THE OXIDATION BEHAVIOR OF ALUMINIZEDHK40 STEEL COATED WITH Y2O3 THIN FILM

J Chin Soc Corr Pro

2003, Vol. 23

Issue (2): 124-128 DOI:

Research Report

Current Issue | Archive | Adv Search

THE OXIDATION BEHAVIOR OF ALUMINIZEDHK40 STEEL COATED WITH Y2O3 THIN FILM

Zhirong Huang;Hong Xv;Peining Li

华东理工大学化机研究所

Download:

PDF(176KB)
Export: BibTeX | EndNote (RIS)

Abstract A uniform,dense and defect-free Y2O3 thin film was applied on the surface of aluminized HK40 steel by electrodeposition pyroly sis method.The influence of this film on the isothermal oxidation behavior of th e aluminized HK40 steel,which was exposed to ambient atmosphere at 850℃,1000℃ respectively,was investigated.The results show that,by surface-applied Y2O3 thin film,the oxidation resistance of the aluminized HK40 steel is increased.The effects of the Y2O3 film on the oxidation are discussed.

Key words: high-temperature oxidation rare earth element Y2O 3 thin film

Received: 29 October 2001

ZTFLH:

TG172.82

Corresponding Authors: Zhirong Huang

	Service

	E-mail this article
	Add to citation manager
	E-mail Alert
	RSS
	（）
	Articles by authors
	Zhirong Huang
	Hong Xv
	Peining Li

Cite this article:

Zhirong Huang; Hong Xv; Peining Li. THE OXIDATION BEHAVIOR OF ALUMINIZEDHK40 STEEL COATED WITH Y2O3 THIN FILM. J Chin Soc Corr Pro, 2003, 23(2): 124-128 .

URL:

https://www.jcscp.org/EN/ OR https://www.jcscp.org/EN/Y2003/V23/I2/124

[1]BonnetG ,AguilarG ,ColsonJC ,LarpinJP .Theeffectofrareearthsdepositedonsteelsurfaces,bydifferentprocesses(SOL/GEL ,Electrophoresis,OMCVD ),onhightemperaturecorrosionbehavior[J].Corros.Sci.,1993,35(5-8):893-899
[2]LuXinying,ZhuRizhang,HeYedong.ReactiveelementeffectofelectrodepositedY2O3oxidefilmsontheoxidationofFe-25CrandFe-25Cr-10Alalloys[J].Oxid.Met.,1995,43(3/4):217-236
[3]RamanathanLV .Roleofrare-earthelementsonhightemperatureoxidationbehaviorofFe-Cr,Ni-CrandNi-Cr-Alalloys[J].Corros.Sci.,1993,35(5-8):871-878
[4]HouPY ,ShuiZR ,ChongGY ,StringerJ .Effectofreactiveele mentoxidecoatingsonthehightemperatureoxidationbehaviorofaFeCrAlalloy[J].J.Electrochem.Soc.,1992,139(4):1119-1126
[5]TienJK ,PettitFS .Mechanismofoxideadher enceonFe-25Cr-4Al(YorSc)alloys[J].Metall.Trans.,1972,3:1587-1599
[6]JedlinakiJ ,MrowecS .Theinfluenceofimplant edyttriumontheoxidationbehaviorofβ-NiAl[J].Mater.Sci.Eng.,1987,87:291-287
[7]RamanarayananTA ,AyerR ,Petkovic-LutonR ,etal.Theinfluenceofyttriumonoxidescalegrowthandadherence[J].Oxid.Met.,1988,29(5/6):445-472
[8]NelsonRL ,RamsayJD ,WoodheadL .Thecoat ingofmetalswithceramicoxidesviacolloidalin termediates[J].ThinSolidFilms,1981,81:329-337
[9]HouPY ,StringerJ .Effectofsurface-appliedreactiveelementoxideontheoxidationofbinaryalloyscontainingCr[J].J .Electrochem.Soc.,1987,134(7):1836-1894
[10]StroosndderMF ,GuttmannV ,FransenT ,WitJ .Corrosionofalloy800Handtheeffectofsur face-appliedCeO2 inasulphizing/oxidizing/carburizingenvironmentat700℃[J].Oxid.Met.,1990,33:371-397
[11]BonnetG ,LarpinJP ,ColsonJC .OMCVDneodymiumoxidefilmeffectonZ4CN18-09(AISI304)steelhigh-temperaturecorrosionbehavior[J].SolidStateIonics,1992,51(1):11-13
[12]HuntzAM .StressesinNiO ,Cr2O3andAl2O3oxidescales[J].MaterialsScienceandEngineer ing,1995,A201:211-228

[1]	ZHENG Yanxin, LIU Ying, SONG Qingsong, ZHENG Feng, JIA Yuchuan, HAN Peide. High-temperature Oxidation Behavior and Wear Resistance of Copper-based Composites with Reinforcers of C, ZrSiO₄ and Fe[J]. 中国腐蚀与防护学报, 2020, 40(2): 191-198.
[2]	Chao SUN, Xiao YANG, Yuhua WEN. Effect of High-Al Austenitic Stainless Alloy Coatings Prepared by Magnetron Sputtering on High Temperature Oxidation Resistance of 316 Stainless Steel[J]. 中国腐蚀与防护学报, 2017, 37(6): 590-596.
[3]	Ming ZHU,Guyue ZHOU,Huihui ZHANG. Corrosion Behavior of 316 Stainless Steel in Mixed Molten Nitrate Salts with and without Rare Earth Element[J]. 中国腐蚀与防护学报, 2017, 37(1): 16-22.
[4]	Xizhong WANG,Jianhao WU,Hui PENG,Hongbo GUO,Shengkai GONG. Hot-gas Corrosion Resistance of La₂Ce₂O₇/8YSZ Duble-ceramic-layered Thermal Barrier Coating[J]. 中国腐蚀与防护学报, 2017, 37(1): 36-40.
[5]	Jiapeng HUANG,Bin YANG,Hang WANG. Effect of Multiple Addition of Y, La and Ce on Oxidation Behavior of Ni-10Cr-5Al Alloy at 1000 ℃ in Air[J]. 中国腐蚀与防护学报, 2016, 36(5): 489-496.
[6]	GUO Yong'an, LI Bosong, LAI Wanhui, GUO Jianting, ZHOU Lanzhang. OXIDATION BEHAVIOR OF Ni-BASED SUPERALLOY K444 AT 900℃ IN AIR DURING LONG TERM[J]. 中国腐蚀与防护学报, 2012, 32(4): 285-290.
[7]	GUO Pingyi, SHAO Yong, GAO Yanmin, WU Mingfang. ELECTROCHEMICAL IMPEDANCE MEASUREMENT ON THERMAL GROWN OXIDE FILMS OF RARE EARTH ELEMENT Yb/Dy-MODIFIED Fe-Cr ALLOYS[J]. 中国腐蚀与防护学报, 2010, 30(4): 317-322.
[8]	ANG Dongsheng TIAN Zongjun CHEN Zhiyong SHEN Lida WU Hongyan ZHANG Pingze LIU . HIGH-TEMPERATURE OXIDATION RESISTANCE COATINGS ON TiAl ALLOY SURFACE[J]. 中国腐蚀与防护学报, 2009, 29(1): 1-8.
[9]	Shizhen Zhang; Jianting Guo; Weili Ren; Wenlong Zhou. EFFECTS OF RARE EARTH ELEMENTS ON HIGH TEMPERATURE OXIDATION RESISTANCE OF NiAl/CrMo(Hf) ALLOY[J]. 中国腐蚀与防护学报, 2005, 25(2): 110-114 .
[10]	Yong Shen. High-Temperature Oxidation Resistance of High-Nb TiAl-Based Alloy[J]. 中国腐蚀与防护学报, 2004, 24(4): 203-207 .
[11]	Mingkai Lei; Fujun Yang; Peng Luo; Xiaopeng Zhu. MODELING OF CYCLIC OXIDATION KINETIC FOR HIGH-TEMPERATURE ALLOYS BASED ON BUCKLING SPALLATION OF OXIDE SCALE[J]. 中国腐蚀与防护学报, 2002, 22(2): 65-68 .

No Suggested Reading articles found!

Viewed

Full text

Abstract

Cited

Shared

Discussed