAVIOR OF Fe-10Cr NANOCRYSTALLINE COATINGS ( I ) THE PASSIVE BEHAVIOR OF Fe-10CrNANOCRYSTALLINE COATINGS IN ACIDIC SOLUTION. J Chin Soc Corr Pro, 2007, 27(1): 35-42 .

URL: 

https://www.jcscp.org/EN/     OR     https://www.jcscp.org/EN/Y2007/V27/I1/35

[1]Tjong S C,Chen H.Nanocrystalline materials and coatings[J].Ma-ter.Sci.Eng.R,2004,45:1-88
[2]Zeiger W,Schneider M,Scharnweber D,et al.Corrosion behaviour ofa nanocrystalline FeAl8 alloy[J].Nanostructured Materials,1995,6:1013-1016
[3]Mariano N A,Souza C A C,Oliviera MF,et al.Corrosion resistanceof amorphous and nanocrystalline Fe-M-B(M=Zr,Nb)alloys[J].Mater.Sci.Forum,2000,861:343-346
[4]Oblonsky L J,Ryan M P,Isaacs H S.In situ determination of thecomposition of surface films formed on Fe-Cr alloys[J].J.Electro-chem.Soc.,1998,145:1922-1932
[5]Kirchheim R,Heine H,Fischmeister H,et al.The passivity of iron-chromium alloys[J].Corros.Sci.,1989,29:899-917
[6]Mitrovic-Scepanovic V,MacDougall B,Graham MJ.Nature of pas-sive films on Fe-26Cr alloy[J].Corros.Sci.,1984,24:479-490
[7]Haupt S,Strehblow HH.A combined surface analytical and electro-chemical study of the formation of passive layers[J].Corros.Sci.,1995,37:43-54
[8]Maurice V,Yang W P,Marcus P.XPS and STMstudy of the passivefilms formed on Fe-22Cr(110)single-crystal surfaces[J].J.Electrochem.Soc.,1996,143:1182-1200
[9]Mischler S,Vogel A,Mathieu HJ,et al.The chemical composition ofthe passive film on Fe-24Cr and Fe-24Cr-11Mo studied byAES,XPS and SIMS[J].Corros.Sci.,1991,32:925-944
[10]Olsson C O A,Landolt D.Passive films on stainless steels—chemis-try,structure and growth[J].Electrochim.Acta,2003,48:1093-1104
[11]Wang F H.The effect of nanocrystallization on the selective oxida-tion and adhesion of Al2O3scales[J].Oxid.Met.,1997,48:215-224
[12]Wang F H.Oxidation resistance of sputtered Ni3(AlCr)nanocrys-tallized coating[J].Oxid.Met.,1997,47:247-258
[13]Intrui R B,Szklarska-Smialowska Z.Localized corrosion of nano-crystalline 304 type stainless steel films[J].Corrosion,1992,48:398-403
[14]Atkins P W.Physical Chemistry[M].Oxford:Oxford UniversityPress,1994
[15]Tong W P,Tao N R,Wang Z B,et al.Nitriding iron at lower tem-perature[J].Science,2003,299:686-688
[16]Cao C N.The Principles of Corrosion Electrochemistry[M].Bei-jing:Chemical Industry Press,2004(曹楚南.腐蚀电化学原理[M].北京:化学工业出版社,2004)
[17]Meng G Z,Li Y,Wang F H.Electrochemical behavior of Fe-20Crnanocrystalline coatings[J].J.Chin.Soc.Corros.Prot.,2006,26(1):11-18(孟国哲,李瑛,王福会.Fe-20Cr纳米涂层的电化学行为[J].中国腐蚀与防护学报,2006,26(1):11-18)
[18]Cabrera N,Mott N F.Rep.Prog.Phys.,1948-1949,12:163
[19]Hakiki N E,Boundin S,Rondot B,et al.The electronic structure ofpassive films formed on stainless steel[J].Corros.Sci.,1995,37:1809-1822
[20]Simoes A M P,Ferrira M G S,Rondot B,et al.Study of passivefilms formed on AISI 304 stainless steel by impedance measure-ments and photoelectrochemistry[J].J.Electrochem.Soc.,1990,137:82-87
[21]Ahn J S,Kwon S H.Effects of solution temperature on electronicproperties of passive film formed on Fe in pH8.5 borate buffer so-lution[J].Electrochim.Acta,2004,49:3347-3353
[1] SHI Kunyu, WU Weijin, ZHANG Yi, WAN Yi, YU Chuanhao. Electrochemical Properties of Nb Coating on TC4 Substrate in Simulated Body Solution[J]. 中国腐蚀与防护学报, 2021, 41(1): 71-79.
[2] LI Lin, CHEN Yiqing, GAO Peng, AI Fangfang, ZHONG Bin, SAN Hongyu, YANG Ying. Corrosion Resistance of Various Bridge Steels in Deicing Salt Environments[J]. 中国腐蚀与防护学报, 2020, 40(5): 448-454.
[3] ZHANG Xin, YANG Guangheng, WANG Zehua, CAO Jing, SHAO Jia, ZHOU Zehua. Corrosion Behavior of Al-Mg-RE Alloy Wires Subjected to Different Cold Drawing Deformation[J]. 中国腐蚀与防护学报, 2020, 40(5): 432-438.
[4] HU Lulu, ZHAO Xuyang, LIU Pan, WU Fangfang, ZHANG Jianqing, LENG Wenhua, CAO Fahe. Effect of AC Electric Field and Thickness of Electrolyte Film on Corrosion Behavior of A6082-T6 Al Alloy[J]. 中国腐蚀与防护学报, 2020, 40(4): 342-350.
[5] WANG Xinhua, YANG Yong, CHEN Yingchun, WEI Kailing. Effect of Alternating Current on Corrosion Behavior of X100 Pipeline Steel in a Simulated Solution for Soil Medium at Korla District[J]. 中国腐蚀与防护学报, 2020, 40(3): 259-265.
[6] HU Yuting, DONG Pengfei, JIANG Li, XIAO Kui, DONG Chaofang, WU Junsheng, LI Xiaogang. Corrosion Behavior of Riveted Joints of TC4 Ti-Alloy and 316L Stainless Steel in Simulated Marine Atmosphere[J]. 中国腐蚀与防护学报, 2020, 40(2): 167-174.
[7] SHEN Shuyang, WANG Dongsheng, SUN Shibin, YANG Ti, ZHAO Qianjing, WANG Xin, ZHANG Yafei, CHANG Xueting. Corrosion Behavior in Artificial Seawater of Subzero Treated EH40 Marine Steel Suitable for ExtremelyCold Environments[J]. 中国腐蚀与防护学报, 2020, 40(2): 151-158.
[8] SU Xiaohong,HU Huie,KONG Xiaodong. Corrosion Behavior of W Particles/Zr41.2Ti13.8Cu12.5Ni10Be22.5 Metallic Glass Matrix Composite in 3%NaCl Solution[J]. 中国腐蚀与防护学报, 2020, 40(1): 70-74.
[9] ZHANG Rui,LI Yu,GUAN Lei,WANG Guan,WANG Fuyu. Effect of Heat Treatment on Electrochemical Corrosion Behavior of Selective Laser Melted Ti6Al4V Alloy[J]. 中国腐蚀与防护学报, 2019, 39(6): 588-594.
[10] WANG Qinying,PEI Rui,XI Yuchen. Erosion-corrosion Behavior of Laser-clad Ni-based Alloy Coating on Q235 Carbon Steel[J]. 中国腐蚀与防护学报, 2019, 39(5): 458-462.
[11] GUO Tieming,ZHANG Yanwen,QIN Junshan,SONG Zhitao,DONG Jianjun. Corrosion Behavior of Q345q Bridge Steel in Three Simulated Atmospheres[J]. 中国腐蚀与防护学报, 2019, 39(4): 319-330.
[12] Shaokun YAN,Dajiang ZHENG,Jiang WEI,Guangling SONG,Lian ZHOU. Electrochemical Activation of Passivated Pure Titanium in Artificial Seawater[J]. 中国腐蚀与防护学报, 2019, 39(2): 123-129.
[13] Dong LIU,Hongliang XIANG,Chunyu LIU. XPS Analysis of Corrosion Product Scale on Surface of Silver-bearing Antibacterial Duplex Stainless Steel[J]. 中国腐蚀与防护学报, 2018, 38(6): 533-542.
[14] Ming LIU,Xuequn CHENG,Xiaogang LI,Tianjian LU. Corrosion Resistance Mechanisms of Passive Films Formed on Low Alloy Rebar Steels in Liquor of Cement Extract[J]. 中国腐蚀与防护学报, 2018, 38(6): 558-564.
[15] Bobo HUANG,Ping LIU,Xinkuan LIU,Pinxiu MEI,Xiaohong CHEN. Seawater Corrosion Behavior of New 70-1 Tin Brass Net in Waters off Dachen Island for Two Years[J]. 中国腐蚀与防护学报, 2018, 38(6): 594-600.
No Suggested Reading articles found!