CORROSION RESISTANCE BEHAVIOR OF CERIUM-DOPED TiO2 FILM IN THE PRESENCE OF MARINE BACTERIUM SULFATE-REDUCING BACTERIA

J Chin Soc Corr Pro

2010, Vol. 30

Issue (6): 481-486 DOI:

Research Articles

Current Issue | Archive | Adv Search

CORROSION RESISTANCE BEHAVIOR OF CERIUM-DOPED TiO₂ FILM IN THE PRESENCE OF MARINE BACTERIUM SULFATE-REDUCING BACTERIA

WANG Hongfen¹, WANG Zhiqi², HONG Haixia¹, CHEN Shougang¹,YIN Yansheng¹

1. Institute of Materials Science and Engineering, Ocean University of China, Qingdao 266100
2. Qingdao Institute of Bioenergy and Bioprocess Technology, Chinese Academy of Sciences, Qingdao 266101

Download:

PDF(2312KB)
Export: BibTeX | EndNote (RIS)

Abstract Cerium-doped TiO₂ film was prepared on 304 stainless steel by a sol-gel process. Sulfate-reducing bacteria(SRB) was incubated by semi-continuous culture method. The effect of SRB on corrosion behavior of cerium-doped TiO₂/304ss and bare 304ss immersed in SRB medium were studied by morphology analysis and electrochemical methods. The results showed that cerium-doped TiO₂ film on 304ss could inhibit attachment of SRB. The corrosion current density of cerium-doped TiO₂/304ss was lower, while electrochemical impedance was higher than that of bare 304ss. Therefore, a conclusion could be drawn that cerium-doped TiO₂ film coating on 304ss could inhibit attachment of SRB and prevent corrosion caused by SRB in seawater.

Key words: TiO₂ thin film sulfate-reducing bacteria polarization electrochemical impedance spectroscopy 304 stainless steel

Received: 12 October 2009

ZTFLH:

TG172

Corresponding Authors: WANG Hongfen E-mail: yys2003@ouc.edu.cn

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	YU Hong-Fen
	YU Zhi-Ai

Cite this article:

WANG Hongfen, WANG Zhiqi, HONG Haixia, CHEN Shougang,YIN Yansheng. CORROSION RESISTANCE BEHAVIOR OF CERIUM-DOPED TiO₂ FILM IN THE PRESENCE OF MARINE BACTERIUM SULFATE-REDUCING BACTERIA. J Chin Soc Corr Pro, 2010, 30(6): 481-486.

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2010/V30/I6/481

[1] Duan J Z, Wu S, Zhang X J, et al. Corrosion of carbon steel influenced by anaerobic biofilm in natural seawater [J]. Electrochim.Acta., 2008, 54: 22-28

[2] Yebra D M, Kiil S, Weinell C E, et al. Effects of marine microbial biofilms on the biocide release rate from antifouling paints-a model-based analysis [J]. Prog. Org. Coat.,2006, 57: 56-66

[3] Mattila K, Carpen L, Hakkarainen T, et al.Biofilm development during ennoblement of stainless steel in Baltic sea water: A microscopic study [J]. Int. Biodeterior. Biodegrad.,1997, 40(1): 1-10

[4] Yin Y S, Cheng S, Chen S G, et al.Microbially influenced corrosion of 303 stainless steel by marine bacterium vibrio natriegens: (II) Corrosion mechanism [J].Mater. Sci. Eng., 2009, C29: 756-760

[5] Duan J Z, Hou B R, Yu Z G.Characteristics of sulfide corrosion products on 316L stainless steel surfaces in the presence of sulfate-reducing bacteria [J].Mater. Sci. Eng., 2006, C26: 624-629

[6] Liu H F, Xu L M, Zheng J S.Influence of SRB biofilm on corrosion of carbon steel [J]. J. Chin.Soc. Corros. Prot., 2000, 20 (1): 41-46

(刘宏芳, 许立铭, 郑家燊. SRB生物膜与碳钢腐蚀的关系 [J]. 中国腐蚀与防护学报, 2000, 20(1): 41-46)

[7] Gonzalez J E G, Santana F J H, Mirza-rosca J C. Effect of bacterial biofilm on 316ss corrosion in natural seawater by EIS [J].Corros. Sci., 1998, 40(12): 2141-2154

[8] Wang D H, Bierwagen G P.Sol-gel coatings on metals for corrosion protection [J]. Prog. Org.Coat., 2009, 64(4): 327-338

[9] Cottis R, Turgoose S. Analysis of electrochemical impedance spectroscopy data. In: Syrett B C ed.,Corrosion testing made easy: Electrochemical Impedance and Noise Analysis [M]. NACE International, Houston, TX, 1999

[10] Bao Y S. Corrosion Behavior of TiO₂ Film in Seawater [D].Qingdao: Ocean University of China, 2008

(鲍玉胜. TiO₂薄膜的耐海水腐蚀性能研究 [D]. 青岛: 中国海洋大学, 2008)

[1]	WANG Xintong, CHEN Xu, HAN Zhenze, LI Chengyuan, WANG Qishan. Stress Corrosion Cracking Behavior of 2205 Duplex Stainless Steel in 3.5%NaCl Solution with Sulfate Reducing Bacteria[J]. 中国腐蚀与防护学报, 2021, 41(1): 43-50.
[2]	ZHANG Hao, DU Nan, ZHOU Wenjie, WANG Shuaixing, ZHAO Qing. Effect of Fe³⁺ on Pitting Corrosion of Stainless Steel in Simulated Seawater[J]. 中国腐蚀与防护学报, 2020, 40(6): 517-522.
[3]	LI Ziyun, WANG Gui, LUO Siwei, DENG Peichang, HU Jiezhen, DENG Junhao, XU Jingming. Early Corrosion Behavior of EH36 Ship Plate Steel in Tropical Marine Atmosphere[J]. 中国腐蚀与防护学报, 2020, 40(5): 463-468.
[4]	SUN Shuo, YANG Jie, QIAN Xinzhu, CHANG Renli. Preparation and Electrochemical Corrosion Behavior of Electroless Plated Ni-Cr-P Alloy Coating[J]. 中国腐蚀与防护学报, 2020, 40(3): 273-280.
[5]	CHEN Xu, LI Shuaibing, ZHENG Zhongshuo, XIAO Jibo, MING Nanxi, HE Chuan. Microbial Corrosion Behavior of X70 Pipeline Steel in an Artificial Solution for Simulation of Soil Corrosivityat Daqing Area[J]. 中国腐蚀与防护学报, 2020, 40(2): 175-181.
[6]	CHEN Xu,MA Jiong,LI Xin,WU Ming,SONG Bo. Synergistic Effect of SRB and Temperature on Stress Corrosion Cracking of X70 Steel in an ArtificialSea Mud Solution[J]. 中国腐蚀与防护学报, 2019, 39(6): 477-483.
[7]	ZHANG Tianyi,LIU Wei,FAN Yueming,LI Shimin,DONG Baojun,BANTHUKUL Wongpat,CHOWWANONTHAPUNYA Thee. Effect of Synergistic Action of Cu/Ni on Corrosion Resistance of Low Alloy Steel in a Simulated Tropical Marine Atmosphere[J]. 中国腐蚀与防护学报, 2019, 39(6): 511-518.
[8]	LUO Hong,GAO Shujun,XIAO Kui,DONG Chaofang,LI Xiaogang. Effect of Magnetron Sputtering Process Parameters on CrN Films on 304 Stainless Steel and TheirCorrosion Behavior[J]. 中国腐蚀与防护学报, 2019, 39(5): 423-430.
[9]	QI Peng, WAN Yi, ZENG Yan, ZHENG Laibao, ZHANG Dun. Rapid Detection Methods for Sulfate-reducing Bacteria in Marine Environments[J]. 中国腐蚀与防护学报, 2019, 39(5): 387-394.
[10]	WANG Biao,DU Nan,ZHANG Hao,WANG Shuaixing,ZHAO Qing. Accelerating Effect of Pitting Corrosion Products on Metastable Pitting Initiation and the Stable Pitting Growth of 304 Stainless Steel[J]. 中国腐蚀与防护学报, 2019, 39(4): 338-344.
[11]	Xia WANG,Shuaifei REN,Daixiong ZHANG,Huan JIANG,Yue GU. Inhibition Effect of Soybean Meal Extract on Corrosion of Q235 Steel in Hydrochloric Acid Medium[J]. 中国腐蚀与防护学报, 2019, 39(3): 267-273.
[12]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Equivalent Electrical Circuits Fitting of Electrochemical Impedance Spectroscopy for Rebar Steel Corrosion of Coral Aggregate Concrete[J]. 中国腐蚀与防护学报, 2019, 39(3): 260-266.
[13]	Tangqing WU,Zhaofen ZHOU,Xinming WANG,Dechuang ZHANG,Fucheng YIN,Cheng SUN. Thermodynamic and Dynamic Analyses of Microbiologically Assisted Cracking[J]. 中国腐蚀与防护学报, 2019, 39(3): 227-234.
[14]	Wenshan PENG,Jian HOU,Kangkang DING,Weimin GUO,Ri QIU,Likun XU. Corrosion Behavior of 304 Stainless Steel in Deep Sea Environment[J]. 中国腐蚀与防护学报, 2019, 39(2): 145-151.
[15]	Bo DA,Hongfa YU,Haiyan MA,Zhangyu WU. Influence of Inhibitors on Reinforced Bar Corrosion of Coral Aggregate Seawater Concrete[J]. 中国腐蚀与防护学报, 2019, 39(2): 152-159.

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed