STUDY ON THE ELECTROCHEMICAL CORROSION BEHAVIOROF TiN COATING IN ACID AND SALT SOLUTIONⅠ.The corrosion resistance and failure mechanism of TiN coating in acid and salt solution

J Chin Soc Corr Pro

2003, Vol. 23

Issue (2): 65-69 DOI:

Research Report

Current Issue | Archive | Adv Search

STUDY ON THE ELECTROCHEMICAL CORROSION BEHAVIOROF TiN COATING IN ACID AND SALT SOLUTIONⅠ.The corrosion resistance and failure mechanism of TiN coating in acid and salt solution

Ying Li;Fuhui Wang;Zhongbao Shao

中国科学院金属研究所;金属腐蚀与防护国家重点实验室

Cite this article:

Ying Li; Fuhui Wang; Zhongbao Shao. STUDY ON THE ELECTROCHEMICAL CORROSION BEHAVIOROF TiN COATING IN ACID AND SALT SOLUTIONⅠ.The corrosion resistance and failure mechanism of TiN coating in acid and salt solution. J Chin Soc Corr Pro, 2003, 23(2): 65-69 .

Download:

PDF(240KB)
Export: BibTeX | EndNote (RIS)

Abstract The corrosion properties of TiN coating fabricated by Hollow cathode Ionic Deposition was studied by electrochemical methods and su rface analysis such as SEM and STM.In acid and salt solution,TiN shows an excell ent corrosion resistance after 100 h immersing test.TiN coating acted as a physi cal barrier between the stainless steel and corrosion media.The corrosion proces s initiated from the pinhole and the corrosion process under the coating is very similar to the pit corrosion form.

Key words: TiN corrosion resistance failure mechanism

Received: 22 June 2001

ZTFLH:

TG174.71

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Ying Li
	Fuhui Wang
	Zhongbao Shao

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I2/65

[1]BeverskogB ,CarlssonJO ,DelblancBauerA ,DeshpandeyCV ,BdnshahHJ ,O’BrienBP .CorrosionpropertiesofTiCfilm pre paredbyactivereactiveevaporation[J].Surf.Coat.Technol.,1990,41:221.
[2]RudenjaS ,PanJ,OdnevallWallinderI ,LeygrafC ,KuluP .Passiva tionandanodicoxidationofdupluxTiNcoatingonstainlesssteel[J].J.Electrochem.Soc.1999,146:4082
[3]MarcoJF ,AgudeloAC ,GancedoJR ,HanzelD .Corrosionresis tanceofsingleTiNlayers,Ti/TiNbilayersandTi/TiN/Ti/TiNmultilayersonironunderasaltfogspray(phohesion)test:anevalu ationbyXPS[J].SurfaceandInterfaceAnalysis,1999,27:71
[4]ChenBF ,PanWL ,YuGP ,WangJ ,HuangJH .OnthecorrosionbehaviorofTiN -coatedAISID2steel[J].Surf.Coat.Technol.,1999,111:16
[5]Bin-SudinM ,LeylandA ,JamesAS ,MatthewsA ,HousdenJ ,GarsideB .SubstratesurfacefinisheffectsinduplexcoatingsofPA PVDTiNandCrNwithelectrolessnickel-phosphorusinterlayers[J].Surf.Coat.Technol.(Switzerland),1996,81:215

[1]	LI Yan, GAO Ke, ZHANG Wei, CHEN Xinbin, SUI Xianjie, CHEN Hongsheng, WANG Xiaoya, LENG Xuesong, WU Junwei. Recent Advances on Functional Enhancement Design and Performance Regulation Mechanism of Coatings for Deep-sea Equipment[J]. 中国腐蚀与防护学报, 2026, 46(5): 1305-1325.
[2]	ZENG Qi, YU Wenjun, MEN Xiangnan, FENG Baojing, YANG Yao, ZHU Kai, GE Yulin, YING Tao, ZENG Xiaoqin. Recent Research Progress of Rare-earth Mg-alloys with High Strength and Corrosion Resistance[J]. 中国腐蚀与防护学报, 2026, 46(5): 1415-1424.
[3]	ZHENG Kai, WANG Yitao, WANG Dongsheng, LIU Wei, JIANG Yingchang, HUANG Rong, CHANG Xueting. Influence of Corrosion-stress Coupling Effect on Corrosion and Failure of Low-carbon Martensitic Stainless Steel for Polar Marine Propellers[J]. 中国腐蚀与防护学报, 2026, 46(5): 1452-1462.
[4]	ZHANG Chunyan, ZHANG Yuxin, CHEN Bixiu, YU Baoxing, ZHOU Peng. Effect of Shrinkage Cavities of Cast AZ91D Mg-alloy on Corrosion Resistance of Its Chemical Conversion Coating Prepared with Permanganate-phosphate[J]. 中国腐蚀与防护学报, 2026, 46(5): 1475-1484.
[5]	QI Xiaohan, ZHAI Haimin, LI Wensheng, HONG Hao, CAO Yuan, YU Lei, CHEN Bohan. Influence of Adding Nano-Al₂O₃ to Wet Enamel Frit Powder Slurry on Microstructure and Corrosion Resistance Enamel Coatings Applied on Al-alloy[J]. 中国腐蚀与防护学报, 2026, 46(5): 1497-1507.
[6]	ZHAO Xianrui, DAI Zhongguo, LI Zhanjiang, XU Yulang, ZHANG Huixia, LI Wang. Effect of Adding Y and Hf on Corrosion Behavior of AlCoCrFeNi High-entropy Alloy Coatings in NaCl Solution[J]. 中国腐蚀与防护学报, 2026, 46(5): 1549-1559.
[7]	HE Zhangping, YUAN Yukun, DU Yingzhe, LIN Peng, XU Jian. Crevice Corrosion Behavior of 316LN Stainless Steel in Simulated Electric Heater Overheating Conditions[J]. 中国腐蚀与防护学报, 2026, 46(5): 1579-1587.
[8]	ZHANG Honglei, ZHENG Ziqi, DONG Kaihui, WANG Zhengbin, SONG Yingwei, ZHENG Yugui. Performance Variation of Ni-P Coatings on Inner Wall of B30 Cu-Ni Alloy Tube Prepared with Chemical Plating Solution of Varying Flow Rates[J]. 中国腐蚀与防护学报, 2026, 46(5): 1588-1594.
[9]	HUANG Hulingtong, WANG Cheng, CHENG Xuequn, YANG Xiaojia, ZHANG Zhanwu, LI Liang. Corrosion Behavior of Q235 Carbon Steel in a Simulated Saline Soil of Southern Xinjiang[J]. 中国腐蚀与防护学报, 2026, 46(5): 1595-1604.
[10]	YU Chunlin, GU Mingfei, SUN Yi'ang, YUAN Kexin, YANG Jing, WANG Lixi, ZHU Chengfei, ZHU Haikui. Durability Assessment of Powder Spraying Coating on Surface of 316 Stainless Steel in Artificial Marine Environments[J]. 中国腐蚀与防护学报, 2026, 46(5): 1627-1633.
[11]	TAN Jun, CUI Chunjiang, DUAN Mingxia, LIU Xiangzhou, MENG Hailong, JIANG Ying. Corrosion Prediction and Prevention for Gathering Pipelines in Gas Field[J]. 中国腐蚀与防护学报, 2026, 46(5): 1634-1642.
[12]	YONG Xingyue, DONG Xiaomei, GAO Xinhua, LI Zuoxian, CHEN Yanfei, JI Haotian. Application of Electrochemical Impedance Spectroscopy in Research of Organic Coatings[J]. 中国腐蚀与防护学报, 2026, 46(4): 945-961.
[13]	XU Qiufa, GUO Yue, LIU Jun, YANG Dong, CUI Yu. Effect of Hydrostatic Pressure on Stress Corrosion Cracking of Cast and Forged Ti-6Al-4V Alloys[J]. 中国腐蚀与防护学报, 2026, 46(4): 1031-1044.
[14]	MA Huanhuan, LV Shengdong, QIAN Yixin, LIN Yong, HAO Xiangping, ZHANG Dawei, WANG Luning. Localized Corrosion and Service Life Prediction of Copper Heat Exchange Tubes in a Sodium Acetate Trihydrate Phase Change Thermal Energy Storage System[J]. 中国腐蚀与防护学报, 2026, 46(4): 1045-1057.
[15]	KE Dingfang, WU Fangfang, ZHU Zhaobin, XIE Shengyi, HONG Jing, CHEN Yue, LI Liang, LI Hao, CAO Fahe. Composite of Graphene Oxide/Cerium-based Metal Organic Frameworks for Preparing Protective Coatings with High Stability and Long-term Corrosion Resistance[J]. 中国腐蚀与防护学报, 2026, 46(4): 1095-1106.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed